Modified-release drug spheroids coated with an aqueous mixture of high-viscosity hydroxypropylmethylcellulose (HPMC) and sodium carboxymethylcellulose (NaCMC) were formulated. The preparation of core drug spheroids and the coating procedures were performed using the rotary processor and a bottom-spray fluidized bed, respectively. Dissolution studies indicated that incorporation of suitable additives, such as poly(vinylpyrrolidone) (PVP) and poly(ethylene glycol) 400 (PEG) improved the flexibility and integrity of the coat layer by retarding the drug release. An increase in coating levels applied generally retarded the release rate of the drug. However, the ratio of HPMC to NaCMC in the mixed, plasticized polymeric coat played a more dominant role in determining the dissolution T50% values. The optimal ratio of HPMC to NaCMC for prolonged drug release was found to be 3:1, whereas an increase in the amount of NaCMC in the mixed polymer coat only increased drug release. The synergistic viscosity effect of HPMC and NaCMC in retarding drug release rate was greater in distilled water than in dissolution media of pH 1 and 7.2. Cross-sectional view of the scanning electron micrograph showed that all of the coated spheroids exhibited a well-fused, continuous, and distinct layer of coating film. The drug release kinetics followed a biexponential first-order kinetic model.
The influence of microwave irradiation on the drug release properties of freshly prepared and aged alginate, alginate-chitosan and chitosan beads was investigated. The beads were prepared by extrusion method with sulphathiazole as a model drug. The dried beads were subjected to microwave irradiation at 80 W for 10 min, 20 min or three consecutive cycles of 10 and 20 min, respectively. The profiles of drug dissolution, drug content, drug stability, drug polymorphism, drug-polymer interaction, polymer crosslinkage and complexation were determined by dissolution testing, drug content assay, differential scanning calorimetry and Fourier transform infra-red spectroscopy. The chemical stability of drug embedded in beads was unaffected by microwave conditions and length of storage time. The release property of drug was mainly governed by the extent of polymer interaction in beads. The aged alginate beads required intermittent cycles of microwave irradiation to induce drug release retarding effect in contrast to their freshly prepared samples. Unlike the alginate beads, the level of polymer interaction was higher in aged alginate-chitosan beads than the corresponding fresh beads. The drug release retarding property of aged alginate-chitosan beads could be significantly enhanced through subjecting the beads to microwave irradiation for 10 min. No further change in drug release from these beads was observed beyond 30 min of microwave irradiation. Unlike beads containing alginate, the rate and extent of drug released from the aged chitosan beads were higher upon treatment by microwave in spite of the higher degree of polymer interaction shown by the latter on prolonged storage. The observation suggested that the response of polymer matrix to microwave irradiation in induction of drug release retarding property was largely affected by the molecular arrangement of the polymer chains.