Organically (octyl amine, OA) surface modified electrocatalyst (OA-Pt/CB) was studied for its oxygen reduction reaction (ORR) activity via dc methods and its charge and mass transfer properties were studied via electrochemical impedance spectroscopy (EIS). Comparison with a commercial catalyst (TEC10V30E) with similar Pt content was also carried out. In EIS, both the catalysts showed a single time-constant with an emerging high-frequency semicircle of very small diameter which was fitted using suitable equivalent circuits. The organically modified catalyst showed lower charge-transfer resistance and hence, low polarization resistance in high potential region as compared to the commercial catalyst. The dominance of kinetic processes was observed at 0.925-1.000 V, whereas domination of diffusion based processes was observed at lower potential region for the organic catalyst. No effect due to the presence of carbon was observed in the EIS spectra. Using the hydrodynamic method, higher current penetration depth was obtained for the organically modified catalyst at 1600 rpm. Exchange current density and Tafel slopes for both the electrocatalysts were calculated from the polarization resistance obtained from EIS which was in correlation with the results obtained from dc methods.
A gold nanoparticle (AuNP) has a localized surface plasmon resonance peak depending on its size, which is often utilized for surface-enhanced Raman scattering (SERS). To obtain information on the cholesterol (Chol)-incorporated lipid membranes by SERS, AuNPs (5, 100 nm) were first functionalized by 1-octanethiol and then modified by lipids (AuNP@lipid). In membrane surface-enhanced Raman spectroscopy (MSERS), both signals from 1,2-dioleoyl-sn-glycero-3-phosphocholine (DOPC) and Chol molecules were enhanced, depending on preparation conditions (size of AuNPs and lipid/AuNP ratio). The enhancement factors (EFs) were calculated to estimate the efficiency of AuNPs on Raman enhancement. The size of AuNP100nm@lipid was 152.0 ± 12.8 nm, which showed an surface enhancement Raman spectrum with an EF2850 value of 111 ± 9. The size of AuNP5nm@lipid prepared with a lipid/AuNP ratio of 1.38 × 104 (lipid molecule/particle) was 275.3 ± 20.2 nm, which showed the highest enhancement with an EF2850 value of 131 ± 21. On the basis of fluorescent probe analyses, the membrane fluidity and polarity of AuNP@lipid were almost similar to DOPC/Chol liposome, indicating an intact membrane of DOPC/Chol after modification with AuNPs. Finally, the membrane properties of AuNP@lipid systems were also discussed on the basis of the obtained MSERS signals.
Core-shell Fe3O4/Au nanostructures were constructed using an advanced method of two-step synthesis from Juglans regia (walnut) green husk extract. Several complementary methods were applied to investigate structural and magnetic properties of the samples. X-ray diffraction (XRD), high-resolution transmission electron microscopy (HR-TEM), electron diffraction, optical, thermogravimetric analysis (TGA), and vibrating sample magnetometer (VSM) were used for nanoparticle characterizations. As shown by HR-TEM, the mean diameter of core-shell Fe3O4/Au nanoparticles synthesized using co-precipitation method was 6.08 ± 1.06 nm. This study shows that the physical and structural properties of core-shell Fe3O4/Au nanoparticles possess intrinsic properties of gold and magnetite. VSM revealed that the core-shell Fe3O4/Au have high saturation magnetization and low coercivity due to the magnetic properties. The core-shell nanoparticles show the inhibitory concentration (IC)50 of 235 μg/ml against a colorectal cancer cell line, HT-29. When tested against non-cancer cells, IC50 was not achieved even up to 500 μg/ml. This study highlights the magnetic properties and anticancer action of core-shell Fe3O4/Au nanoparticles. This compound can be ideal candidate for cancer treatment and other biomedical applications.
A novel polyoxometalate-based electrode was developed by incorporating phosphotungstic acid (PWA) in nylon-6,6 nanofiber, followed by carbonization. The developed PWA-carbon nanofiber (PWA-CNF) showed the characteristics of the dual-scale porosity of micro- and mesoporous substrate with surface area of around 684 m2 g-1. The compound exhibited excellent stability in vanadium electrolyte and battery cycling. Evaluation of electrocatalytic properties toward V2+/V3+ and VO2+/VO2+ redox couples indicated promising advantages in electron transfer kinetics and increasing energy efficiency, particularly for the VO2+/VO2+ couple. Moreover, the developed electrode exhibited substantially improved energy efficiency (14% higher than that of pristine carbon felt) in the single cell vanadium redox flow battery. This outstanding performance was attributed to high surface area and abundant oxygen-containing linkages in the developed electrode.
In this study, a simple, rapid, and eco-friendly green method was introduced to synthesize magnetite nanoparticles (Fe3O4-NPs) successfully. Seaweed Kappaphycus alvarezii (K. alvarezii) was employed as a green reducing and stabilizing agents. The synthesized Fe3O4-NPs were characterized with X-ray diffraction (XRD), ultraviolet-visible spectroscopy (UV-Vis), Fourier transform infrared (FT-IR), and transmission electron microscopy (TEM) techniques. The X-ray diffraction planes at (220), (311), (400), (422), (511), (440), and (533) were corresponding to the standard Fe3O4 patterns, which showed the high purity and crystallinity of Fe3O4-NPs had been synthesized. Based on FT-IR analysis, two characteristic absorption peaks were observed at 556 and 423 cm(-1), which proved the existence of Fe3O4 in the prepared nanoparticles. TEM image displayed the synthesized Fe3O4-NPs were mostly in spherical shape with an average size of 14.7 nm.
Phospholipase A2 (Pla2) is an enzyme that induces inflammation, making Pla2 activity an effective approach to reduce inflammation. Therefore, investigating natural compounds for this Pla2 inhibitory activity has important therapeutic potential. The objective of this study was to investigate the potential in bromelain-phytochemical complex inhibitors via a combination of in silico and in vitro methods. Bromelain-amenthoflavone displays antagonistic effects on Pla2. Bromelian-asiaticoside and bromelain-diosgenin displayed synergistic effects at high concentrations of the combined compounds, with inhibition percentages of more than 70% and 90%, respectively, and antagonistic effects at low concentrations. The synergistic effect of the bromelain-asiaticoside and bromelain-diosgenin combinations represents a new application in treating inflammation. These findings not only provide significant quantitative data, but also provide an insight on valuable implications for the combined use of bromelain with asiaticoside and diosgenin in treating inflammation, and may help researchers develop more natural bioactive compounds in daily foods as anti-inflammatory agent.