Steam gasification of microalgae upon perovskite oxide-supported nickel (Ni) catalysts was carried out for H2-rich gas production. Ni-perovskite oxide catalysts with partial substitution of B in perovskite structures (Ni/CaZrO3, Ni/Ca(Zr0.8Ti0.2)O3, and Ni/Ca(Zr0.6Ti0.4)O3) were synthesized and compared with those of the Ni/Al2O3 catalyst. The perovskite oxide supports improved Ni dispersion by reducing the particle size and strengthening the Ni-support interaction. Higher gas yields and H2 selectivity were obtained using Ni-perovskite oxide catalysts rather than Ni/Al2O3. In particular, Ni/Ca(Zr0.8Ti0.2)O3 showed the highest activity and selectivity for H2 production because of the synergetic effect of metallic Ni and elements present in the perovskite structures caused by high catalytic activity coupled with enhanced oxygen mobility. Moreover, increasing the temperature promoted the yield of gas and H2 content. Overall, considering the outstanding advantages of perovskite oxides as supports for Ni catalysts is a promising prospect for H2 production via gasification technology.
This study highlights the potential of pyrolysis of food waste (FW) with Ni-based catalysts under CO2 atmosphere as an environmentally benign disposal technique. FW was pyrolyzed with homo-type Ni/Al2O3 (Ni-HO) or eggshell-type Ni/Al2O3 (Ni-EG) catalysts under flowing CO2 (50 mL/min) at temperatures from 500 to 700 °C for 1 h. A higher gas yield (42.05 wt%) and a lower condensable yield (36.28 wt%) were achieved for catalytic pyrolysis with Ni-EG than with Ni-HO (34.94 wt% and 40.06 wt%, respectively). In particular, the maximum volumetric content of H2 (21.48%) and CO (28.43%) and the lowest content of C2-C4 (19.22%) were obtained using the Ni-EG. The formation of cyclic species (e.g., benzene derivatives) in bio-oil was also effectively suppressed (24.87%) when the Ni-EG catalyst and CO2 medium were concurrently utilized for the FW pyrolysis. Accordingly, the simultaneous use of the Ni-EG catalyst and CO2 contributed to altering the carbon distribution of the pyrolytic products from condensable species to value-added gaseous products by facilitating ring-opening reactions and free radical mechanisms. This study should suggest that CO2-assisted catalytic pyrolysis over the Ni-EG catalyst would be an eco-friendly and sustainable strategy for disposal of FW which also provides a clean and high-quality source of energy.
Steam and air gasification with 5 wt% Ni/Al2O3 eggshell (Ni-EG) and homo (Ni-H) catalysts were performed for the first time to produce biohydrogen from food waste. The steam gasification produced comparably higher gas yield than air gasification. In non-catalytic experiments, steam gasification generated a higher volume percent of H2, whereas more CO, CO2, CH4, and C2-C4 were produced in air gasification. Ni-EG demonstrated higher potential to obtain H2-rich gases with a low C2-C4 content compared to that obtained by Ni-H, particularly in steam gasification at 800 °C, which produced gaseous products with 59.48 vol% H2. The long-term activity of both catalysts in steam gasification was evaluated, and Ni-EG exhibited higher stability than Ni-H. The ideal distribution of Ni species on the outer region of γ-Al2O3 pellets in Ni-EG resulted in higher activity, stability, and selectivity than Ni-H in both steam and air gasification.
In this study, nickel-loaded perovskite oxides catalysts were synthesized via the impregnation of 10%Ni on XTiO3 (X = Ce, Sr, La, Ba, Ca, and Fe) supports and employed in the catalytic steam gasification of swine manure to produce H2-rich syngas for the first time. The synthesized catalysts were characterized using BET, H2-TPR, XRD, HR-TEM, and EDX analysis. Briefly, using perovskite supports resulted in the production of ultrafine catalyst nanoparticles with a uniform dispersion of Ni particles. According to the catalytic activity test, the gas yield showed the increment as 10% Ni/LaTiO3 < 10% Ni/FeTiO3 < 10% Ni/CeTiO3 < 10% Ni/BaTiO3 < 10% Ni/SrTiO3 < 10% Ni/CaTiO3. Meanwhile, zero coke formation was achieved due to the oxygen mobility of prepared catalysts. Also, the increase in the H2 production for the applied catalysts was in the sequence as 10% Ni/CeTiO3 < 10% Ni/FeTiO3 < 10% Ni/LaTiO3 < 10% Ni/BaTiO3 < 10% Ni/SrTiO3 < 10% Ni/CaTiO3. The maximum H2 selectivity (∼48 vol%) obtained by10% Ni/CaTiO3 was probably due to the synergistic effect of Ni and Ti on enhancing the water-gas shift reaction, and Ca on creating the maximum oxygen mobility compared to other alkaline earth metals doped at the A place of perovskite. Overall, this study provides a suitable solution for enhanced H2 production through steam gasification of swine manure along with suggesting the appropriate supports to prevent Ni deactivation by lowering coke formation at the same time.
Air gasification of the Wood-Plastic Composite (WPC) was performed over Ni-loaded HZSM-5 catalysts to generate H2-rich gas. Increasing SiO2/Al2O3 ratio (SAR) of HZSM-5 adversely affected catalytic activity, where the highest gas yield (51.38 wt%) and H2 selectivity (27.01 vol%) were acquired using 20 %Ni/HZSM-5(30) than those produced over 20 %Ni/HZSM-5(80) and 20 %Ni/HZSM-5(280). Reducing SAR was also favorably conducive to increasing the acyclic at the expense of cyclic compounds in oil products. These phenomena are attributed to enhanced acid strength and Ni dispersion of 20 %Ni/HZSM-5(30) catalyst. Moreover, catalytic activity in the terms of gas yield and H2 selectivity enhanced with growing Ni loading to 20 %. Also, the addition of promoters (Cu and Ca) to 20 %Ni/HZSM-5(30) boosted the catalytic efficiency for H2-rich gas generation. Raising temperature indicated a positive relevance with the gas yield and H2 selectivity. WPC valorization via gasification technology would be an outstanding outlook in the terms of a waste-to-energy platform.