A combination of palm olein (POl) and fructose was used as carbon source for the biosynthesis of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(3HB-co-3HHx)] by recombinant Cupriavidus necator Re2058/pCB113. Cultures grown using 5g/L PO alone as carbon source produced cell dry weight (CDW) of 5.13g/L, 67% PHA/CDW and accumulated a copolymer containing 27mol% 3HHx in shake flask cultures. When cultures were grown in 5g/L fructose alone as the carbon source they produced CDW of 2.32g/L, 11% PHA/CDW and accumulated only poly(3-hydroxybutyrate) [P(3HB)] homopolymer. When the cells were cultured in 5g/L POl in combination with 7g/L fructose, CDW of 7.41g/L and 80% PHA/CDW was obtained with 17mol% 3HHx monomer fraction. Biosynthesis was carried out using a 13L fermenter to study the accumulation of 3HHx monomer fraction in the bacterial cells at different time point. The molecular weights of P(3HB-co-3HHx) with 4-15mol% 3HHx monomer were in the range between 5.47-6.85×105Da, which were at least two fold higher than previously reported values. Interestingly, the increase in Mwof the copolymer along with the increase in 3HHx molar fraction was observed. The viscoelastic property of the copolymer further confirmed the increase in Mw.
Thermally assisted hydrolysis and methylation-gas chromatography (THM-GC) in the presence of an organic alkali was validated for the compositional analysis of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(3HB-co-3HHx)] accumulated in whole bacterial cells. Recombinant Cupriavidus necator Re2058/pCB113 was grown in a batch fermentation with different concentration of palm oil and fructose in order to control the molar fraction of 3HHx in P(3HB-co-3HHx) produced in the cells. Trace amounts (30μg) of freeze-dried cells were directly subjected to THM-GC in the presence of tetramethylammonium hydroxide (TMAH) at 400°C. The obtained chromatograms clearly showed nine characteristic peaks, attributed to the THM products from 3HB and 3HHx units in the polymer chains, without any appreciable interference by the bacterial matrix components. Based on these peak intensities, the copolymer compositions were determined rapidly without using any cumbersome and lengthy sample pretreatment as in conventional GC method. Moreover, the compositions thus obtained were strongly correlated with those by NMR and conventional GC involving solvent extraction.
Carbon dioxide assisted particle formation combined with electrospraying using supercritical CO2 (scCO2) as an aid (Carbon Dioxide Assisted Nebulization-Electrodeposition, CAN-ED) was used to produce Bortezomib loaded poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) P(3HB-co-3HHx) nanoparticles for sustained release. The morphology and structure of the prepared nanoparticles were investigated by SEM, TEM and FT-IR spectroscopy. Average diameter of particles obtained was 155nm and the average core sizes of P(3HB-co-3HHx) nanoparticles were between 6 and 13nm. The drug loading capacity, drug release and stability of Bortezomib loaded P(3HB-co-3HHx) nanoparticles were analyzed. The maximum loading capacity was achieved at pH=6.0 in phosphate buffer (K2HPO4/KH2PO4). It was found that temperature did not affect the stability of Bortezomib loaded nanoparticles and it was good both at 37°C and 4°C. This study pointed out that CAN-ED is a green method to produce P(3HB-co-3HHx) nanoparticles for pH responsive targeting of Bortezomib especially to parts of the body where size exclusion is not crucial.
A simple, efficient and economical method for the recovery of P(3HB-co-3HHx) was developed using various chemicals and parameters. The initial content of P(3HB-co-3HHx) in bacterial cells was 50-60 wt%, whereas the monomer composition of 3HHx used in this experiments was 3-5 mol%. It was found that sodium hydroxide (NaOH) was the most effective chemical for the recovery of biodegradable polymer. High polyhydroxyalkanoate purity and recovery yield both in the range of 80-90 wt% were obtained when 10-30 mg/ml of cells were incubated in NaOH at the concentration of 0.1 M for 60-180 min at 30 °C and polished using 20 % (v/v) of ethanol.
Palm kernel oil, palm olein, crude palm oil and palm acid oil were used for the synthesis of poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(3HB-co-3HHx)] by a mutant strain of Wautersia eutropha (formerly Ralstonia eutropha) harboring the Aeromonas caviae polyhydroxyalkanoate (PHA) synthase gene. Palm kernel oil was an excellent carbon source for the production of cell biomass and P(3HB-co-3HHx). About 87% (w/w) of the cell dry weight as P(3HB-co-3HHx) was obtained using 5 g palm kernel oil/l. Gravimetric and microscopic analyses further confirmed the high PHA content in the recombinant cells. The molar fraction of 3HHx remained constant at 5 mol % regardless of the type and concentration of palm oil products used. The small amount of 3HHx units was confirmed by 13C NMR analysis. The number average molecular weight (M(n)) of the PHA copolymer produced from the various palm oil products ranged from 27 0000 to 46 0000 Da. The polydispersity was in the range of 2.6-3.9.