Graft copolymerisation of methyl methacrylate (MMA) onto Agave angustifolia was conducted with ceric ammonium nitrate (CAN) as the redox initiator. The maximum grafting efficiency was observed at CAN and MMA concentrations of 0.91 × 10(-3) and 5.63 × 10(-2)M, respectively, at 45°C for 3h reaction time. Four characteristic peaks at 2995, 1738, 1440, and 845 cm(-1), attributed to PMMA, were found in the IR spectrum of grafted cellulose. The crystallinity index dropped from 0.74 to 0.46, while the thermal stability improved upon grafting. The water contact angle increased with grafting yield, indicating increased hydrophobicity of cellulose. SEM images showed the grafted cellulose to be enlarged and rougher. The changes in the physical nature of PMMA-grafted cellulose can be attributed to the PMMA grafting in the amorphous regions of cellulose, causing it to expand at the expense of the crystalline component.
Infection after joint replacement surgery is problematic and difficult to treat. The utility of antibiotic laden bone cement for reduction of risk of infection in primary and revision joint replacement surgery has already been established in many studies. In this study, we examined the efficacy of bone cement containing cefuroxime, employing a modified in vitro Kirby-Bauer susceptibility model for investigation of 13 strains of organisms that are found in orthopaedic infections. Organisms investigated were broad spectrum and effective for Gram-positive, Gram-negative, aerobic organisms and anaerobes. Simplex P with added cefuroxime was effective against 8 out of 13 strains. Cefuroxime is stable during exothermic polymerisation of the cement, and is released from the cement at concentrations high enough to inhibit the growth of most organisms encountered after joint arthroplasty.
A new crosslinked chitosan grafted with methyl methacrylate (M-CTS) adsorbent was synthesized via free radical polymerization for effective removal of Cu(II) ions from aqueous solution. Crosslinked chitosan (1 g) was grafted with 29.96 × 10-1 M methyl methacrylate in the presence of 2.63 × 10-1 M ammonium persulfate as initiator at 60 °C for 2 h to give grafting and yield percentages of 201% and 67%, respectively. Batch adsorption experiment was performed as a function of solution pH, initial metal ion concentration and contact time. The isotherm data were adequately described by Langmuir model, while kinetic study revealed that the pseudo-second order rate model best fitted for the experimental data. The maximum adsorption capacity for M-CTS at pH 4 was 192.31 mg g-1. Furthermore, the reusability of over six adsorption-desorption cycles suggested that M-CTS is a durable adsorbent and good candidate for metal ions treatment.
In this study, modified agave cellulose fibre combined by graft copolymerisation with methylmethacrylate was tested as a potential reinforcement for polylactic acid (PLA)-natural rubber/liquid natural rubber blends. Mechanical, morphological, thermal, wetting, and biodegradation characterisations were performed to assess the influence of cellulose-graft-polymethylmethacrylate (cell-g-PMMA) content on the properties of biocomposites. The addition of cell-g-PMMA improved the mechanical properties of the composites because of the chemical interaction between PLA and PMMA. Thermal stability decreased slightly upon cell-g-PMMA addition because of the low thermal stability of PMMA. A soil burial test revealed that the degradation of composites decreased with an increase in the cell-g-PMMA content. However, the weight loss after burial, which directly affected the water absorption capacity, was still higher for the cell-g-PMMA composites than for the polymer alone.
Introduction: Insulin is given by injection, because when administered orally, it would be destroyed by enzymes in the digestive system, hence only about 0.1% reaches blood circulation. The purpose of the present study was to use pH sensitive polyelectrolyte methyl methacrylate (MMA)/itaconic acid (IA) nanogels as carriers in an attempt to improve absorption of insulin administered orally. Methods: Insulin (Ins) was incorporated into the MMA/IA nanogels (NGs) using the polyelectrolyte complexation (PEC) method to form Ins/NGs-PEC. Several parameters, including Ins:NGs ratio, pH, incubation time and stirring rate were optimized during preparation of InsNGs-PEC. The prepared formulations were characterized in terms of particle size (PS), polydispersity index (PdI), zeta potential (ZP) and percent entrapment efficiency (% EE). Results: The optimized InF12 nanogels had a PS, PdI, ZP and %EE of 190.43 nm, 0.186, -16.70 mV and 85.20%, respectively. The InF12 nanogels were lyophilized in the presence of different concentrations of trehalose as cryoprotectant. The lyophilized InF12 containing 2%w/v trahalose (InF12-Tre2 nanogels) was chosen as final formulation which had a PS, PdI, ZP and %EE of 430.50 nm, 0.588, -16.50 mv and 82.10, respectively. The in vitro release of insulin from InF12-Tre2 nanogels in the SGF and SIF were 28.71% and 96.53%, respectively. The stability study conducted at 5±3°C for 3 months showed that lnF12-Tre2 nanogels were stable. The SDS-PAGE assay indicated that the primary structure of insulin in the lnF12-Tre2 nanogels was intact. The in-vivo study in the diabetic rats following oral administration of InF12-Tre2 nanogels at a dose of 100 IU/kg body weight reduced blood glucose level significantly to 51.10% after 6 hours compared to the control groups. Conclusions: The pH sensitive MMA/IA nanogels are potential carriers for oral delivery of insulin as they enhanced the absorption of the drug.