A preliminary study was carried out to fabricate a three electrode system based on electrochemical sensoring. The cyclic voltammetry (CV) technique was chosen to select the type of metal suitable for evaporation and to compare the results produced from the fabricated gold electrode with the conventional macro-electrode system. The methodology and apparatus used involved low cost apparatus and methodology such as soft lithography, wet-etching, thermal evaporation, direct current sputtering, polymethylmethacrylate moulding and polydimethylsiloxane coating. The experiment was conducted at a fixed scan rate of 100 mV/s by using 0.01 M K3Fe(CN)6 in 0.1M KCl and well known method using Randles-Sevcik equation, peak current ratio and voltage separation was used to analyze the characterization on the fabricated sensors. Electrodes of 6.5 mm2 and 0.26 mm2 were fabricated to prove the adsorption effect of the reactant and the influence of the electrode area on the value of the peak current. CV analysis proved that the fabricated sensor was reliable for a range of 24 h at 25ºC room temperature.