METHODS: This article was divided into the following parts: Part 1 Surface roughness and substance loss: an in vitro study, which involves intact extracted teeth sectioned and treated using a piezoelectric ultrasonic device (PM200 EMS Piezon, Switzerland) with a conventional scaler tip (FS-407) and a Perio Slim (PS) scaler tip (Perio Slim DS-016A). All sectioned samples for tooth surface roughness (n = 20) and tooth substance loss (n = 46) analyses were measured and compared using a 3D surface texture analyser and scanning electron microscope (SEM) respectively, at baseline and following scaling. Part 2 Pain Perception: a clinical study, which was a split mouth study design including 30 participants with gingivitis and/or mild chronic periodontitis; treated with supra-gingival scaling from teeth #13 to #23. Subjects were randomised to group A or group B. Group A was treated first with PS scaler tips, whereas group B was treated first with conventional scaler tips. Pain perception was recorded using the visual analogue scale (VAS).
RESULTS: In vitro study: both scaler tips caused significant reduction in root substance roughness after scaling (p 0.05) was observed. The PS scaler tip caused statistically significantly less root substance loss (p
METHODS: Four groups [WMTA, RMPC, fast-set WMTA (FS-WMTA) and fast-set RMPC (FS-RMPC)] were prepared. Initial setting time was evaluated using Vicat apparatus. The pH was measured at seven-day intervals. For discolouration potential, cements were packed in the pulp chamber of 46 extracted maxillary incisors. Spectrophotometric readings were obtained at seven-day intervals, and the rate of colour change (ΔE) was recorded. For the push-out bond strength testing, cements were applied in 48 sectioned root samples, and the test was performed using universal testing machine at crosshead speed of 0.5 mm/min until bond failure. Statistical analysis was done according to the nature of each group of data using SPSS 26.
RESULTS: Addition of CaCl2.2H2O decreased the initial setting times of both RMPC and WMTA significantly (p<0.05). The pH values of FS-WMTA and FS-RMPC were comparable to their non-accelerated counterparts ranging from 10 to 12. Discolouration effect was more obviously observed with WMTA and FS-WMTA with time compared to RMPC formulations. Push-out bond strength of the two materials also showed an increase with the addition of the accelerator, however, only FS-WMTA showed statistically significant difference compared to WMTA (p<0.05).
CONCLUSION: The addition of CaCl2.2H2O improves the physical and mechanical properties of the newly formulated RMPC and WMTA. The RMPC formulation overcomes the discolouration potential of WMTA. (EEJ-2022-12-155).
MATERIALS AND METHODS: The HVGICs evaluated were Zirconomer [ZR] (Shofu), Equia Forte [EQ] (GC) and Riva [RV] (SDI). Sixty specimens (12mm x 2mm x 2mm) of each material were fabricated using customized Teflon molds. After initial set, the specimens were removed from their molds, finished, measured and randomly divided into 3 groups of 20. Half the specimens in each group were left uncoated while the remaining half was covered with the respective manufacturers' resin coating. The specimens were subsequently conditioned in distilled water, artificial saliva or citric acid at 37°C for 7 days. The uncoated and coated specimens (n=10) were then subjected to dynamic mechanical testing in flexure mode at 37°C with a frequency of 0.1 to 10Hz. Storage modulus, loss modulus and loss tangent data were subjected to normality testing and statistical analysis using one-way ANOVA/Scheffe's post-hoc test and Ttest at significance level p<0.05.
RESULTS: Mean storage modulus ranged from 1.39 ± 0.36 to 10.80 ± 0.86 GPa while mean loss modulus varied from 0.13 ± 0.03 to 0.70 ± 0.14 GPa after conditioning in the different mediums. Values for loss tangent ranged from 39.4 ± 7.75 to 213.2 ± 20.11 (x10 -3 ). Significant differences in visco-elastic properties were observed between mediums and materials. When conditioned in distilled water and artificial saliva,storage modulus was significantly improved when ZR, EQ and RV were uncoated. Significantly higher values were, however, observed with resin coating when the materials were exposed to citric acid.
CONCLUSION: The visco-elastic properties of HVGICs were influenced by both resin coating and chemical environment.