We conducted a prospective study in order to audit our experience of repairing cranial defects using Methyl methacrylate. This included a total of 49 patients undergoing cranioplasty using methyl methacrylate, of which 45 were males and 4 females. The age of patients at the time of surgery ranged from 16 to 40 years old, with an average of 24 years. Malays were the majority (67%), followed by Chinese (23%) and Indian (10%). Cranial defects were mainly caused by motor vehicle accident (94%), while gunshot wounds, industrial accidents and tumours, each contribute 2%. Bone flaps were commonly removed during previous surgery related to traumatic subdural haemorrhage (33%), contusion (21%) and intracerebral haemorrhage (14%). The size of cranial defects ranged from 28 cm2 to 440 cm2, with an average of 201 cm2. Most had right sided (55%) and lateral defects [temporoparietal (52%) followed by temporal (16%), frontal (16%), frontotemporal (14%) and occipital (2%)]. Duration of surgery ranged from 70 to 275 minutes, with an average of 135 minutes. Nine of 12 patients (75%) with neurological disability had some improvement while 85% of symptomatic patients had symptoms improvement after cranioplasty. The infection rate in this series was 4%.
This study investigated the impact of calcium silicate (CS) content on composition, compressive mechanical properties, and hardness of CS cermets with Ti-55Ni and Ti-6Al-4V alloys sintered at 1200°C. The powder metallurgy route was exploited to prepare the cermets. New phases of materials of Ni16Ti6Si7, CaTiO3, and Ni31Si12 appeared in cermet of Ti-55Ni with CS and in cermet of Ti-6Al-4V with CS, the new phases Ti5Si3, Ti2O, and CaTiO3, which were emerged during sintering at different CS content (wt%). The minimum shrinkage and density were observed in both groups of cermets for the 50 and 100 wt% CS content, respectively. The cermets with 40 wt% of CS had minimum compressive Young's modulus. The minimum of compressive strength and strain percentage at maximum load were revealed in cermets with 50 and 40 wt% of CS with Ti-55Ni and Ti-6Al-4V cermets, respectively. The cermets with 80 and 90 wt% of CS showed more plasticity than the pure CS. It concluded that the composition and mechanical properties of sintered cermets of Ti-55Ni and Ti-6Al-4V with CS significantly depend on the CS content in raw cermet materials. Thus, the different mechanical properties of the cermets can be used as potential materials for different hard tissues replacements.
Recently, a modified form of a three-dimension (3D) porous poly(caprolactone-trifumarate) (PCLTF) scaffold has been produced using a fabrication technique that involves gelatin microparticles porogen leaching. This poly(caprolactone trifumarate-gelatin microparticles) (PCLTF-GMPs) scaffold has been shown to be biocompatible, more flowable clinically, and has a shorter degradation time as compared to its existing predecessors. In this report, a detailed characterization of this new scaffold was performed by testing its cytocompatibility, analyzing the surface topography, and understanding its thermal, physical and mechanical properties. The result showed that the PCLTF-GMPs has no critical cytotoxic effect. To confirm improvement, the surface properties were compared against the older version of PCLTF fabricated using salt porogen leaching. This PCLTF-GMPs scaffold showed no significant difference (unpaired t-test; p>0.05) in mechanical properties before and after gelatin leaching. However, it is mechanically weaker when compared to its predecessors. It has a high biodegradability rate of 16weeks. The pore size produced ranges from 40 to 300μm, and the RMS roughness is 613.7±236.9nm. These characteristics are condusive for osteoblast in-growth, as observed by the extension of filopodia across the macropores. Overall, this newly produced material has good thermal, physical and mechanical properties that complements its biocompatibility and ease of use.