Acetone soluble oil palm empty fruit bunch cellulose acetate (OPEFB-CA) of DS 2.52 has been successfully synthesized in a one-step heterogeneous acetylation of OPEFB cellulose without necessitating the hydrolysis stage. This has only been made possible by the mathematical modeling of the acetylation process by manipulating the variables of reaction time and acetic anhydride/cellulose ratio (RR). The obtained model was verified by experimental data with an error of less than 2.5%. NMR analysis showed that the distribution of the acetyl moiety among the three OH groups of cellulose indicates a preference at the C6 position, followed by C3 and C2. XRD revealed that OPEFB-CA is highly amorphous with a degree of crystallinity estimated to be ca. 6.41% as determined from DSC. The OPEFB-CA films exhibited good mechanical properties being their tensile strength and Young's modulus higher than those of the commercial CA.
The use of dielectric property measurements to define specific trends in the molecular structures of poly(caprolactone) containing star polymers and/or the interbatch repeatability of the synthetic procedures used to generate them is demonstrated. The magnitude of the dielectric property value is shown to accurately reflect: (a) the number of functional groups within a series of materials with similar molecular size when no additional intermolecular order is present in the medium, (b) the polymer molecular size for a series of materials containing a fixed core material and so functional group number, and/or (c) the batch to batch repeatability of the synthesis method. The dielectric measurements are validated by comparison to spectroscopic/chromatographic data.
Hydroxyapatite powder was mechanochemically synthesized from calcium pyrophosphate (Ca2P2O7) and calcium carbonate (CaCO3) using a solid-state reaction. The two powders were mixed in distilled water, milled for 8 hours, dried and calcined at 1100 degrees C for 1 hour. The phase(s) formed was analyzed by x-ray diffraction (XRD). It was found that hydroxyapatite was not the only one formed. This result will be used as the starting point to produce a single-phase hydroxyapatite in terms of excess hydroxyl group in a mechanochemical reaction.
Hydroxyapatite (HA) has been earmarked as suitable for implantation within the human of its chemical makeup to human bone. In this paper, HA powders were synthesized via the precipitation method where phosphoric acid (H3PO4) was titrated into calcium hydroxide solution [Ca(OH)2]. Two parameters such as temperature and stirring rate were identified as factors that influenced the amount and purity of HA powder. Phase identification of the synthesized powder was done using X-Ray Diffraction (XRD). The results show that HA phase can be synthesized from this titration process of Ca(OH)2 and H3PO4 with yield amount of HA powder around 45 - 61 grams but with less than hundred percent purity. In order to study the effect of heat treatment to HA crystals structure, HA powder was calcined at 850 degrees C for 2 hours. It's found that the degree of crystallinity increases after calcination because of lattice expansion when the materials were heated at higher temperature