MATERIALS AND METHODS: Tristar Trubalance aligner sheets were used to fabricate the CAs. Thirty-four resin models were 3D printed and 17 each, were bonded with ellipsoidal or rectangular attachments on maxillary right central incisors. Fuji Prescale pressure film was used to measure the force generated by the attachment of CA. The images of colour density produced on the films were processed using a calibrated pressure mapping system utilising image processing techniques and topographical force mapping to quantify the force. The force measurement process was repeated after the flash was removed from the attachment using tungsten-carbide bur on a slow-speed handpiece.

MATERIALS AND METHODS: Sixmaster dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Ten copings of 0.6 mm thickness were fabricated from each type of ceramic, for a total of thirty copings. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented with resin luting cement Panavia F according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.

RESULTS: The results of the present study showed the following mean loads at fracture: Turkom-Cera (2184 +/- 164 N), In-Ceram (2042 +/- 200 N), and Procera AllCeram (1954 +/- 211 N). ANOVA and Scheffe's post hoc test showed that the mean load at fracture of Turkom-Cera was significantly different from Procera AllCeram (p < 0.05). Scheffe's post hoc test showed no significant difference between the mean load at fracture of Turkom-Cera and In-Ceram or between the mean load at fracture of In-Ceram and Procera AllCeram.

OBJECTIVES: The aim of the study was to evaluate the effect of fiber post location on fracture resistance and failure mode of endodontically treated premolars with 2 roots.

MATERIAL AND METHODS: Fifty extracted maxillary first premolars with 2 roots were divided randomly into 5 groups. Group 1 was comprised of sound teeth, which received only metal crowns (control). Teeth from groups 2, 3, 4, and 5 were decoronated 2 mm above the cementoenamel junction (CEJ) and were endodontically treated. No post was placed in group 2 teeth. Teeth from groups 3, 4 and 5 were given a fiber post placed in the buccal canal, palatal canal, and both buccal and palatal canals, respectively. All teeth in groups 2, 3, 4, and 5 were built up with composite and full coverage metal crowns. A compressive static load was applied at an angle of 25° to the crowns with a crosshead speed of 0.5 mm/min, until fracture.

RESULTS: One-way analysis of variance (ANOVA) showed significant differences among the groups (p = 0.002). A post hoc test showed significantly lower fracture resistance of group 4 compared to group 5 (p = 0.011). Furthermore, group 2 had significantly less fracture resistance compared to group 1 (p = 0.021) and group 5 (p = 0.002). According to Fisher's exact test, different post locations are non-significantly associated with fracture mode (p = 0.256).

OBJECTIVES: The aim of the present article was to review the current literature on the fracture loads and fracture modes of SRCR implant restorations - in vitro studies, and also studies demonstrating the clinical performance of such design.

MATERIAL AND METHODS: A literature search was conducted from January 2000 to June 2022, using 6 databases to identify studies on fracture load and clinical performance that fulfilled the eligibility criteria. Thirty-eight studies met the inclusion criteria (22 in vitro and16 in vivo). The in vivo studies comprised case reports/series/letters (9), clinical techniques (2), retrospective/prospective studies (3), and randomized controlled trials (RCTs) (2).

RESULTS: The reviewed articles reported the effects of the SRCR design on the fracture risk if screw access channels were filled or unfilled, with regard to their diameter, and the preparation before or after glazing. The effect of the type of material used in the construction on the fracture modes SRCR restorations was also reported. The long-term clinical data was mainly retrospective and referred to metal-ceramic constructions. Limited long-term clinical data was available for all-ceramic materials and high-performance polymers (HPPs).

PURPOSE: The purpose of this in vitro study was to incorporate microparticles into a commercially available 3D printed denture base resin and compare its mechanical and biological properties with the conventional polymethyl methacrylate (PMMA) denture base material.

MATERIAL AND METHODS: Microparticles were collected from milled zirconia blanks and were blended with a 3D printing denture base resin (NextDent Denture 3D+). The optimal zirconia microparticle content (2%) for blending and printed was determined by using a liquid-crystal display (LCD) 3D printer. The printed specimens were then postrinsed and postpolymerized based on the manufacturer's instructions. Mechanical and biological characterization were carried out in terms of flexural strength, fracture toughness, and fungal adhesion. One-way ANOVA was carried out to analyze the results statistically.

METHODS: Sixty-four extracted mandibular molars were root-treated and lined with flowable composite (1.5 mm thickness) before being embedded in epoxy resin blocks. The samples were divided into four groups (n = 16): three endocrown groups with different preparation designs (butt-joint, 0.8 mm chamfer, and 1.0 mm shoulder) and one group with conventional crowns. Crown preparations were performed with a high-speed handpiece mounted on a modified milling device, targeting a 2.0 mm anatomical occlusal reduction for conventional crowns and a 4.0 mm central chamber depth with a 2.0 mm axial wall height (ferrule) for endocrowns (except the butt-joint design, which had no ferrule preparation). Restorations were fabricated using the Chairside Economical Restoration of Esthetic Ceramics (CEREC) Computer-Aided Design and Computer-Aided Manufacturing (CAD/CAM) system with lithium disilicate (IPS e.max CAD; minimum occlusal thickness: 1.5 mm) as the restorative material and cemented with the RelyX Ultimate dual-cure resin adhesive. After 1,500 thermocycling cycles, the samples were divided into two subgroups (n = 8) for axial and oblique loading tests. The fracture resistance was tested using a universal testing machine at a crosshead speed of 0.5 mm/min, applying a load of up to 5,000 N until fracture. Failure modes were examined using a stereomicroscope at 5x magnification and categorized as catastrophic or non-catastrophic. The mean fracture resistance was compared using one-way Analysis of Variance (ANOVA) with Bonferroni post-hoc tests, and Fisher's exact test was used to assess the association between preparation designs and failure modes (p < 0.05).

RESULTS: Endocrowns with shoulder margins showed significantly higher fracture resistance (3,042.83 ± 850.76 N) than conventional crowns (1,908.28 ± 635.82 N) under axial loading (p = 0.02). No significant differences were found under oblique loading between the preparation designs. The preparation design significantly influenced the failure mode under axial loading (p = 0.049). Endocrowns exhibited a higher rate of catastrophic fractures than conventional crowns, regardless of loading direction.

METHODS: 75 human mandibular molars were randomly divided into five equal groups. Teeth were standardized, endodontically-treated and restored according the assigned group as follows: amalgam core only, prefabricated titanium post in the distal canal and amalgam core, composite core only; fiber post in the distal canal and composite core. One group of untreated sound teeth was used as a control. Non-precious metal crowns were fabricated and cemented on the prepared specimens with Rely X U200 resin cement. All specimens were subjected to a compressive load at crosshead speed 0.5 mm/minute, 25° to the long axis of the tooth. Failure loads and modes were recorded.

RESULTS: Mean failure loads among the groups were significantly different (P= 0.035). Post-hoc multiple pair-wise comparisons revealed the amalgam core and composite core groups produced significantly lower fracture resistance than the control group (P= 0.041 and P= 0.025, respectively) and no significant differences among the different intra-radicular techniques (P> 0.05). The composite core with fiber post and amalgam core with titanium posts showed the highest percentage of favorable failures (67%) and non-favorable failures (87%) respectively.