Solid polymer electrolyte based on methyl cellulose (MC)-lithium triflate (LiCF3SO3) plasticised with ethylene carbonate (EC) was prepared using solution cast technique. The X-ray diffraction (XRD) studies proved that the amorphous nature of the electrolyte systems was increases due to the addition of salt and plasticiser. The improved surface morphology of plasticised polymer system ensures it has good electrode-electrolyte contact during performance testing. The polymer electrolyte was found to have high thermal stability indicating that the electrolyte can be used at higher temperature. The ionic conductivity increased up to 1.24 x 10-4 S cm-1 at optimum amount of EC plasticiser associated to the effect of plasticiser that initially leads to the formation of Li+-EC complex. Consequently, it reduces the fraction of polymer-Li+ complex which contributes to the increase of the segmental chain flexibility in the plasticized system. Temperature dependent studies indicate ionic conductivity increase due to the temperature increase and is in line with Arrhenius behaviour pattern. An activation energy of 0.26 eV at highest conductivity sample was obtained. The addition of plasticiser lowers the activation energy thus increasing the ion mobility of the system and contributing to ionic conductivity increment. The plasticization method is a promising means to dealing with the solid polymer electrolyte problem and producing electrolytes that meet the needs of electrochemical devices.