This study was carried out to investigate the electrical properties of YBCO sample as superconductor
and the effect of addition of Co3O4 on the superconducting properties of YBCO superconductor. The
YBCO sample was prepared by solid state reaction route. The samples were prepared by each with
weight percentage of cobalt oxide of x= 0.00, x= 0.01, x= 0.02 and x= 0.03. Electrical Conduction by
Multimeter, Fourier Transform Infrared (FTIR), Critical temperature (Tc) measurement, X-ray
Diffraction (XRD), and Scanning Electron Microscopy (SEM) were conducted for analysis.
Multimeter showed all samples were in electric conduction, FTIR showed that carbonyl compound in
the sample was removed after calcinations. Tc measurement showed that the critical temperature of
sample of x= 0.02 was increased compared to sample of x= 0.00. XRD showed all samples have
orthorhombic structure and SEM showed that the grain size was increased as increased the cobalt
addition in YBCO superconductor. Besides, the EDX also showed the composition of elements
YBCO were tally with chemicals used for pure YBCO and addition cobalt oxide into YBCO
superconductor.