MATERIALS AND METHODS: Forty discs each of Fuji LX, Fuji VII and of Vitrebond were prepared in a plastic mould. Twenty discs of each material were coated for 30 seconds with a 10% solution of AgF. Five discs each of coated and uncoated material were placed individually in 4m1 of differing eluant solutions. The eluant solutions comprised deionized distilled water (DDW) and three separate acetate buffered solutions at pH 7, pH 5 and pH 3. After 30 minutes the discs were removed and placed in five vials containing 4m1 of the various solutions for a further 30 minutes. This was repeated for further intervals of time up to 216 hours, and all eluant solutions were stored. Fluoride concentrations in the eluant solutions were estimated using a fluoride specific electrode, with TISAB IV as a metal ion complexing and ionic concentration adjustment agent. Cumulative fluoride release patterns were determined from the incremental data.

RESULTS: The coating of AgF greatly enhanced the level of fluoride ion release from all materials tested. Of the uncoated samples, Vitrehond released the greater concentrations of fluoride ion, followed by Fuji VII. However, cumulative levels of fluoride released from coated samples of the GICs almost matched those from coated Vitrebond.

METHODS: Six master dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Thirty copings (Procera AllCeram) of 0.6-mm thickness were manufactured. Three types of luting media were used: zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and dual-cured composite resin cement (Panavia F). Ten copings were cemented with each type. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.

RESULTS: ANOVA revealed significant differences in the load at fracture among the three groups (p < 0.001). The fracture strength results showed that the mean fracture strength of zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and resin luting cement (Panavia F) were 1091.9 N, 784.8 N, and 1953.5 N, respectively.

Objectives: The aim of this study is to evaluate the efficacy of dentin bonding agent (DBA) in preventing coronal discoloration caused by four different root canal sealers- MTA Fillapex, Sealapex, Zical and Z. O. B seal at different time intervals by measuring chromatic alterations using digital images analysis method.

Methodology: Ninety mandibular premolars were collected and sectioned at 1 mm below the cementoenamel junction. Standard access cavity preparations of dimensions (depth-3 mm, width-0.8 mm, and length-3 mm) were prepared with a No. 245 bur through the cervical access. Following the standard irrigation protocol, specimens were then randomly divided into nine groups (four groups without DBA [1-4] +4 groups with DBA [5-8] +1 negative control [9]). In Groups 1-4, four different root canal sealers (MTA Fillapex, Sealapex, Zical, and Z.O.B seal) were applied to the walls of the pulp chamber. For Groups 5-8, the samples were etched with 37% phosphoric acid and DBA application was done before the respective root canal sealer application. The cervical access in all specimens was sealed using glass ionomer cement. Digital photographs were taken under standard lighting and environmental conditions at different time intervals: preprocedural, postprocedural, and after 1, 2, 3, and 4 months. These images were analyzed using Adobe Photoshop CS6 from which laboratory values and subsequently Delta E values were obtained.

Results: Statistical analysis performed using repeated measures ANOVA and post hoc Tukey's tests show that the groups with DBA application had significantly lower mean Delta E values (P < 0.05) compared to the groups without DBA application.