316L stainless steel is a common biomedical material. Currently, biomedical parts are produced through powder injection molding (PIM). Carbon control is the most critical in PIM. Improper debinding can significantly change the properties of the final product. In this work, thermal debinding and sintering were performed in two different furnaces (i.e. laboratory and commercially available furnaces) to study the mechanical properties and corrosion resistance. Debounded samples were sintered in different atmospheres. The samples sintered in inert gas showed enhanced mechanical properties compared with wrought 316L stainless steel and higher corrosion rate than those sintered in the vacuum furnace. The densification and tensile strength of the hydrogen sintered samples increased up to 3% and 51%, respectively, compared with those of the vacuum-sintered samples. However, the samples sintered in inert gas also exhibited reduced ductility and corrosion resistance. This finding is attributed to the presence of residual carbon in debonded samples during debinding.
The incorporation of kenaf fiber fillers into a polymer matrix has been pronounced in the past few decades. In this study, the effect of multiwalled carbon nanotubes (MWCNTs) with a short kenaf fiber (20 mesh) with polypropylene (PP) added was investigated. The melt blending process was performed using an internal mixer to produce polymer composites with different filler contents, while the suitability of this melt composite for the injection molding process was evaluated. Thermogravimetric analysis (TGA) was carried out to investigate the thermal stability of the raw materials. Rheological analyses were conducted by varying the temperature, load factor, and filler content. The results demonstrate a non-Newtonian pseudoplastic behavior in all samples with changed kenaf fillers (10 to 40 wt %) and MWCNT contents (1 to 4 wt %), which confirm the suitability of the feedstock for the injection molding process. The addition of MWCNTs had an immense effect on the viscosity and an enormous reduction in the feedstock flow behavior. The main contribution of this work is the comprehensive observation of the rheological characteristics of newly produced short PP/kenaf composites that were altered after MWCNT additions. This study also presented an adverse effect on the composites containing MWCNTs, indicating a hydrophilic property with improved water absorption stability and the low flammability effect of PP/kenaf/MWCNT composites. This PP/kenaf/MWCNT green composite produced through the injection molding technique has great potential to be used as car components in the automotive industry.
Titanium-ceramic composites are potential implant material candidates because of their unique mechanical properties and biocompatibility. This review focused on the latest advancement in processing of titanium-ceramic materials. Previously, titanium-ceramic incorporated using different coating techniques, i.e., plasma spraying and electrophoretic depositions, to enhance the biocompatibility of the implants. A major drawback in these coating methods is the growth of tissue at only the surface of the composite and might peel off over time. Recently, metal-ceramic composite was introduced via powder metallurgy method such as powder injection moulding. A porous structure can be obtained via powder metallurgy. Producing a porous titanium-ceramic structure would improve the mechanical properties, biocompatibility and tissue growth within the structure. Hence, further research needed to be done by considering the potential of powder injection moulding method which offer lower costs and more complex shapes for future implant.
The use of kenaf fiber as a reinforcement material for polymer composites is gaining popularity, especially in the production of automotive components. The main objective of this current work is to relate the effect of alkali treatment on the single fiber itself and the composite material simultaneously. The effect of temperature condition during mechanical testing is also investigated. Composite materials with discontinuous natural kenaf fibers and epoxy resin were fabricated using a compression moulding process. The epoxy composites were reinforced with 50 wt% untreated and treated kenaf fibers. The kenaf fiber was treated with NaOH solution (6% by weight) for 24 h at room temperature. Kenaf fiber treated with NaOH treatment had a clean surface and no impurities. For the first time we can see that alkali treatment had a damaging effect on the mechanical properties of kenaf fibers itself and the treated kenaf/epoxy composites. The composite reinforced with untreated kenaf fiber and treated kenaf fiber showed increased tensile strength (72.85% and 12.97%, respectively) compared to the neat epoxy. Reinforcement of the composite with treated kenaf fiber decreased the tensile strength due to the fiber pull out and the formation of voids which weakens the adhesion between the fibers and matrix. The temperature conditions also play an important role in composites with a significant impact on the deterioration of composite materials. Treated kenaf fiber has thermal stability and is not sensitive to temperature and as a result reinforcement with treated kenaf gives a lower loss value of 76%.
The micro-scale joining of two different materials using two-component micro-powder injection molding (2C-µPIM) is an intriguing technique. The formation of defects in bi-materials at different processing stages makes this technique challenging. This study presents the fabrication of defect-free bi-material micro-parts containing hydroxyapatite (HA) and 3 mol% yttria-stabilized zirconia (3YSZ) via 2C-µPIM. Critical powder volume concentrations (CPVCs) of 61.7 vol% and 47.1 vol% were obtained for the HA and 3YSZ powders, respectively. Based on the CPVCs, the optimal loadings for the HA and 3YSZ powders were selected as 60 vol% and 45 vol%, respectively. The HA and 3YSZ feedstocks were prepared by separately mixing the optimal powder contents with low-density polyethylene (LDPE) and palm stearin binders. The feedstocks displayed pseudoplastic behavior, and the lowest ranges of viscosity for the HA and 3YSZ at a temperature of 180 °C were 157.1-1392.5 Pa·s and 726.2-985.5 Pa·s, respectively. The feedstocks were injected to produce green HA/3YSZ micro-sized components. It was found that a solvent debinding temperature of 70 °C removed 60.6% of the palm stearin binder from the sample. In the thermal debinding stage, the open channels that formed in the bi-material sample's solvent debound at 70 °C and contributed to the removal of 93 to 95% of the binder system. When the debound bi-materials were sintered at 1300 °C, the highest relative density of 96.3% was obtained. The sintering operation revealed a linear shrinkage between 13 and 17% in the sintered HA/3YSZ micro-parts.
The combination of metallic bio-inert material, stainless-steel 316L (SS316L) and a bio-active material, hydroxyapatite (HA) can produce a composite which has superior properties for orthopaedic applications. The main objective of this study is to investigate the effects of sintering temperature and holding time on the physical and mechanical properties of the sintered part. 50wt.% SS316L and 50wt.% HA were mixed with a binder system of palm stearin (PS) and polyethylene (PE) at 61 vol.% powder loading. Rheological properties show a pseudo-plastic behaviour of the feedstock, where viscosity decreases with increasing shear rate. The feedstock was injection moulded into a tensile bar shape while thermal debinding was carried out at 320°C and 500°C. The brown parts were sintered at 1000, 1100, 1200 and 1300°C, with three different sintering times of 1, 3 and 5 hours in the furnace. It was found that the highest sintered density measured was 95.61% of the theoretical density. In addition, the highest hardness and Young's modulus measured were 150.45 HV and 52.61 GPa respectively, which are higher than those of human bone. The lowest percentage of carbon content was 0.022wt.% given by the sample sintered at 1300°C for 1 hour. Therefore, SS316L/HA composite with good mechanical and physical properties was successfully produced through the PIM process.
The fabrication of bi-material micro-components via two-component micro-powder injection moulding (2C-µPIM) from 3 mol% yttria-stabilised zirconia (3YSZ) and micro/nano bimodal stainless steel 316L (SS 316L) powders has received insufficient attention. Apart from this, retaining the bonding between ceramic and metal at different processing stages of 2C-µPIM is challenging. This study investigated the solvent and thermal debinding mechanisms of green bi-material micro-parts of 3YSZ and bimodal SS 316L without collapsing the ceramic/metal joining. In this research, feedstocks were prepared by integrating the powders individually with palm stearin and low-density polyethylene binders. The results demonstrated that during the solvent debinding process, the palm stearin removal rate in the bi-materials composed of 3YSZ and bimodally configured SS 316L feedstocks intensified with an increase in temperature. The establishment of interconnected pores in the solvent-debound components facilitated the thermal debinding process, which removed 99% of the binder system. Following sintering, the debound bi-materials exhibited a relative density of 95.3%. According to a study of the microstructures using field emission scanning electron microscopy, an adequate bond between 3YSZ and bimodal SS 316L was established in the micro-part after sintering. The bi-material sintered at 1350 °C had the highest hardness of 1017.4 HV along the joining region.
To date, the mechanical performance of kenaf composites is still unsatisfied in term of its mechanical performance. Therefore, research focuses on kenaf composites fabrication through the selection of polymer resin, including epoxy, polypropylene, and polylactic acid. The incorporated kenaf fibre at 10 wt % to 40 wt % loadings was conducted using injection and a compression moulding process. The compressed materials indicated high tensile strength at 240 MPa compared to inject materials (60 MPa). Significant improvement on impact strength (9 kJ/m2) was due to the unpulled-out fibre that dispersed homogenously and hence minimize the microcrack acquire. Meanwhile, high flexural strength (180 MPa) obtained by kenaf/epoxy composites due to the fibre orientate perpendicular to the loading directions, which improve its mechanical properties. The findings indicate that the kenaf fibre reinforced thermoset materials exhibit better mechanical properties as a function to the battery tray applications.