The joining of ceramic-metal could be done through a few techniques: brazing, diffusion bonding, friction welding etc. However, the mechanism of ceramic-metal joining was still not properly understood. In this study, alumina rod was bonded to mild steel rod via friction welding technique by using Al 1100 sheet as interlayer. The diameter of the rods was 10 mm. Friction pressure of 20 MPa and forging pressure of 40 MPa were used. Rotational speeds were maintained at 900 rpm and friction times of 2 to 20 seconds were applied. The joining strength was determined through four point bending test. The maximum bending strength, 240 MPa was obtained at the friction times of 20 seconds. Under optical microscope and SEM observation, the deformation of the aluminum interface was clearly obtained. Mechanical interlocking and close contact between the aluminaaluminum and aluminum-mild steel were observed at magnifications of 3000X. The strength of alumina-steel bonding is much dependent on the wettability of the alumina surface by the molten aluminum and the existing of mechanical interlocking between interlayer and sample materials.