Hydrolyzing the amorphous region while keeping the crystalline region unaltered is the key technology for producing nanocellulose. This study investigated if the dissolution properties of the amorphous region of microcrystalline cellulose can be enhanced in the presence of Fe(3+) salt in acidic medium. The process parameters, including temperature, time and the concentration of metal chloride catalyst (FeCl₃), were optimized by using the response surface methodology (RSM). The experimental observation demonstrated that temperature and time play vital roles in hydrolyzing the amorphous sections of cellulose. This would yield hydrocellulose with higher crystallinity. The factors that were varied for the production of hydrocellulose were the temperature (x₁), time (x₂) and FeCl₃ catalyst concentration (x₃). Responses were measured in terms of percentage of crystallinity (y₁) and the yield (y₂) of the prepared hydrocellulose. Relevant mathematical models were developed. Analysis of variance (ANOVA) was carried out to obtain the most significant factors influencing the responses of the percentage of crystallinity and yield. Under optimum conditions, the percentage of crystallinity and yield were 83.46% and 86.98% respectively, at 90.95 °C, 6 h, with a catalyst concentration of 1 M. The physiochemical characteristics of the prepared hydrocellulose were determined in terms of XRD, SEM, TGA and FTIR analyses. The addition of FeCl₃ salt in acid hydrolyzing medium is a novel technique for substantially increasing crystallinity with a significant morphological change.
* Title and MeSH Headings from MEDLINE®/PubMed®, a database of the U.S. National Library of Medicine.