In this study, a symmetric supercapacitor has been fabricated by adopting the nanostructured iron oxide (Fe304)-activated carbon (Ac) composite as the core electrode materials. The composite electrodes were prepared via a facile mechanical mixing process and PTFE polymeric solution has been used as the electrode material binder. Structural analysis of the nanocomposite electrodes were characterized by scanning electron microscopy ( sEm) and Brunauer-Emmett-Teller (BET) analysis. The electrochemical performances of the prepared supercapacitor were studied using cyclic voltammetry (cv) and electrochemical impedance spectroscopy (Eis) in 1.0 M Na2S03 and 1.0 M Na2SO4 aqueous solutions, respectively. The experimental results showed that the highest specific capacitance of 43 FIg is achieved with a fairly low Fe304 nanomaterials loading (4 wt. %) in 1 M Na2S03. It is clear that the low concentration of nanostructured Fe304 has improved the capacitive performance of the composite via pseudocapacitance charge storage mechanism as well as the enhancement on the specific surface areas of the electrode. However, further increasing of the Fe304 content in the electrode is found to distort the capacitive performance and deteriorate the specific surface area of the electrode, mainly due to the aggregation of the Fe304 particles within the composite. Additionally, the cv results showed that the Fe3041Ac nanocomposite electrode in Na2S03 electrolyte exhibits a better charge storage performance if compared with Na2SO4 solution. It is believed that Fe304 nanoparticles can provide favourable surface adsorption sites for sulphite (S032-) anions which act as catalysts for subsequent redox and intercalation reactions.