METHODOLOGY: Eighty-four mandibular first premolars were split into seven groups (and n = 12), Group 1: Dia-Root, Group 2: One-Fil, Group 3: BioRoot RCS, Group 4: AH Plus, Group 5: CeraSeal, Group 6: iRoot SP, Group 7: GP without sealer (control). Two groups were made, one for dentinal tubule penetration and the other for push-out bond strength; the total sample size was one hundred sixty-eight. Root canal treatment was performed using a method called the crown down technique, and for obturation, the single cone technique was used. A confocal laser scanning microscope (Leica, Microsystem Heidel GmbH, Version 2.00 build 0585, Germany) was used to evaluate dentinal tubule penetration, and Universal Testing Machine was utilised to measure the push-out bond strength (Shimadzu, Japan) using a plunger size of 0.4 mm and speed of 1mm/min. Finally, the adhesive pattern of the sealers was analysed by HIROX digital microscope (KH-7700). Statistical analysis was carried out by a one-way Anova test, Dunnet's T3 test, and Chi-square test.
RESULTS: Highest dentinal tubule penetration was noticed with One-Fil (p<0.05), followed by iRoot SP, CeraSeal, AH Plus, Dia-Root also, the most negligible value was recorded for BioRoot RCS. Meanwhile, BioRoot RCS (p<0.05) demonstrated the greater value of mean push-out bond strength, followed by One-fil, iRoot SP, CeraSeal, AH Plus and Dia-Root. Regarding adhesive pattern, most of the samples were classified as type 3 and type 4 which implies greater sealing ability and better adherence to the dentinal wall. However, BioRoot RCS revealed the most type 4 (p<0.05), followed by AH Plus, One-Fil, CeraSeal and Dia-Root.
CONCLUSION: The highest dentinal tubule penetration was shown by One-Fil compared to other groups. Meanwhile, BioRoot RCS had greater push-out bond strength and more adhesive pattern than other tested materials.
METHODS: A comprehensive search of was conducted for all relevant in-vitro studies. All randomized controlled in-vitro studies that evaluated the effect of calcium hydroxide on the push-out bond strength of resin-based or calcium silicate-based endodontic sealers were assessed. The variables of interest were extracted, and the risk of the included studies was evaluated. The standardized mean difference was calculated and the significance level was set at p value <0.05.
RESULTS: A total of 26 studies were eligible for analysis. There were 45 independent comparison groups and 1009 recruited teeth. The pooled data showed no significant difference in push-out bond strength between calcium hydroxide and control group in the resin-based group (SMD = 0.03; 95% CI = -0.55, 0.60; p = 0.93), and calcium silicate-based group (SMD = 0.02; 95% CI = -0.31, 0.35; p = 0.90). Most of the studies (21 out of 26) were at medium risk of bias and five studies showed a low risk of bias.
CONCLUSION: The available evidence suggests that calcium hydroxide used as intracanal medication does not influence the push-out bond strength of the resin- and calcium silicate-based endodontic sealers.
CLINICAL SIGNIFICANCE: The results of this meta-analysis suggest that calcium hydroxide used as intracanal medication does not influence the push-out bond strength of resin-based and calcium silicate-based endodontic sealers.
PURPOSE: The purpose of this in vitro study was to determine the wetting properties of 3 different commercially available denture base resin materials with artificial salivary substitute by using contact angle measurements and to compare these properties before and after thermocycling.
MATERIAL AND METHODS: A total 120 specimens were fabricated with 3 different denture base materials (n=40): heat-polymerized polymethylmethacrylate (DenTek), injection-molded nylon polyamide (Valplast), and microwave polymerized (VIPI WAVE). The advancing and receding contact angles were measured with a goniometer by using the WinDrop++ software program. The contact angle hysteresis was calculated from the advancing and receding contact angles values. The same specimens were subjected to thermocycling to measure the advancing and receding contact angles values. The comparative evaluation was carried out before and after thermocycling.
RESULTS: The mean ±standard deviation contact angles of the microwave-polymerized material were (62.40 ±1.21 degrees) advancing contact angle, (32.12 ±0.66 degrees) receding contact angle, and (30.28 ±1.40 degrees) contact angle of hysteresis. It was followed by the injection-molded nylon polyamide material, whose mean ±standard deviation contact angle values were (68.57 ±1.72 degrees) advancing contact angle, (43.02 ±1.39 degrees) receding contact angle, (26.27 ±2.05 degrees) contact angle hysteresis and high impact strength heat-polymerized polymethylmethacrylate material, whose mean ±standard deviation contact angle values were (69.81 ±0.16 degrees) advancing contact angle, (41.90 ±1.02 degrees) receding contact angle, and (27.91 ±0.97 degrees) contact angle hysteresis. The statistical analysis showed significant differences among contact angle values of the microwave-polymerized material as compared with the heat-polymerized polymethylmethacrylate and injection-molded nylon polyamide materials (P
MATERIAL AND METHOD: Forty sound permanent mandibular premolars were collected from a dental clinical setting and disinfected. All forty samples were mounted vertically in a rubber mold exposing only the clinical crown. All samples were bleached using Opalescence Boost Professional Teeth Whitening. After the bleaching procedure, each sample was randomly allocated into four groups according to surface treatment. Samples in group 1 were treated with methylene blue photosensitizer (MBP). Samples in group 2 were exposed to 10% sodium ascorbate. Samples in group 3 were treated with Er, Cr: YSGG laser (ECL). Samples in group 4 were not treated (control). All Samples were treated with 37% phosphoric acid and a bonding agent was applied. A bulk-fill composite was cured to all specimens and all samples were treated in a thermocycler. Specimens were placed in a universal testing machine for shear bond strength (SBS) testing. Descriptive statistics were associated by analysis of variance (ANOVA) and Tukey's post hoc test maintaining level of significance (p<0.05) RESULTS: The lowest SBS scores were achieved in the bleached enamel (BE) group (15.25±1.745 MPa). Whereas, the highest bond integrity was attained by AA group (32.23±1.854 MPa). Samples treated with ECL (31.87±1.659 MPa) and AA (32.23±1.854) were comparable (p>0.05). Samples treated with PDT exhibited significantly different SBS (22.41±1.258) compared to other experimental groups CONCLUSION: ECL showed a reversal effect of BE compared to AA and has the potential to be used in clinical settings. BE reversal using MBP needs further investigation.
OBJECTIVES: The aim of this in vitro study was to evaluate the long-term effects of various staining solutions on the color stability of different temporary materials produced with the computer-aided design and computer-aided manufacturing (CAD/CAM) technology.
MATERIAL AND METHODS: In the study, the following materials were used: VITA CAD-Temp® (group 1); Ceramill® Temp (group 2); and Telio® CAD (group 3). Forty disk-shaped specimens (10 mm in diameter, 2 mm in thickness) of each material (N = 120) were produced with a CAD/CAM system. Staining solutions - of tea (A), of coffee (B) and cola (C) - and distilled water (D, control) were used, and color was evaluated before and after storing the samples in the solutions. Measurements were taken with a spectrophotometer and the color parameters (L*, a*, b*, and ΔE) were calculated according to the Commission internationale de l'éclairage system (CIELab). The results were evaluated with the two-way analysis of variance (ANOVA) and Tukey's tests (α = 0.05).
RESULTS: Clinically perceivable (ΔE00 > 0.8) and statistically significant (p < 0.001) color differences were detected in all specimens. The highest ΔE00 value was found in the Ceramill Temp specimens. In addition, the highest ΔE00 values were noted for the specimens stored in cola and the coffee solution for all groups. The lowest ΔE00 value was observed for the groups stored in the tea solution.
CONCLUSIONS: Clinically perceivable color changes were observed in all the specimens kept in the solutions. Color changes were greater for cola and coffee as compared to tea.