MATERIALS AND METHODS: The flexural strength and flexural modulus, following thermal cycling (5000 cycles of 5-55°C) of 3 MCC-reinforced poly methyl methacrylate (PMMA) specimens were compared with the conventional and commercially available high-impact PMMA. The 3 test groups were represented by addition of various weight combinations of MCC and acrylic powders.

RESULTS: All 3 test groups with the addition of MCC demonstrated improved flexural strength and flexural modulus compared to the conventional resin, without and after thermal cycling. The highest mean flexural strength corresponded to the specimens reinforced with 5% MCC followed by 2% MCC.

OBJECTIVES: The aim of this in vitro study was to evaluate the long-term effects of various staining solutions on the color stability of different temporary materials produced with the computer-aided design and computer-aided manufacturing (CAD/CAM) technology.

MATERIAL AND METHODS: In the study, the following materials were used: VITA CAD-Temp® (group 1); Ceramill® Temp (group 2); and Telio® CAD (group 3). Forty disk-shaped specimens (10 mm in diameter, 2 mm in thickness) of each material (N = 120) were produced with a CAD/CAM system. Staining solutions - of tea (A), of coffee (B) and cola (C) - and distilled water (D, control) were used, and color was evaluated before and after storing the samples in the solutions. Measurements were taken with a spectrophotometer and the color parameters (L*, a*, b*, and ΔE) were calculated according to the Commission internationale de l'éclairage system (CIELab). The results were evaluated with the two-way analysis of variance (ANOVA) and Tukey's tests (α = 0.05).

RESULTS: Clinically perceivable (ΔE00 > 0.8) and statistically significant (p < 0.001) color differences were detected in all specimens. The highest ΔE00 value was found in the Ceramill Temp specimens. In addition, the highest ΔE00 values were noted for the specimens stored in cola and the coffee solution for all groups. The lowest ΔE00 value was observed for the groups stored in the tea solution.

MATERIALS AND METHODS: The HVGICs evaluated were Zirconomer [ZR] (Shofu), Equia Forte [EQ] (GC) and Riva [RV] (SDI). Sixty specimens (12mm x 2mm x 2mm) of each material were fabricated using customized Teflon molds. After initial set, the specimens were removed from their molds, finished, measured and randomly divided into 3 groups of 20. Half the specimens in each group were left uncoated while the remaining half was covered with the respective manufacturers' resin coating. The specimens were subsequently conditioned in distilled water, artificial saliva or citric acid at 37°C for 7 days. The uncoated and coated specimens (n=10) were then subjected to dynamic mechanical testing in flexure mode at 37°C with a frequency of 0.1 to 10Hz. Storage modulus, loss modulus and loss tangent data were subjected to normality testing and statistical analysis using one-way ANOVA/Scheffe's post-hoc test and Ttest at significance level p<0.05.

RESULTS: Mean storage modulus ranged from 1.39 ± 0.36 to 10.80 ± 0.86 GPa while mean loss modulus varied from 0.13 ± 0.03 to 0.70 ± 0.14 GPa after conditioning in the different mediums. Values for loss tangent ranged from 39.4 ± 7.75 to 213.2 ± 20.11 (x10 -3 ). Significant differences in visco-elastic properties were observed between mediums and materials. When conditioned in distilled water and artificial saliva,storage modulus was significantly improved when ZR, EQ and RV were uncoated. Significantly higher values were, however, observed with resin coating when the materials were exposed to citric acid.

METHODS: Experimental adhesives modified with different fractions of dioctadecyldimethyl ammonium bromide quaternary ammonium and riboflavin (QARF) were formulated. Dentine specimens were bonded to resincomposites with control or the experimental adhesives to be evaluated for bond strength, interfacial morphology, micro-Raman analysis, nano-CT and nano-leakage expression. In addition, the antibacterial and biocompatibilities of the experimental adhesives were investigated. The endogenous proteases activities and their molecular binding-sites were studied.

RESULTS: Modifying the experimental adhesives with QARF did not adversely affect micro-tensile bond strength or the degree of conversion along with the demonstration of anti-proteases and antibacterial abilities with acceptable biocompatibilities. In general, all experimental adhesives demonstrated favourable bond strength with increased and improved values in 1% QARF adhesive at 24 h (39.2 ± 3.0 MPa) and following thermocycling (34.8 ± 4.3 MPa).

MATERIALS AND METHODS: Three different makes of ceramic brackets, Pure Sapphire(M), Clarity™ ADVANCED(P) and Dual Ceramic(P) were used. Eighteen specimens of each make were prepared and allocated to three groups (n = 6). MARC(®)-resin calibrator was used to determine the light curing unit (LCU) tip irradiance (mW/cm(2)) and TLE (J/cm(2)) transmitted through the ceramic brackets, and through ceramic bracket plus Transbond™ XT Light Cure Adhesive, for 5, 10 and 20 s. Vickers-hardness values at the bottom of the cured adhesive were determined. Statistical analysis used one-way analysis of variance (ANOVA); P = 0.05.

PURPOSE: The purpose of this in vitro study was to evaluate the wettability of 3 different artificial saliva substitutes on heat-polymerized acrylic resin and to compare these properties with natural saliva and distilled water.

MATERIAL AND METHODS: A total of 150 heat-polymerized acrylic resin specimens were prepared with 25×15×2 mm dimensions. The specimens were divided into 5 groups (n=30): human saliva, distilled water, Aqwet, Mouth Kote, and Stoppers 4. The advancing and receding contact angle values were measured by using a goniometer, and the contact angle hysteresis and equilibrium angle were calculated. One-way ANOVA and the Bonferroni multiple comparisons test were performed to determine the difference between contact angle values among the groups (α=.05).

AIM: To investigate the effect of four commonly used wound care regimens on the tensile strength of suture materials.

METHODS: The failure load of 9 different suture materials was tested using the Instron Electroplus E3000 tensile testing machine (Instron Corporation, Norwood, Massachusetts). Tensile strength was represented as the failure load, measured in Newtons (N), and defined as the maximal load that could be applied across the suture prior to failure. Each suture was tested dry and after immersion in one of 4 products for 7 days and tested on day 7. The immersion agents tested were: sodium chloride 0.9%, MicroSafe® (Sonoma Pharmaceuticals, Petaluma, CA), Aqueous Povidone-iodine 10% solution (Betadine-Mundipharma), and Fucidin ointment.

RESULTS: Sodium chloride 0.9%, MicroSafe®, Aqueous Povidone-iodine 10%, and Fucidin seem to increase the failure load of most absorbable and non-absorbable sutures. However, the failure load of Polyglactin 910 suture (Surgilactin, coated, violet-Ethicon) is reduced by long-term exposure to either sodium chloride 0.9% or MicroSafe®, while the failure load of the Polydioxanone suture (PDS Plus-Ethicon) is reduced by long-term exposure to MicroSafe® only.