CaCu3Ti4O12 was synthesized starting from a solution of TiO2 to which Ca and Cu nitrates were added. Due to the differences in the solubilities of the Ca, Cu and Ti, initial variations from ideal stoichiometry and a high solution pH was necessary to obtain stoichiometric CaCu3Ti4O12 precipitates. As precipitated samples were amorphous with CuO phases observed after drying of the precipitates at 300 oC. CaCu3Ti4O12 phases were observed after heat treatment at 1000 oC. XRD studies show the presence of CuO and TiO2 in addition to the CaCu3Ti4O12 for non stoichiometric samples. Observations under the SEM show the presence of Cu rich and Ti rich phases in addition to the CaCu3Ti4O12.