Triyttrium Pentairon (iii) Oxide (Y3Fe501,2) or familiar called as Yttrium Iron Garnet (YIG) is successfully prepared using a conventional mixed-oxide method of 5:3 Fe to Y ratios. YIG prepared from conventional mixed-oxide usually produced some associated phase which surely will affect electrical properties. In this study, various temperature used in the sintering process to induce associated phases (YIP) to be fully reacting to form single phase of YIG and the effect on resonance frequency is studied for resonator applications. The mixtures of oxide powders are calcined at 1100 "C and sintered at various temperatures of (1350, 1380, 1400, 1420 1450 QC, respectively). Cubic phase is detected from the formation of YIG. Some other phases such as YIP and hematite also present as secondary phase. However, it is seen that, based on the Rietvield refinement method, the total amount of secondary phase simulated are inversely proportional with sintering temperature. The powder was pressed into cylindrical pellet and tested as a microwave resonator in antenna application. It was found that, on the actual antenna circuit the operating frequencies measured are in the range of 10-12 GHz for all samples which suitable for X-band. At the end, overall radiation pattern for all samples exhibit an omnidirectional behavior.