METHODS: Six makes, three each monocrystalline (M) and polycrystalline (P) were used; PureSapphire (M), SPA Aesthetic (M), Ghost (M), Mist (P), Reflections (P), and Dual Ceramic (P). The Ortholux™ Light Curing Unit (LCU) was used to cure the orthodontic adhesive Transbond™XT. The LCU's tip irradiance was measured and TLE transmitted through the ceramic bracket was obtained, then adhesive added to the bracket, and transmitted TLE measured through bracket-plus-adhesive samples. The LCU was set at five seconds as recommended for curing adhesive through ceramic brackets.
RESULTS: Mean tip irradiance was 1859.2±16.2mW/cm2. The TLE transmitted through brackets alone ranged 1.7 to 3.9J/cm2, in the descending order: Ghost>Pure Sapphire>Reflections>Mist>SPA Aesthetics>Dual Ceramic. The TLE transmitted through bracket-plus-adhesive samples ranged 1.6 to 3.7J/cm2, in the descending order: Ghost>Mist>Reflections>Pure Sapphire>SPA Aesthetics>Dual Ceramic. TLE was reduced with the addition of adhesive (range -0.1 to -0.7J/cm2). There was a significant difference for Pure Sapphire, Reflections, and Mist (P<0.05), but not for SPA Aesthetics, Ghost, and Dual Ceramic. There was no overall significant difference between the monocrystalline and polycrystalline makes. The two best makes were of the monocrystalline type, concerning TLE transmission, but with the exception of polycrystalline Dual Ceramic; the next worst make was a monocrystalline bracket, SPA Aesthetics.
CONCLUSION: Light energy attenuation through ceramic orthodontic brackets is make-dependent, with no overall difference between monocrystalline and polycrystalline brackets. Light energy is further attenuated with the addition of resin-based orthodontic adhesive.
METHODS: A comprehensive search of was conducted for all relevant in-vitro studies. All randomized controlled in-vitro studies that evaluated the effect of calcium hydroxide on the push-out bond strength of resin-based or calcium silicate-based endodontic sealers were assessed. The variables of interest were extracted, and the risk of the included studies was evaluated. The standardized mean difference was calculated and the significance level was set at p value <0.05.
RESULTS: A total of 26 studies were eligible for analysis. There were 45 independent comparison groups and 1009 recruited teeth. The pooled data showed no significant difference in push-out bond strength between calcium hydroxide and control group in the resin-based group (SMD = 0.03; 95% CI = -0.55, 0.60; p = 0.93), and calcium silicate-based group (SMD = 0.02; 95% CI = -0.31, 0.35; p = 0.90). Most of the studies (21 out of 26) were at medium risk of bias and five studies showed a low risk of bias.
CONCLUSION: The available evidence suggests that calcium hydroxide used as intracanal medication does not influence the push-out bond strength of the resin- and calcium silicate-based endodontic sealers.
CLINICAL SIGNIFICANCE: The results of this meta-analysis suggest that calcium hydroxide used as intracanal medication does not influence the push-out bond strength of resin-based and calcium silicate-based endodontic sealers.
AIM: To investigate the effect of four commonly used wound care regimens on the tensile strength of suture materials.
METHODS: The failure load of 9 different suture materials was tested using the Instron Electroplus E3000 tensile testing machine (Instron Corporation, Norwood, Massachusetts). Tensile strength was represented as the failure load, measured in Newtons (N), and defined as the maximal load that could be applied across the suture prior to failure. Each suture was tested dry and after immersion in one of 4 products for 7 days and tested on day 7. The immersion agents tested were: sodium chloride 0.9%, MicroSafe® (Sonoma Pharmaceuticals, Petaluma, CA), Aqueous Povidone-iodine 10% solution (Betadine-Mundipharma), and Fucidin ointment.
RESULTS: Sodium chloride 0.9%, MicroSafe®, Aqueous Povidone-iodine 10%, and Fucidin seem to increase the failure load of most absorbable and non-absorbable sutures. However, the failure load of Polyglactin 910 suture (Surgilactin, coated, violet-Ethicon) is reduced by long-term exposure to either sodium chloride 0.9% or MicroSafe®, while the failure load of the Polydioxanone suture (PDS Plus-Ethicon) is reduced by long-term exposure to MicroSafe® only.
CONCLUSION: In our experiment, the commonly used wound care products have been shown to alter the tensile strength of suture materials. Further human studies are required to ascertain the clinical validity and applicability of our findings.