The effects of three preparation variables: CO(2) activation temperature, CO(2) activation time and KOH:char impregnation ratio (IR) on the 2,4,6-trichlorophenol (2,4,6-TCP) uptake and carbon yield of the activated carbon prepared from oil palm empty fruit bunch (EFB) were investigated. Based on the central composite design, two quadratic models were developed to correlate the three preparation variables to the two responses. The activated carbon preparation conditions were optimized using response surface methodology by maximizing both the 2,4,6-TCP uptake and activated carbon yield within the ranges studied. The optimum conditions for preparing activated carbon from EFB for adsorption of 2,4,6-TCP were found as follows: CO(2) activation temperature of 814 degrees C, CO(2) activation time of 1.9h and IR of 2.8, which resulted in 168.89 mg/g of 2,4,6-TCP uptake and 17.96% of activated carbon yield. The experimental results obtained agreed satisfactorily with the model predictions. The activated carbon prepared under optimum conditions was mesoporous with BET surface area of 1141 m(2)/g, total pore volume of 0.6 cm(3)/g and average pore diameter of 2.5 nm. The surface morphology and functional groups of the activated carbon were respectively determined from the scanning electron microscopy and Fourier transform infrared analysis.
In this work, the adsorption of 2,4-dichlorophenoxyacetic acid (2,4-D) on activated carbon derived from date stones (DSAC) was studied with respect to pH and initial 2,4-D concentration. The experimental data were analyzed by the Freundlich isotherm, the Langmuir isotherm, and the Temkin isotherm. Equilibrium data fitted well with the Langmuir model with maximum adsorption capacity of 238.10 mg/g. Pseudo-first and pseudo-second-order kinetics models were tested with the experimental data, and pseudo-first-order kinetics was the best for the adsorption of 2,4-D by DSAC with coefficients of correlation R(2)>or=0.986 for all initial 2,4-D concentrations studied. The results indicated that the DSAC is very effective for the adsorption of 2,4-D from aqueous solutions.
In this work, the adsorption of malachite green (MG) on rattan sawdust (RSD) was studied at 30 degrees C. The results indicated that RSD can be used as a low-cost adsorbent for the removal of MG dye from aqueous solutions. Equilibrium data were analyzed by two isotherms, namely the Freundlich isotherm and the Langmuir isotherm. The best fit to the data was obtained with the Langmuir isotherm. The monolayer adsorption capacity of RSD was found to be 62.71 mg/g. The adsorption kinetics can be predicted by the pseudo-first-order model. The mechanism of adsorption was also studied. It was found that for a short time period the rate of adsorption is controlled by film diffusion. However, at longer adsorption times, pore-diffusion controls the rate of adsorption. The amount adsorbed on the outer surface was estimated from the time where film-diffusion stops controlling the adsorption rate.
The aim of the present work was to investigate the feasibility of grass waste (GW) for methylene blue (MB) adsorption. The adsorption of MB on GW material was studied as a function of GW dose (0.05-1.20 g), solution pH 3-10, contact time and initial concentration (70-380 mg/L). The influence of these parameters on the adsorption capacity was studied using the batch process. The experimental data were analyzed by the Langmuir and Freundlich isotherms. The adsorption isotherm was found to follow the Langmuir model. The monolayer adsorption capacity was found to be 457.640 mg/g. The kinetic data were fitted to the pseudo-first-order and pseudo-second-order models, and were found to follow closely the pseudo-second-order kinetic model. The results revealed that GW adsorbent is potentially low-cost adsorbent for adsorption of MB.
The adsorption characteristics of 2,4,6-trichlorophenol (TCP) on activated carbon prepared from oil palm empty fruit bunch (EFB) were evaluated. The effects of TCP initial concentration, agitation time, solution pH and temperature on TCP adsorption were investigated. TCP adsorption uptake was found to increase with increase in initial concentration, agitation time and solution temperature whereas adsorption of TCP was more favourable at acidic pH. The adsorption equilibrium data were best represented by the Freundlich and Redlich-Peterson isotherms. The adsorption kinetics was found to follow the pseudo-second-order kinetic model. The mechanism of the adsorption process was determined from the intraparticle diffusion model. Boyd plot revealed that the adsorption of TCP on the activated carbon was mainly governed by particle diffusion. Thermodynamic parameters such as standard enthalpy (DeltaH degrees ), standard entropy (DeltaS degrees ), standard free energy (DeltaG degrees ) and activation energy were determined. The regeneration efficiency of the spent activated carbon was high, with TCP desorption of 99.6%.
The liquid-phase adsorption of phenol onto coconut shell-based activated carbon, CS850A was investigated for its equilibrium studies and kinetic modeling. Coconut shell was converted into high quality activated carbon through physiochemical activation at 850 degrees C under the influence of CO(2) flow. Beforehand, the coconut shell was carbonized at 700 degrees C and the resulted char was impregnated with KOH at 1:1 weight ratio. In order to evaluate the performance of CS850A, a series of batch adsorption experiments were conducted with initial phenol concentrations ranging from 100 to 500 mg l(-1), adsorbent loading of 0.2g and the adsorption process was maintained at 30+/-1 degrees C. The adsorption isotherms were in conformation to both Langmuir and Freundlich isotherm models. Chemical reaction was found to be a rate-controlling parameter to this phenol-CS850A batch adsorption system due to strong agreement with the pseudo-second-order kinetic model. Adsorption capacity for CS850A was found to be 205.8 mg g(-1).
The synthesized zeolite NaY from rice husk ash (RHA) and the commercial zeolite NaY both modified with surfactants in amounts equal to 50%, 100% and 200% of their external cation exchange capacity (ECEC) were used to remove chromate and arsenate anions from aqueous solutions. While the unmodified zeolite Y had little or no affinity for the Cr(VI) and As(V) anionic species, the surfactant-modified zeolite Y (SMZY) showed significant ability to remove of these anions from the aqueous solutions. The highest chromates and arsenates adsorption efficiency was observed from solutions of pH values 3 and 8, respectively because of the dominance of the univalent species of both anions. The adsorption equilibrium data were best fitted with the Langmuir isotherm model with the highest removal capacities observed for the SMZY initially prepared considering the hexadecyltrimethyl ammonium (HDTMA) amount equal to the 100% of the ECEC of zeolite Y. Synthesized SMZY remove Cr(VI) and As(V) more than the corresponding commercial one due to its lower silica to alumina ratio. Thus, the HDTMA-covered modified zeolite Y synthesized using RHA can be used to remove Cr(VI) and As(V) from water.
In this paper, pineapple stem (PS) waste, an agricultural waste available in large quantity in Malaysia, was utilized as low-cost adsorbent to remove basic dye (methylene blue, MB) from aqueous solution by adsorption. Batch mode experiments were conducted at 30 degrees C to study the effects of initial concentration of methylene blue, contact time and pH on dye adsorption. Equilibrium adsorption isotherms and kinetic were investigated. The experimental data were analyzed by the Langmuir and Freundlich models and the isotherm data fitted well to the Langmuir isotherm with monolayer adsorption capacity of 119.05mg/g. The kinetic data obtained at different concentrations were analyzed using a pseudo-first-order and pseudo-second-order equation and intraparticle diffusion equation. The experimental data fitted very well the pseudo-second-order kinetic model. The PS was found to be very effective adsorbent for MB adsorption.
This study aimed at investigating the feasibility of using jackfruit peel (JFP), a solid waste, abundantly available in Malaysia, for the adsorption of methylene blue, a cationic dye. Batch adsorption studies were conducted to evaluate the effects of contact time, initial concentration (35-400mg/L), pH (2-11), and adsorbent dose (0.05-1.20g) on the removal of dye at temperature of 30 degrees C. The experimental data were analyzed by the four different types of linearized Langmuir isotherm, the Freundlich isotherm and the Temkin isotherm. The experimental data fitted well with the type 2 Langmuir model with a maximum adsorption capacity of 285.713mg/g. Pseudo-first and pseudo-second-order kinetics models were tested with the experimental data, and pseudo-second-order kinetics was the best for the adsorption of MB by JFP with coefficients of correlation R(2)> or =0.9967 for all initial MB concentrations studied. The results demonstrated that the JFP is very effective for the adsorption of methylene blue (MB) from aqueous solutions.
In this paper, the newly explored TiO(2)-Chitosan/Glass was suggested as a promising alternative material to conventional means of wastewater treatment. Characterization of TiO(2)-Chitosan/Glass photocatalyst was studied with SEM-EDX, XRD, and Fourier transform infrared spectroscopy (FTIR) analysis. The combination effect of photodegradation-adsorption process for the removal of methyl orange (MO), an acid dye of the monoazo series occur promisingly when four layers of TiO(2)-Chitosan/Glass photocatalyst was used for MO removal. Approximately, 87.0% of total MO removal was achieved. The reactive -NH(2), -OH, and metal oxide contents in the prepared photocatalyst responsible for the photodegradation-adsorption effect were confirmed by FTIR study. Similarly, MO removal behavior was well supported by SEM-EDX and XRD analysis. Significant dependence of MO removal on the TiO(2)-Chitosan loading can be explained in terms of relationship between quantum yield of photocatalytic reactions and photocatalyst structure/activity. Hence, the research work done thus far suggests a new method, having both the advantages of photodegradation-adsorption process in the abatement of various wastewater pollutants.
In this work, the adsorption of malachite green (MG) was studied on activated carbon prepared from bamboo by chemical activation with K(2)CO(3) and physical activation with CO(2) (BAC). Adsorption studies were conducted in the range of 25-300 mg/L initial MG concentration and at temperature of 30 degrees C. The experimental data were analyzed by the Freundlich isotherm, the Langmuir isotherm, and the multilayer adsorption isotherm. Equilibrium data fitted well with the Langmuir model with maximum adsorption capacity of 263.58 mg/g. The rates of adsorption were found to confirm to pseudo-second-order kinetics with good correlation and the overall rate of dye uptake was found to be controlled by pore diffusion throughout the entire adsorption period. The results indicate that the BAC could be used to effectively adsorb MG from aqueous solutions.
The potential of garlic peel (GP), agricultural waste, to remove methylene blue (MB) from aqueous solution was evaluated in a batch process. Experiments were carried out as function of contact time, initial concentration (25-200mg/L), pH (4-12) and temperature (303, 313 and 323 K). Adsorption isotherms were modeled with the Langmuir, Freundlich, and Temkin isotherms. The data fitted well with the Freundlich isotherm. The maximum monolayer adsorption capacities were found to be 82.64, 123.45, and 142.86 mg/g at 303, 313, and 323 K, respectively. The kinetic data were analyzed using pseudo-first-order and pseudo-second-order models. The results indicated that the garlic peel could be an alternative for more costly adsorbents used for dye removal.
The continuous adsorption of lead ions from aqueous solution on commercial, granular, unpretreated palm shell activated carbon (PSAC) was studied. Effect of pH, flow rates and presence of complexing agents (malonic and boric acids) were examined. The breakthrough period was longer at pH 5 indicating higher adsorption capacity of lead ions at higher pH. Increase of the flow rate, expectedly, resulted in the faster saturation of the carbon bed. Presence of complexing agents did not improve adsorption uptake of lead ions. However, presence of malonic acid resulted in smoother pH stabilization of solution compared to single lead and lead with boric acid systems. The results on continuous adsorption of lead were applied to the model proposed by Wang et al. [Y.-H. Wang, S.-H. Lin, R.-S. Juang, Removal of heavy metals ions from aqueous solutions using various low-cost adsorbents, J. Hazard. Mater. B 102 (2003) 291-302]. The agreement between experimental and modelled breakthrough curves was satisfactory at both pHs.
Adsorption isotherm and kinetics of methylene blue on activated carbon prepared from coconut husk were determined from batch tests. The effects of contact time (1-30 h), initial dye concentration (50-500 mg/l) and solution temperature (30-50 degrees C) were investigated. Equilibrium data were fitted to Langmuir, Freundlich, Temkin and Dubinin-Radushkevich isotherm models. The equilibrium data were best represented by Langmuir isotherm model, showing maximum monolayer adsorption capacity of 434.78 mg/g. The kinetic data were fitted to pseudo-first-order, pseudo-second-order and intraparticle diffusion models, and was found to follow closely the pseudo-second-order kinetic model. Thermodynamic parameters such as standard enthalpy (DeltaH degrees), standard entropy (DeltaS degrees) and standard free energy (DeltaG degrees) were evaluated. The adsorption interaction was found to be exothermic in nature. Coconut husk-based activated carbon was shown to be a promising adsorbent for removal of methylene blue from aqueous solutions.
The application of low-cost adsorbents obtained from plant wastes as a replacement for costly conventional methods of removing heavy metal ions from wastewater has been reviewed. It is well known that cellulosic waste materials can be obtained and employed as cheap adsorbents and their performance to remove heavy metal ions can be affected upon chemical treatment. In general, chemically modified plant wastes exhibit higher adsorption capacities than unmodified forms. Numerous chemicals have been used for modifications which include mineral and organic acids, bases, oxidizing agent, organic compounds, etc. In this review, an extensive list of plant wastes as adsorbents including rice husks, spent grain, sawdust, sugarcane bagasse, fruit wastes, weeds and others has been compiled. Some of the treated adsorbents show good adsorption capacities for Cd, Cu, Pb, Zn and Ni.
This paper presents the results of research on heavy metals removal from water by filtration using low cost coarse media which could be used as an alternative approach to remove heavy metals from water or selected wastewater. A series of batch studies were conducted using different particle media (particle size 2.36-4.75 mm) shaken with different heavy metal solutions at various pH values to see the removal behaviour for each metal. Each solution of cadmium (Cd), lead (Pb), zinc (Zn), nickel (Ni), copper (Cu) and chromium (Cr(III)) with a concentration of 2 mg/L was shaken with the media. At a final pH of 8.5, limestone has significantly removed more than 90% of most metals followed by 80% and 65% removals using crushed bricks and gravel, respectively. The removal by aeration and settlement methods without solid media was less than 30%. Results indicated that the removal of heavy metals was influenced by the media and not directly by the pH. Investigations on the removal behaviour of these metals indicated that rough solid media with the presence of carbonate were beneficial for the removal process. Adsorption and precipitation as metals oxide and probably as metals carbonate were among the two mechanisms that contributed to the removal of metals from solution.
The study was attempted to produce activated carbons from palm oil mill effluent (POME) sludge. The adsorption capacity of the activated carbons produced was evaluated in aqueous solution of phenol. Two types of activation were followed, namely, thermal activation at 300, 500 and 800 degrees C, and physical activation at 15 degrees C (boiling treatment). A control (raw POME sludge) was used to compare the adsorption capacity of the activated carbons produced. The results indicated that the activation temperature of 800 degrees C showed maximum absorption capacity by the activated carbon (POME 800) in aqueous solution of phenol. Batch adsorption studies showed an equilibrium time of 6 h for the activated carbon of POME 800. It was observed that the adsorption capacity was higher at lower values of pH (2-3) and higher value of initial concentration of phenol (200-300 mg/L). The equilibrium data were fitted by the Langmuir and Freundlich adsorption isotherms. The adsorption of phenol onto the activated carbon POME 800 was studied in terms of pseudo- first and second order kinetics to predict the rate constant and equilibrium capacity with the effect of initial phenol concentrations. The rate of adsorption was found to be better correlation for the pseudo-second order kinetics compared to the first order kinetics.
In this paper, broad bean peels (BBP), an agricultural waste, was evaluated for its ability to remove cationic dye (methylene blue) from aqueous solutions. Batch mode experiments were conducted at 30 degrees C. Equilibrium sorption isotherms and kinetics were investigated. The kinetic data obtained at different concentrations have been analyzed using pseudo-first-order, pseudo-second-order and intraparticle diffusion equations. The experimental data fitted very well the pseudo-first-order kinetic model. Analysis of the temportal change of q indicates that at the beginning of the process the overall rate of adsorption is controlled by film-diffusion, then at later stage intraparticle-diffusion controls the rate. Diffusion coefficients and times of transition from film to pore-diffusion control were estimated by piecewise linear regression. The experimental data were analyzed by the Langmuir and Freundlich models. The sorption isotherm data fitted well to Langmuir isotherm and the monolayer adsorption capacity was found to be 192.7 mg/g and the equilibrium adsorption constant Ka is 0.07145 l/mg at 30 degrees C. The results revealed that BBP was a promising sorbent for the removal of methylene blue from aqueous solutions.
HBcAg (hepatitis B core antigen) is a nanoplex bioproduct that has a great potential in the development of therapeutic drugs and vaccines. In the present study, a continuous-flow bead milling for the disruption of Escherichia coli was optimized and a direct recovery protocol to isolate the recombinant HBcAg from the unclarified E. coli disruptate was developed. The optimal condition for continuous-flow bead milling for the release of HBcAg from E. coli was achieved at a feed flow rate of 15 litres/h, biomass concentration of 10% [ww/v (wet weight/vol.)] and impeller tip speed of 14 m/s. The sucrose-density-gradient analysis showed that the particulate form of the HBcAg released by this optimal condition is still preserved. In the direct purification of HBcAg from the unclarified disruptate, the AE-EBAC (anion-exchange expanded-bed adsorption chromatography) technique was employed. A 54% adsorption and 50.7% recovery of HBcAg were achieved in this direct recovery process. The purity of HBcAg recovered was 49.8%, which corresponds to a purification factor of 2.0. ELISA showed that the HBcAg recovered is functionally active.
In this study, the kinetics of adsorption of Pb(II) from aqueous solution onto palm shell-based activated carbon (PSAC) were investigated by employing ion selective electrode (ISE) for real-time Pb(II) and pH monitoring. Usage of ISE was very appropriate for real-time adsorption kinetics data collection as it facilitated recording of adsorption data at very specific and short time intervals as well as provided consistent kinetics data. Parameters studied were initial Pb(II) concentration and agitation speed. It was found that increases in initial Pb(II) concentration and agitation speed resulted in higher initial rate of adsorption. Pseudo first-order, pseudo second-order, Elovich, intraparticle diffusion and liquid film diffusion models were used to fit the adsorption kinetics data. It was suggested that chemisorption was the rate-controlling step for adsorption of Pb(II) onto PSAC since the adsorption kinetics data fitted both the pseudo second-order and Elovich models well.