MATERIALS AND METHODS: Sound extracted human molars were randomly divided into: manufacturer's instructions (MI), manual blend 2 mm (MB2), and manual blend 4 mm (MB4). Occlusal enamel was removed and flattened, dentin surfaces were bonded by Prime & Bond universal (Dentsply and Optibond FL, Kerr). For the MI group, adhesives were applied following the manufacturer's instructions then light-cured. For MB groups, SDR flow+ bulk-fill flowable composite resin was applied in 2- or 4-mm increment then manually rubbed by a micro brush for 15 s with uncured dentine bonding agents and the mixture was light-cured. Composite buildup was fabricated incrementally using Ceram.X One, Dentsply nanohybrid composite resin restorative material. After 24-h water storage, the teeth were sectioned to obtain beams of about 0.8 mm2 for 24-h and thermocycled micro-tensile bond strength at 0.5 mm/min crosshead speed. Degree of conversion was evaluated with micro-Raman spectroscopy. Contraction gaps at 24 h after polymerization were evaluated and atomic force microscopy (AFM) nano-indentation processes were undertaken for measuring the hardness across the interface. Depth of resin penetration was studied using a scanning electron microscope (SEM). Bond strength data was expressed using two-way ANOVA followed by Tukey's test. Nanoindentation hardness was separately analyzed using one-way ANOVA.
RESULTS: Factors "storage F = 6.3" and "application F = 30.11" significantly affected the bond strength to dentine. For Optibond FL, no significant difference in nanoleakage was found in MI/MB4 groups between baseline and aged specimens; significant difference in nanoleakage score was observed in MB2 groups. Confocal microscopy analysis showed MB2 Optibond FL and Prime & Bond universal specimens diffusing within the dentine. Contraction gap was significantly reduced in MB2 specimens in both adhesive systems. Degree of conversion (DC) of the MB2 specimens were numerically more compared to MS1 in both adhesive systems.
CONCLUSION: Present study suggests that the new co-blend technique might have a positive effect on bond strengths of etch-and-rinse adhesives to dentine.
MATERIALS AND: METHODS: Extracted human upper central incisors were prepared and stained with red wine for 14 days before being subjected to four different bleaching agents: professionally prescribed opalescence PF 15%, VOCO Perfect Bleach 10%, nonprescription OTC Crest 3D Whitestrips, and Whitelight Teeth Whitening System. Colorimetric measurement was performed with Vita Easyshade Handheld Spectrophotometer, enamel surface microhardness measured using Vickers Hardness machine, and surface roughness was evaluated with profilometer, before and after bleaching. Scanning electron microscope (SEM) evaluation and atomic force microscopy were conducted postbleaching.
STATISTICAL ANALYSIS: The data were analyzed with t-test, two-way ANOVA, one-way ANOVA, and Turkey's test at a significance level of 5%.
RESULTS: All bleaching products have the same efficacy to whiten stained enamel. Opalescence PF 15% showed significant increase in the microhardness (92.69 ± 68.316). All groups demonstrated significant increase in surface roughness (p < 0.05). SEM evaluation showed that Opalescence PF 15% resulted in same microscopic appearance as unbleached enamel, while VOCO Perfect Bleach 10%, Whitelight Teeth Whitening System and Crest 3D Whitestrips demonstrated mild to moderate irregularities and accentuated irregularities, respectively.
CONCLUSION: Professionally prescribed bleaching agent of Opalescence PF 15% is effective tin whitening the teeth, while the other bleaching products may be effective but also have deleterious effects on the enamel.