Carbon nanoparticles have been widely used in various applications. However, they are commonly known to have low dispersibility and chemical inertness which limit their practical ability in medical or biological area. Some studies have been performed to modify carbon nanoparticles such as carbon nanotubes using ultraviolet (UV)-Ozone system. However, little is known on the effects of such system towards other types of carbon nanoparticles such as mesoporous hollow carbon nanoparticles (MHCNs). Thus, in this study, improvement of MHCNs physiochemical properties have been studied using UV-Ozone treatment for the first time. The treatment was conducted in water as dispersant agent at ozone flowrate of 1.0 L/min and exposure time of 45 min. SEM images observed that MHCNs morphology and surface structure remain intact after the treatment. Observations on the dispersibility of MHCNs in phosphate buffered saline (PBS) solution shows that the dispersibility was improved compared to the untreated ones. This was supported by the low Z-average and PDI values of treated MHCNs obtained at ~400 nm and 0.2, respectively when compared to the untreated MHCNs which was obtained at 970 nm and 0.417, respectively. Thermogravimetric analysis (TGA) showed an increased in weight loss of treated MHCNs at the lower temperature compared to untreated MHCNs. Results from Fourier Transform Infrared (FTIR) showed an increase number of new functional groups that includes carboxylic acid group presence at the surface of treated MHCNs which contributes to the improvement of their dispersibility, thermal properties and chemical functionality. These findings opened a new possibility of using UV-Ozone treatment to improve physicochemical properties of MHCNs for medical area such as in drug delivery application in addition to their excellent storage and carrier system.