METHODS: Twenty patients with two adjacent missing posterior teeth were recruited. Patients were assigned equally and randomly into two groups; Bicon(®) (6 or 8 mm) and Ankylos(®) (8 mm) implants. A two-stage surgical approach and single crowns were used for implant placement and loading. Outcomes included peri-implant clinical parameters, implant stability (Periotest values; PTVs) and peri-implant bone changes, which were assessed at baseline, 2, 6 and 12 months post-loading.
RESULTS: No implant loss was encountered up to 12 months post-loading. No significant difference in the clinical or radiographic parameters was observed except for PTVs (p < 0.05) that was lower in Ankylos(®) implants.
CONCLUSIONS: The use of short dental implants was associated with excellent 12 months clinical and radiographic outcomes. Ankylos(®) and Bicon(®) implants demonstrated similar peri-implant soft tissue and alveolar bone changes. However, Ankylos(®) implants demonstrated better implant stability at all evaluation intervals.
METHODS: Six master dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Thirty copings (Procera AllCeram) of 0.6-mm thickness were manufactured. Three types of luting media were used: zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and dual-cured composite resin cement (Panavia F). Ten copings were cemented with each type. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.
RESULTS: ANOVA revealed significant differences in the load at fracture among the three groups (p < 0.001). The fracture strength results showed that the mean fracture strength of zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and resin luting cement (Panavia F) were 1091.9 N, 784.8 N, and 1953.5 N, respectively.
CONCLUSION: Different luting agents have an influence on the fracture resistance of Procera AllCeram copings.
Materials and Methods: A cross-sectional questionnaire-based research was conducted among 65 pediatric dentists in Malaysia. Online questionnaires were distributed to the pediatric dentists employed at public hospitals (MOH) and universities in Malaysia.
Result: It was found that over half of the respondents (65.6%) employed HTPMC. The analysis of the co-occurrence network frequency revealed that a high frequency of female pediatric dentists who were within the age group of 31-40 years old had fulfilled their postgraduation overseas and was employed in the university mainly applied HTPMC.
Conclusion: The application of HTPMC among respondent pediatric dentists in Malaysia was high. However, most respondents considered HTPMC a treatment option only to manage carious primary molar rather than a treatment of choice.