METHODS: Sprague-Dawley (Rattus norvegicus) rats were used as the experimental animals. The skin around the dorsum of the tested animals was shaved and pasted with 0.1 mg and 0.5 mg of the nanotitania extraction. The color and condition of the pasted area and the behavior of the animals were observed.
RESULTS: 0.1 mg nanotitania extraction application on the dorsum of the rat produced no skin color changes at day 1, day 3, day 5, or day 7 postapplication. There were no changes in their behavior up to day 7 with no skin rashes or skin scratches seen or fur changes. However, 0.5 mg of nanotitania extraction resulted in redness and less fur regrowth at day 7.
CONCLUSIONS: A 0.1 mg modified nanotitania extraction was observed to have no effect on the skin of Sprague-Dawley rats.
METHODS: This was a prospective, cross sectional study recruiting injured motorcyclists from Hanoi, Vietnam hospital. The participants were interviewed by a trained researcher. The participants' helmets were collected post-crash. Initially, the helmets were examined for their type and external characteristics. A 3 cm × 3 cm cut was made on the helmet in the impacted and non-impacted areas (control). These areas were investigated for evidence of POD and presence of micro-cracks and material disintegration. 50 participants were enrolled. Sources of information included questionnaire and laboratory analyses. The helmet factors of interest were age of the helmet, exposure of helmet to sunlight and rain (duration/day) and history of previous impact. Laboratory analyses included Fourier Transform Infra Red (FTIR) for degradation and scanning electron microscopy (SEM) for micro-structural examination.
RESULTS: Majority of the helmets was the open-face type, 40 (80.0%). 31 (62.0%) helmets aged less than three years (LTY) and 19 (38.0%) were three years old or more (MTY). 19 (61.3%) of the LTY helmets and 12 (63.2%) MTY helmets showed evidence of POD. The duration of helmet exposure to sunlight was between 93 to 6570 hours (mean 2347.74 hours; SD 1733.39). The SEM showed 15 helmets (30%) with micro-fractures, 21 helmets (42.0%) with material disintegration. Prolonged uv exposure to the ABS helmets resulted in changes in the helmet material in the form of material disintegration and microcracks and this association was statistically significant (p = 0.03).
CONCLUSION: POD occurs due to routine exposure to the ultraviolet light. Prolonged uv exposure affects outer shell surface material integrity.