Chitosan-deep eutectic solvent (DES) beads were prepared from chitosan and DESs. The DESs used were choline chloride-urea (DES A) and choline chloride-glycerol (DES B). Both chitosan-DES beads were used to remove malachite green (MG) dye from an aqueous solution. The optimum pH for chitosan-DES A was recorded at pH 8.0 while optimum pH for chitosan-DES B was pH 9.0. The maximum adsorption capacity obtained for chitosan-DES A and chitosan-DES B were 6.54 mg/g and 8.64 mg/g, respectively. The optimum conditions for both chitosan-DES beads to remove MG were 0.08 g of adsorbent and 20 min of agitation time. Five kinetic models were applied to analyse the data and the results showed that the pseudo-second-order and intraparticle diffusion model fitted best with R2 > 0.999. For the adsorption capacity, results show that the Freundlich and Langmuir adsorption isotherms fitted well with chitosan-DES A and chitosan-DES B, respectively. The maximum adsorption capacities (qmax) obtained from chitosan-DES A and chitosan-DES B were 1.43 mg/g and 17.86 mg/g, respectively. Desorption indicated good performance in practical applications.
In current research work, chitosan (Chi) was subjected to subsequent physical and chemical modifications by incorporating kaolin clay (KA) into its polymeric structure, and crosslinking process with a covalent cross-linker namely epichlorohydrin (ECH) respectively. The final product of crosslinked chitosan-epichlorohydrin/kaolin (Chi-ECH/KA) composite was successfully applied for color removal and chemical oxygen demand (COD) reduction of textile dye namely reactive blue 19 dye (RB19) from aqueous environment. The influence of pertinent parameters, i.e. A: Chi-ECH/KA dose (0.02-0.1 g), B: pH (4-10), and C: time (5-30 min) on the RB19 color removal and COD reduction were statistically optimized by using response surface methodology with Box-Behnken design (RSM-BBD). The experimental data of the adsorption kinetic and the adsorption isotherm demonstrated a better fitness to pseudo-second order model and Langmuir isotherm model respectively. Excellent absorption ability of 560.9 mg/g was recorded for Chi-ECH/KA composite. The calculated thermodynamic functions clarified that the RB19 adsorption process was endothermic and spontaneous in nature. The mechanism of RB19 adsorption onto the Chi-ECH/KA may include electrostatic interactions, hydrogen bonding, Yoshida H-bonding, and n-π interactions. This study introduces Chi-ECH/KA composite as an eco-friendly, potential and multi-function composite bio adsorbent for removal of textile dye and COD reduction from aqueous environment.
Recently, chitin and chitosan are widely investigated for food preservation and active packaging applications. Chemical, as well as biological methods, are usually adopted for the production of these biopolymers. In this study, modification to a chemical method of chitin synthesis from shrimp shells has been proposed through the application of high-frequency ultrasound. The impact of sonication time on the deproteinization step of chitin and chitosan preparation was examined. The chemical identities of chitin and chitosan were verified using infrared spectroscopy. The influence of ultrasound on the deacetylation degree, molecular weight and particle size of the biopolymer products was analysed. The microscopic characteristics, crystallinity and the colour characteristics of the as-obtained biopolymers were investigated. Application of ultrasound for the production of biopolymers reduced the protein content as well as the particle size of chitin. Chitosan of high deacetylation degree and medium molecular weight was produced through ultrasound assistance. Finally, the as-derived chitosan was applied for beef preservation. High values of luminosity, chromatid and chrome were noted for the beef samples preserved using chitosan films, which were obtained by employing biopolymer subjected to sonication for 15, 25 and 40 min. Notably; these characteristics were maintained even after ten days of packaging. The molecular weight of these samples are 73.61 KDa, 86.82 KDa and 55.66 KDa, while the deacetylation degree are 80.60%, 92.86% and 94.03%, respectively; in the same order, the particle size of chitosan are 35.70 μm, 25.51 μm and 20.10 μm.
The adsorption of Cu(II) ions from aqueous solution by chitosan and chitosan/PVA beads was studied in a batch adsorption system. Chitosan solution was blended with poly(vinyl alcohol) (PVA) in order to obtain sorbents that are insoluble in aqueous acidic and basic solution. The adsorption capacities and rates of Cu(II) ions onto chitosan and chitosan/PVA beads were evaluated. The Langmuir, Freundlich and BET adsorption models were applied to describe the isotherms and isotherm constants. Adsorption isothermal data could be well interpreted by the Langmuir model. The kinetic experimental data properly correlated with the second-order kinetic model, which indicates that the chemical sorption is the rate-limiting step. The Cu(II) ions can be removed from the chitosan and chitosan/PVA beads rapidly by treatment with an aqueous EDTA solution. Results also showed that chitosan and chitosan/PVA beads are favourable adsorbers.
For the synthesis of a highly active TiO2-chitosan nanocomposite, pH plays a crucial role towards controlling its morphology, size, crystallinity, thermal stability, and surface adsorption properties. The presence of chitosan (CS) biopolymer facilitates greater sustainability to the photoexcited electrons and holes on the catalysts' surface. The variation of synthesis pH from 2 to 5 resulted in different physico-chemical and photocatalytic properties, whereby a pH of 3 resulted in TiO2-chitosan nanocomposite with the highest photocatalytic degradation (above 99 %) of methylene orange (MO) dye. This was attributed to the efficient surface absorption properties, high crystallinity, and the presence of reactive surfaces of -NH2 and -OH groups, which enhances the adsorption-photodegradation effect. The larger surface oxygen vacancies coupled with reduced electron-hole recombination further enhanced the photocatalytic activity. It is undeniable that the pH during synthesis is critical towards the development of the properties of the TiO2-chitosan nanocomposite for the enhancement of photocatalytic activity.
Squid pens were subjected to alkali hydrolysis to extract chitin and chitosan. Proteins present in the alkaline extraction wastewater were recovered at pH 3, 4, 5 and 6, and were subjected to hydrolysis by trypsin, pepsin and a bacterial protease called HT for 1, 2, 4 and 24h. Hydrolysis of the extracted proteins with either trypsin or HT generated more antioxidant activity than hydrolysis with pepsin. Higher ACE-inhibitory activity was generated in the trypsin and pepsin hydrolysates than in the HT hydrolysate. Squid pen protein recovered from chitosan processing waste alkaline solution can be a potential source of bioactive peptides for addition to foods. The antioxidant and ACE-inhibitory activities of the extracted proteins were initially low and increased upon incubation with the proteases. Pepsin generated significantly lower (P<0.05) antioxidant activities compared to trypsin and HT, while trypsin and pepsin hydrolysates exhibited higher ACE-inhibitory activity than HT (P<0.05).
Over the last few years, several attempts have been made to replace petrochemical products with renewable and biodegradable components. The most challenging part of this approach is to obtain bio-based materials with properties and functions equivalent to those of synthetic products. Various naturally occurring polymers such as starch, collagen, alginate, cellulose, and chitin represent attractive candidates as they could reduce dependence on synthetic products and consequently positively impact the environment. Chitosan is also a unique bio-based polymer with excellent intrinsic properties. It is known for its anti-bacterial and film-forming properties, has high mechanical strength and good thermal stability. Nanotechnology has also applied chitosan-based materials in its most recent achievements. Therefore, numerous chitosan-based bionanocomposites with improved physical and chemical characteristics have been developed in an eco-friendly and cost-effective approach. This review discusses various sources of chitosan, its properties and methods of modification. Also, this work focuses on diverse preparation techniques of chitosan-based bionanocomposites and their emerging application in various sectors. Additionally, this review sheds light on future research scope with some drawbacks and challenges to motivate the researchers for future outstanding research works.
Preparation of chitosan-coated fatty acid liposomes is often restricted by the solubility of chitosan under basic conditions. In this experiment, the preparation of chitosan-coated oleic acid (OA) liposomes using low molecular weight (LMW) chitosan (10 and 25 kDA) was demonstrated. These selected LMW chitosans are water soluble. The coating of the chitosan layer on OA liposomes was confirmed by its microscope images and physicochemical properties, such as zeta potential and the size of the liposomes. The "peeling off" effect on the surface of chitosan-coated OA liposomes was observed in the atomic force microscope images and showed the occurrence of the chitosan layer on the surface of OA liposomes. The size of the chitosan-coated liposomes was at least 20 nm smaller than the OA liposomes, and the increase of zeta potential with the increasing amount of LMW chitosan further confirmed the presence of the surface modification of OA liposomes.
Designing a biosensor for versatile biomedical applications is a sophisticated task and how dedicatedly functionalized fullerene (C60) can perform on this stage is a challenge for today and tomorrow's nanoscience and nanotechnology. Since the invention of biosensor, many ideas and methods have been invested to upgrade the functionality of biosensors. Due to special physicochemical characteristics, the novel carbon material "fullerene" adds a new dimension to the construction of highly sensitive biosensors. The prominent aspects of fullerene explain its outstanding performance in biosensing devices as a mediator, e.g. fullerene in organic solvents exhibits five stages of reversible oxidation/reduction, and hence fullerene can work either as an electrophile or nucleophile. Fullerene is stable and its spherical structure produces an angle strain which allows it to undergo characteristic reactions of addition to double bonds (hybridization which turns from sp(2) to sp(3)). Research activities are being conducted worldwide to invent a variety of methods of fullerene functionalization with a purpose of incorporating it effectively in biosensor devices. The different types of functionalization methods include modification of fullerene into water soluble derivatives and conjugation with enzymes and/or other biomolecules, e.g. urease, glucose oxidase, hemoglobin, myoglobin (Mb), conjugation with metals e.g. gold (Au), chitosan (CS), ferrocene (Fc), etc. to enhance the sensitivity of biosensors. The state-of-the-art research on fullerene functionalization and its application in sensor devices has proven that fullerene can be implemented successfully in preparing biosensors to detect glucose level in blood serum, urea level in urine solution, hemoglobin, immunoglobulin, glutathione in real sample for pathological purpose, to identify doping abuse, to analyze pharmaceutical preparation and even to detect cancer and tumor cells at an earlier stage. Employing fullerene-metal matrix for the detection of tumor and cancer cells is also possible by the inclusion of fullerene in single-walled carbon nanotubes (SWCNTs) known as peapods as well as in double-walled carbon nanotubes (DWCNTs), to augment the effectiveness of biosensors. This review discusses various approaches that have been reported for functionalizing fullerene (C60) derivatives and their application in different types of biosensor fabrication.
Fourier transform infrared (FTIR) spectroscopy studies of poly(vinyl alcohol) (PVA), and chitosan polymer blend doped with ammonium nitrate (NH(4)NO(3)) salt and plasticized with ethylene carbonate (EC) have been performed with emphasis on the shift of the carboxamide, amine and hydroxyl bands. 1% acetic acid solution was used as the solvent. It is observed from the chitosan film spectrum that evidence of polymer-solvent interaction can be observed from the shifting of the carboxamide band at 1660 cm(-1) and the amine band at 1591 cm(-1) to 1650 and 1557 cm(-1) respectively and the shift of the hydroxyl band from 3377 to 3354 cm(-1). The hydroxyl band in the spectrum of PVA powder is observed at 3354 cm(-1) and is observed at 3343 cm(-1) in the spectrum of the PVA film. On addition of NH(4)NO(3) up to 30 wt.%, the carboxamide, amine and hydroxyl bands shifted from 1650, 1557 and 3354 cm(-1) to 1642, 1541 and 3348 cm(-1) indicating that the chitosan has complexed with the salt. In the PVA-NH(4)NO(3) spectrum, the hydroxyl band has shifted from 3343 to 3272 cm(-1) on addition of salt from 10 to 30 wt.%. EC acts as a plasticizing agent since there is no shift in the bands as observed in the spectrum of PVA-chitosan-EC films. The mechanism of ion migration is proposed for the plasticized and unplasticized PVA-chitosan-NH(4)NO(3) systems. In the spectrum of PVA-chitosan-NH(4)NO(3)-EC complex, the doublet CO stretching in EC is observed in the vicinity 1800 and 1700. This indicates that there is some interaction between the salt and EC.
The adsorption of residue oil from palm oil mill effluent (POME) using chitosan powder and flake has been investigated. POME contains about 2g/l of residue oil, which has to be treated efficiently before it can be discharged. Experiments were carried out as a function of different initial concentrations of residue oil, weight dosage, contact time and pH of chitosan in powder and flake form to obtain the optimum conditions for the adsorption of residue oil from POME. The powder form of chitosan exhibited a greater rate compared to the flake type. The results obtained showed that chitosan powder, at a dosage of 0.5g/l, 15min of contact time and a pH value of 5.0, presented the most suitable conditions for the adsorption of residue oil from POME. The adsorption process performed almost 99% of residue oil removal from POME. Equilibrium studies have been carried out to determine the capacity of chitosan for the adsorption of residue oil from POME using the optimum conditions from the flocculation at different initial concentrations of residue oil. Langmuir and Freundlich adsorption models were applied to describe the experimental isotherms and isotherm constants. Equilibrium data fitted very well with the Freundlich model. The pseudo first- and second-order kinetic models and intraparticle diffusion model were used to describe the kinetic data and the rate constants were evaluated. The experimental data fitted well with the second-order kinetic model, which indicates that the chemical sorption is the rate-limiting step, i.e. chemisorption between residue oil and chitosan. The significant uptake of residue oil on chitosan was further proved by BET surface area analysis and SEM micrographs.
The microbial breakdown of chitosan, a fishery waste-based material, and its derivative cross-linked chitosans, in both non-contaminated and contaminated conditions was investigated in a laboratory incubation study. Biodegradation of chitosan and cross-linked chitosans was affected by the presence of heavy metals. Zn was more pronounced in inhibiting microbial activity than Cu and Pb. It was estimated that a longer period is required to complete the breakdown of the cross-linked chitosans (up to approximately 100 years) than unmodified chitosan (up to approximately 10 years). The influence of biodegradation on the bioavailable fraction of heavy metals was studied concurrently with the biodegradation trial. It was found that the binding behaviour of chitosan for heavy metals was not affected by the biodegradation process.
Chitosan based adsorbents have received a lot of attention for adsorption of dyes. Various modifications of this polysaccharide have been investigated to improve the adsorption properties as well as mechanical and physical characteristics of chitosan. This review paper discusses major research topics related to chitosan and its derivatives for application in the removal of dyes from water. Modification of chitosan changes the original properties of this material so that it can be more suitable for adsorption of different types of dye. Many chitosan derivatives have been obtained through chemical and physical modifications of raw chitosan that include cross-linking, grafting and impregnation of the chitosan backbone. Better understanding of these varieties and their affinity toward different types of dye can help future research to be properly oriented to address knowledge gaps in this area. This review provides better opportunity for researchers to better explore the potential of chitosan-derived adsorbents for removal of a great variety of dyes.
Gold nanoparticles (AuNPs) had been synthesized with various molarities and weights of reducing agent, monosodium glutamate (MSG), and stabilizer chitosan, respectively. The significance of chitosan as stabilizer was distinguished through transmission electron microscopy (TEM) images and UV-Vis absorption spectra in which the interparticles distance increases whilst retaining the surface plasmon resonance (SPR) characteristics peak. The most stable AuNPs occurred for composition with the lowest (1 g) weight of chitosan. AuNPs capped with chitosan size stayed small after 1 month aging compared to bare AuNPs. The ability of chitosan capped AuNPs to uptake analyte was studied by employing amorphous carbon nanotubes (α-CNT), copper oxide (Cu2O), and zinc sulphate (ZnSO4) as the target material. The absorption spectra showed dramatic intensity increased and red shifted once the analyte was added to the chitosan capped AuNPs.
Chitosan film reinforced with nano-sized chitin whiskers and crosslinked using tannic acid was synthesized by the casting-vaporation method. The mechanical and physicochemical properties of several film samples (consisting of different ratio of chitin and tannic acid) were compared with neat chitosan. Tensile tests show that the addition of chitin improves the nanocomposite films mechanical properties up to 137% compared to neat chitosan, but this is slightly degraded when tannic acid is introduced. However, tannic acid and chitin whisker content greatly reduced moisture content by 294% and water solubility by 13%. Transmission electron microscopy (TEM) and Fourier-transform-infrared spectroscopy (FTIR) were used to investigate the morphology and molecular interaction of film. X-ray diffraction results indicated that the samples with chitin whiskers had a more rigid structure. The addition of tannic acid changed the structure into an anhydrous crystalline conformation when compared to neat chitosan film.
Development of new materials for different applications especially as bio-composites has received great attention. This study concentrates on development of a biopolymer based on chitosan (CT) and halloysite nanotubes (HNT) and evaluates the copper removal intake as a potential application of this bio-composite. In this study, CT/HNT beads were prepared by ultrasonic-assisted extrusion-dripping method for the first time. Two sources of HNTs (i.e. Dragonite and Matauri Bay) were added into a chitosan solution (2wt.%) at various loading fractions (25, 50, 75wt.%). The effect of ultrasound as a mixing device was also studied by varying the amplitude at constant frequency of 25%, 50% and 75%. Characteristics and physical properties of the prepared CT/HNT beads were also analyzed by SEM, FTIR, TGA and BET the results show that introducing HNT to chitosan increases the adsorption capacity toward copper ions; however HNT loading fraction above 50wt.% resulted in a decrease in adsorption capacity attributed to limited accessibility of the amino groups. The adsorption capacity of the CT/HNT beads prepared from Dragonite source had a larger adsorption capacity of 14.2mg/g as compared to that of Matauri Bay, 10.55mg/g. It was observed that the adsorption capacity of the beads toward copper ions decreased when the loading fraction of HNT is increased at constant ultrasound amplitude. The result of this study helps to understand the links between the characteristics and adsorption abilities of CT/HNT beads.
A biotechnological route via enzymatic esterification was proposed as an alternative way to synthesize the problematic anti-oxidant eugenyl benzoate. The new method overcomes the well-known drawbacks of the chemical route in favor of a more sustainable reaction process. The present work reports a Box-Behnken design (BBD) optimization process to synthesize eugenyl benzoate by esterification of eugenol and benzoic acid catalyzed by the chitosan-chitin nanowhiskers supported Rhizomucor miehei lipase (RML-CS/CNWs). Effects of four reaction parameters: reaction time, temperature, substrate molar ratio of eugenol: benzoic acid and enzyme loading were assessed. Under optimum conditions, a maximum conversion yield as high as 66% at 50°C in 5h using 3mg/mL of RML-CS/CNWs, and a substrate molar ratio (eugenol: benzoic acid) of 3:1. Kinetic assessments revealed the RML-CS/CNWs catalyzed the reaction via a ping-pong bi-bi mechanism with eugenol inhibition, characterized by a Vmax of 3.83mMmin-1. The Michaelis-Menten constants for benzoic acid (Km,A) and eugenol (Km,B) were 34.04 and 138.28mM, respectively. The inhibition constant for eugenol (Ki,B) was 438.6mM while the turnover number (kcat) for the RML-CS/CNWs-catalyzed esterification reaction was 40.39min-1. RML-CS/CNWs were reusable up to 8 esterification cycles and showed higher thermal stability than free RML.
Chitosan ionic liquid beads were prepared from chitosan and 1-butyl-3-methylimidazolium based ionic liquids to remove Malachite Green (MG) from aqueous solutions. Batch adsorption experiments were carried out as a function of initial pH, adsorbent dosage, agitation time and initial MG concentration. The optimum conditions were obtained at pH 4.0, 0.008g of adsorbent dosage and 20min of agitation time were utilized in the kinetic and isotherm studies. Three kinetic models were applied to analyze the kinetic data and pseudo-second order was found to be the best fitted model with R2>0.999. In order to determine the adsorption capacity, the sorption data were analyzed using the linear form of Langmuir, Freundlich and Temkin equations. The isotherm was best fitted by Langmuir isotherm model. The maximum adsorption capacity (qmax) obtained from Langmuir isotherm for two chitosan beads 1-butyl-3-methylimidazolium acetate A and 1-butyl-3-methylimidazolium B are 8.07mgg-1 and 0.24mgg-1 respectively.
Crosslinked chitosan beads were grafted with N-vinyl-2-pyrrolidone (NVP) using ammonium persulfate (APS) as free radical initiator. Important variables on graft copolymerization such as temperature, reaction time, concentration of initiator and concentration of monomer were optimized. The results revealed optimum conditions for maximum grafting of NVP on 1g crosslinked chitosan as follows: reaction temperature, 60°C; reaction time, 2h and concentrations of APS and NVP of 2.63×10-1M and 26.99×10-1M, respectively. The modified chitosan beads were characterized by FTIR spectroscopy, 13C NMR, SEM and BET to provide evidence of successful crosslinking and grafting reactions. The resulting material (cts(x)-g-PNVP) was evaluated as adsorbent for the removal of Cu(II) ions from aqueous solutions in a batch experiment. The Langmuir and Freundlich adsorption models were also applied to describe the equilibrium isotherms. The results showed that the adsorption of the copper ions onto the beads agreed well with Langmuir model with the maximum capacity (qmax) of 122mgg-1.