MATERIAL AND METHOD: Forty sound permanent mandibular premolars were collected from a dental clinical setting and disinfected. All forty samples were mounted vertically in a rubber mold exposing only the clinical crown. All samples were bleached using Opalescence Boost Professional Teeth Whitening. After the bleaching procedure, each sample was randomly allocated into four groups according to surface treatment. Samples in group 1 were treated with methylene blue photosensitizer (MBP). Samples in group 2 were exposed to 10% sodium ascorbate. Samples in group 3 were treated with Er, Cr: YSGG laser (ECL). Samples in group 4 were not treated (control). All Samples were treated with 37% phosphoric acid and a bonding agent was applied. A bulk-fill composite was cured to all specimens and all samples were treated in a thermocycler. Specimens were placed in a universal testing machine for shear bond strength (SBS) testing. Descriptive statistics were associated by analysis of variance (ANOVA) and Tukey's post hoc test maintaining level of significance (p<0.05) RESULTS: The lowest SBS scores were achieved in the bleached enamel (BE) group (15.25±1.745 MPa). Whereas, the highest bond integrity was attained by AA group (32.23±1.854 MPa). Samples treated with ECL (31.87±1.659 MPa) and AA (32.23±1.854) were comparable (p>0.05). Samples treated with PDT exhibited significantly different SBS (22.41±1.258) compared to other experimental groups CONCLUSION: ECL showed a reversal effect of BE compared to AA and has the potential to be used in clinical settings. BE reversal using MBP needs further investigation.
MATERIALS AND METHODS: Sound extracted human molars were randomly divided into: manufacturer's instructions (MI), manual blend 2 mm (MB2), and manual blend 4 mm (MB4). Occlusal enamel was removed and flattened, dentin surfaces were bonded by Prime & Bond universal (Dentsply and Optibond FL, Kerr). For the MI group, adhesives were applied following the manufacturer's instructions then light-cured. For MB groups, SDR flow+ bulk-fill flowable composite resin was applied in 2- or 4-mm increment then manually rubbed by a micro brush for 15 s with uncured dentine bonding agents and the mixture was light-cured. Composite buildup was fabricated incrementally using Ceram.X One, Dentsply nanohybrid composite resin restorative material. After 24-h water storage, the teeth were sectioned to obtain beams of about 0.8 mm2 for 24-h and thermocycled micro-tensile bond strength at 0.5 mm/min crosshead speed. Degree of conversion was evaluated with micro-Raman spectroscopy. Contraction gaps at 24 h after polymerization were evaluated and atomic force microscopy (AFM) nano-indentation processes were undertaken for measuring the hardness across the interface. Depth of resin penetration was studied using a scanning electron microscope (SEM). Bond strength data was expressed using two-way ANOVA followed by Tukey's test. Nanoindentation hardness was separately analyzed using one-way ANOVA.
RESULTS: Factors "storage F = 6.3" and "application F = 30.11" significantly affected the bond strength to dentine. For Optibond FL, no significant difference in nanoleakage was found in MI/MB4 groups between baseline and aged specimens; significant difference in nanoleakage score was observed in MB2 groups. Confocal microscopy analysis showed MB2 Optibond FL and Prime & Bond universal specimens diffusing within the dentine. Contraction gap was significantly reduced in MB2 specimens in both adhesive systems. Degree of conversion (DC) of the MB2 specimens were numerically more compared to MS1 in both adhesive systems.
CONCLUSION: Present study suggests that the new co-blend technique might have a positive effect on bond strengths of etch-and-rinse adhesives to dentine.
METHODS: A 24-item validated questionnaire including closed and open questions on the teaching of posterior composites was emailed to faculty members in all 13 Dental Schools in Malaysia. Responses were compiled on Excel and analysed.
RESULTS: All 13 dental schools responded to the survey yielding a 100 % response. All schools indicated the use of posterior composites for 2- and 3-surface cavities in premolars and molars. The didactic teaching time devoted to composites was greater than for amalgam (38 h vs 29 h). Clinically, most posterior restorations placed by students were composites (average 74.1 %, range 10 %-100 %); the remaining 25.9 % were amalgams (range, 0 %-50 %). Slot-type cavities were the preparation techniques most commonly taught (n = 11,84.6 %). The use of rubber dam for moisture control was mandatory in most schools (n = 11, 84.6 %). History of adverse reaction to composites was found to be the most common contraindication to composite placement. The phase down of teaching and use of amalgam in Malaysia is expected to occur within the next six years.
CONCLUSION: The trend to increase the teaching of posterior composites reported for other countries is confirmed by the findings from Malaysian dental schools. Notwithstanding this trend, the use of amalgam is still taught, and future studies are required to investigate the implications of the phase down of amalgam in favour of posterior composites.
CLINICAL SIGNIFICANCE: Notwithstanding the increase in the teaching of posterior composites there is a pressing need to update and refine clinical guidelines for the teaching of posterior composites globally.
METHODS: Randomized controlled trials and cohort studies with a minimum 2-year follow-up assessing survival and complication rates of resin composite laminate veneers on permanent dentition from 1998 to May 2022. Literature searches were conducted in MEDLINE (PubMed), Scopus, and the Cochrane Central Register of Controlled Trials electronic databases. References cited in the related reviews and included full-text articles were also hand-searched to further identify potentially relevant studies.
RESULTS: A total of 827 articles were identified. Twenty-two studies were considered for full-text review after the title and abstract screening stage. After exclusion, 7 studies (3 randomized controlled trials and 4 cohort studies) were included in the systematic review. Three published scales were adopted for the quality and risk of bias assessment. At the survival rate threshold, the overall heterogeneity (I2) for randomized controlled trials was 50.5% (P = .108). The overall pooled survival rate of the randomized controlled trials was 88% (95% CI: 81%-94%), with the mean follow-up time ranging from 24 to 97 months. Surface roughness, color mismatch, and marginal discoloration were the most reported complications.
CONCLUSION: Resin composite laminate veneers demonstrated moderately high survival rates for the entire sample and the direct laminate veneer group demonstrated higher survival rates than the indirect approach. Most of the complications were regarded as clinically acceptable with or without reintervention.
METHODS: Silanated, titanated and pure NBT at 5% were incorporated in PMMA matrix. Neat PMMA matrix served as a control. NBT was sonicated in MMA prior to mixing with the PMMA. Curing was carried out using a water bath at 75°C for 1.5h and then at 100°C for 30min. NBT was characterised via Fourier transform-infrared spectroscopy (FTIR), Transmission Electron Microscopy (TEM) and Brunauer-Emmett-Teller (BET) analysis before and after surface modification. The porosity and fracture toughness of the PMMA nanocomposites (n=6, for each formulation and test) were also evaluated.
RESULTS: NBT was successfully functionalised by the coupling agents. The TCA exhibited the lowest percentage of porosity (0.09%), whereas silane revealed 0.53% porosity. Statistically significant differences in fracture toughness were observed among the fracture toughness values of the tested samples (p<0.05). While the fracture toughness of untreated samples was reduced by 8%, an enhancement of 25% was achieved after titanation. In addition, the fracture toughness of the titanated samples was higher than the silanated ones by 10%.
CONCLUSION: Formation of a monolayer on the surface of TCA enhanced the NBT dispersion, however agglomeration of silanated NBT was observed due to insufficient coverage of NBT surface. Such behaviour led to reducing the porosity level and improving fracture toughness of titanated NBT/PMMA composites. Thus, TCA seemed to be more effective than silane.
CLINICAL SIGNIFICANCE: Minimising the porosity level could have the potential to reduce fungus growth on denture base resin to be hygienically accepTable Such enhancements obtained with Ti-NBT could lead to promotion of the composites' longevity.
Materials and Methods: In this in-vitro study, a total of 48 single-rooted permanent human teeth were decoronated, and the roots were treated endodontically. Following post space preparation, the sample was divided into four groups (n= 12 each) based on the types of post and cement. Two different types of post [GC everStick®POST (ES) and Parapost® Fiber LuxTM (PF)], and two different types of cement [G-CEMTM (G), and RelyXTM Unicem (R)] were used according to the manufacturer's instructions. All roots were sectioned at the coronal and middle thirds with a thickness of 3±0.1mm. The Push-out bond strength (PBS) test was performed using a universal testing machine at a cross-head speed of 0.5mm/ min. The bond strength values were recorded, and the data were analyzed using the SPSS program. Apart from descriptive statistics, three-way ANOVA was used for the interaction of the independent variables (post, cement, and root level). For differences between the groups, the Mann-Whitney U test was used. A P-value of less than 0.05 was considered significant for all analyses.
Results: Push-out bond strength of samples at the middle level (11.38±10.31 MPa), with PF posts (11.18±9.98 MPa), and of those luted with RelyXTM Unicem cement (13.26±8.73 MPa) was higher than that of their counterparts. The PBS means of RelyXTM Unicem cement at both root levels were much higher than PBS means of G-CEMTM cement. Three-way ANOVA test revealed a significant effect for each variable with a higher effect of cement (Sum of Squares= 1310.690; P< 0.001). No significant difference (P= 0.153) was found between the coronal and middle parts and between ES and PF posts (P= 0.058). However, a highly significant difference (P< 0.001) was found between RelyXTM Unicem and G-CEMTM cements.
Conclusion: The type of cement had a significant effect on push-out bond strength with RelyXTM Unicem which had higher values than G-CEMTM. However, the type of post and root level had no significant effect on PBS, although Parapost® Fiber LuxTM and middle root level had higher values than their counterparts.
Materials and Methods: Sixty-eight human maxillary permanent incisors were divided into four groups. Each specimen was endodontically treated with step-back technique and prepared for each post system according to experimental groups, subsequently cemented in the canal. Composite resin cores were built and laboratory fabricated metal crowns were cemented. All specimens except those in the control group were subjected to thermal cycling. All groups were subjected to gradual loading from 0N-50N for 100 cycles. Specimens were sectioned transversely and the depths of dye penetration along the post were measured. Data were entered in SPSS ver. 22 and analyzed using two-way ANOVA test.
Results: There was no significant difference in marginal dye penetration between each group (p-value>0.05). However, there was a significant difference in percentage of marginal dye penetration between all groups (p-value<0.05); post-hoc comparison showed significant difference between Fiber White and Control groups (p-value=0.009).
Conclusion: All the groups showed dye penetration but the percentage was significant only between Parapost Fiber White and the control groups.
METHODS: Sixty-five extracted maxillary incisors were decoronated, its canal was artificially flared and randomly categorized into group tFRC (tapered FRC post) (n = 22), mFRC (multi-FRC post) (n = 21), and DIS-FRC (direct individually shaped-FRC (DIS-FRC) post) (n = 22), which were further subdivided based on cementation resin. The posts were cemented and a standardized resin core was constructed. After thermocycling, the samples were loaded statically and the maximum load was recorded.
RESULTS: The load capacity of the maxillary central incisor was influenced by the different FRC post system and not the resin cement (p = 0.289), and no significant interaction was found between them. Group mFRC (522.9N) yielded a significantly higher load capacity compared to DIS-FRC (421.1N). Overall, a 55% favorable fracture pattern was observed, and this was not statistically significant.
CONCLUSION: Within the limitation of the study, it can be concluded that prefabricated FRC posts outperform DIS-FRC posts in terms of the load capacity of a maxillary central incisor with a simulated flared root canal. The cementation methods whether a self-adhesive or self-etch resin cement, was not demonstrated to influence the load capacity of a maxillary central incisor with a flared root canal. There were no significant differences between the favorable and non-favorable fracture when FRC post systems were used to restored a maxillary central incisor with a flared root canal.
Materials and Methods: This an in vitro study was done by preparing cavities on the buccocervical surface of 62 extracted premolar teeth which randomly assigned to two groups (n = 31) where Group 1 was restored with nanocomposite and Group 2 was cemented with porcelain cervical inlays. They were then subjected to thermocycling before immersion in 2% methylene blue dye for 24 h. Dye penetration depths were measured using Leica imaging system For statistical analysis, independent t-test was used to analyze the results (P < 0.05).
Results: Porcelain cervical inlay restorations demonstrated statistically lesser microleakage depth for the cervical margins (P = 0.018) when compared to CR. Deeper microleakage depth at the cervical compared to coronal margins of CR (P = 0.006) but no significant difference of both margins for porcelain cervical inlays (P = 0.600).
Conclusion: Porcelain cervical inlays show lesser microleakage than CR which could be alternative treatment option in restoring NCCL with better marginal seal and esthetics.