MATERIALS AND METHODS: Sound extracted human molars were randomly divided into: manufacturer's instructions (MI), manual blend 2 mm (MB2), and manual blend 4 mm (MB4). Occlusal enamel was removed and flattened, dentin surfaces were bonded by Prime & Bond universal (Dentsply and Optibond FL, Kerr). For the MI group, adhesives were applied following the manufacturer's instructions then light-cured. For MB groups, SDR flow+ bulk-fill flowable composite resin was applied in 2- or 4-mm increment then manually rubbed by a micro brush for 15 s with uncured dentine bonding agents and the mixture was light-cured. Composite buildup was fabricated incrementally using Ceram.X One, Dentsply nanohybrid composite resin restorative material. After 24-h water storage, the teeth were sectioned to obtain beams of about 0.8 mm2 for 24-h and thermocycled micro-tensile bond strength at 0.5 mm/min crosshead speed. Degree of conversion was evaluated with micro-Raman spectroscopy. Contraction gaps at 24 h after polymerization were evaluated and atomic force microscopy (AFM) nano-indentation processes were undertaken for measuring the hardness across the interface. Depth of resin penetration was studied using a scanning electron microscope (SEM). Bond strength data was expressed using two-way ANOVA followed by Tukey's test. Nanoindentation hardness was separately analyzed using one-way ANOVA.
RESULTS: Factors "storage F = 6.3" and "application F = 30.11" significantly affected the bond strength to dentine. For Optibond FL, no significant difference in nanoleakage was found in MI/MB4 groups between baseline and aged specimens; significant difference in nanoleakage score was observed in MB2 groups. Confocal microscopy analysis showed MB2 Optibond FL and Prime & Bond universal specimens diffusing within the dentine. Contraction gap was significantly reduced in MB2 specimens in both adhesive systems. Degree of conversion (DC) of the MB2 specimens were numerically more compared to MS1 in both adhesive systems.
CONCLUSION: Present study suggests that the new co-blend technique might have a positive effect on bond strengths of etch-and-rinse adhesives to dentine.
Materials and methods: The antimicrobial effects of vitamin D3 were evaluated against Strep. sobrinus and Strep mutans using the agar disc diffusion method. The minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) of vitamin D3 were determined using a microdilution method following the guidelines by the Clinical Laboratory Standards Institute (CLSI). Scanning electron microscope (SEM) was used to evaluate the morphological changes of bacterial cells following exposure to vitamin D3.
Results: Strep. sobrinus was more sensitive to vitamin D3 compared to Strep. mutans bacteria. The MIC values of vitamin D3 against Strep. sobrinus and Strep. mutans were 60 μg/ mL and 250 μg/mL respectively whereas the MBC values were 120 μg/mL and 500 μg/mL, respectively. Moreover, significant changes in the bacterial morphology were observed in treated bacterial cells with vitamin D3 as compared to the untreated control bacteria using SEM.
Conclusion: These findings suggested that vitamin D3 has excellent antimicrobial effects against Strep. sobrinus and Strep. mutans and may be considered as a promising compound in the prevention of dental caries in the future. Further research is recommended to elucidate the mechanism of vitamin D3 on these bacteria.