Moisture susceptibiltiy is one of the common types of pavement failure found in asphaltic pavements.
Climatic factor such as temperature and moisture has a profound effect on the durability of hot mix
asphalt pavements. Couple with high traffic loads/stresses made stripping of pavement materials
inevitable. Thus, it has become necessary to improve the efficiency of the design of hot mix asphalt
(HMA) for better performance and safe riding comfort. This study investigates and discusses the findings
on the stripping performance of dense graded Superpave mixes using two type of binder; un-modified
binder and rubber polymer modified binder (RPM) using Superpave mix design (AASHTO TP4)
procedure. The RPM binder consists of 4% of both rubber crumb and EVA polymer. Modified Lottman
and Resilient Modulus tests were used to evaluate the stripping performance in these mixtures and this
study also documents the effect of different temperature on tensile strength ratio (TSR) and resilient
modulus ratio (RMR) on the HMA mixtures. Experimental evidences show that the RPM binder mixes
were found to have significantly improved the resistance to moisture damage compared to unmodified
binder mixtures. The RPM binder application may able to alleviate problems related to aggregate
stripping and potholes on our road. Statistical analysis showed good correlation between resilient
modulus and tensile strength ratio.
Ferrocement panels, while offering various benefits, do not cover instances of low and moderated velocity impact. To address this problem and to enhance the impact strength against low-velocity impact, a fibrous ferrocement panel is proposed and investigated. This study aims to assess the flexural and low-velocity impact response of simply supported ferrocement panels reinforced with expanded wire mesh (EWM) and steel fibers. The experimental program covered 12 different ferrocement panel prototypes and was tested against a three-point flexural load and falling mass impact test. The ferrocement panel system comprises mortar reinforced with 1% and 2% dosage of steel fibers and an EWM arranged in 1, 2, and 3 layers. For mortar preparation, a water-cement (w/c) ratio of 0.4 was maintained and all panels were cured in water for 28 days. The primary endpoints of the investigation are first crack and ultimate load capacity, deflection corresponding to first crack and ultimate load, ductility index, flexural strength, crack width at ultimate load, a number of impacts needed to induce crack commencement and failure, ductility ratio, and failure mode. The finding revealed that the three-layers of EWM inclusion and steel fibers resulted in an additional impact resistance improvement at cracking and failure stages of ferrocement panels. With superior ultimate load capacity, flexural strength, crack resistance, impact resistance, and ductile response, as witnessed in the experiment program, ferrocement panel can be a positive choice for many construction applications subjected to repeated low-velocity impacts.
This study examined the development of starch/oil palm empty fruit bunch-based bioplastic composites reinforced with either epoxidized palm oil (EPO) or epoxidized soybean oil (ESO), at various concentrations, in order to improve the mechanical and water-resistance properties of the bio-composites. The SEM micrographs showed that low content (0.75 wt%) of epoxidized oils (EOs), especially ESO, improved the compatibility of the composites, while high content (3 wt%) of EO induced many voids. The melting temperature of the composites was increased by the incorporation of both EOs. Thermal stability of the bioplastics was increased by the introduction of ESO. Low contents of EO led to a huge enhancement of tensile strength, while higher contents of EO showed a negative effect, due to the phase separation. The tensile strength increased from 0.83 MPa of the control sample to 3.92 and 5.42 MPa for the composites with 1.5 wt% EPO and 0.75 wt% ESO, respectively. EOs reduced the composites' water uptake and solubility but increased the water vapor permeability. Overall, the reinforcing effect of ESO was better than EPO. These results suggested that both EOs can be utilized as modifiers to prepare starch/empty-fruit-bunch-based bioplastic composites with enhanced properties.
The response of human skin to "stress relaxation" tests at low loads in vitro was investigated. A number of behaviours, other than those already well established and documented, were observed. The significant behaviours are pure recovery and relaxation-recovery. Other behaviours observed are temporary stress recovery during the relaxation process, and momentary sudden non-linear drop in stress value followed by a second relaxation. The pure recovery and relaxation-recovery responses are repeatable. The latter represents the transitional response between the well-known behaviour of stress relaxation and the behaviour of stress recovery.
The mean strength that has traditionally been taken as a measurement of the strength of a material does not reflect the true strength, and therefore it cannot be used as a design parameter. This explains why many brittle materials fail at unpredictable stress, either below or above the mean strength. By using Weibull statistics, the prediction and assessment of strength can be made more sensibly. The performance of a material can be predicted by considering a stress at a lower level of failure probability.
This paper reports the mechanical properties of cement composite boards made using wood-wool from a lesser known Malaysian timber species. A total of 108 specimens were fabricated using Portland cement (Type I) and wood-wool from Kelampayan (Neolamarckia cadamba). The cement to wood ratio of the specimens was 2 to 1 by weight. The aim of the study was to determine the density; flexural, compressive and tensile strength of wood-wool cement composite boards (WWCCB) by studying boards with wood-wool sized 1.5 mm, 2.5 mm and 3.5 mm and board thickness 25 mm, 50 mm and 75mm. The physical and mechanical properties of the boards were evaluated according to ASTM D 1037-96a (Standard testing method for evaluating properties of wood-based fibre and particle panel materials) and MS934:1986. Results showed that mechanical properties of WWCCB were greatly influenced by the density; as the density decreased, the mechanical strengths also decreased. However, the strength properties of the composite boards did not display a similar trend when subjected to different types of loading conditions. The compressive strength increased with thicker boards (50 mm and 75 mm) but the modulus of elasticity and modulus of rupture declined as the thickness of the board was increased.
Introducing CO2 flux as the carbonate source had an effect on the carbonate content of carbonate apatite (CAp) synthesized by solid state reaction. The reactants were CaCO3 and beta-tricalcium phosphate (β-TCP) and the heat treatment in air was performed at 1250ºC followed by instant cooling in CO2 flux for temperatures ranging from 800ºC room temperature (RT) . The influence of CO2 flux at various temperature drop differences in the cooling process (1250ºC RT, 1250ºC–500ºC, 1250ºC–600ºC, 1250ºC–700ºC, and 1250ºC–800ºC) was tested to optimize the carbonation degree and subsequent effects on the physical and mechanical properties of CAp. Thermally treated samples revealed an increasing degree of carbonation, achieving a maximum of 5.2 wt% at the highest (1250ºC RT) and a minimum of 2.7 wt% at the lowest (1250ºC–800ºC) temperature drop differences, respectively. This showed that the carbonate content was correlated with the increase in exposure to CO2 flux. However, consistent compressive strength, tensile strength, density and porosity were observed against increasing temperature drop differences which indicated that the degree of carbonation exerted no influence on the physical and mechanical properties of CAp. This method enabled the synthesis of solid state CAp simply by exposing calcium phosphate mixtures to CO2 flux. It also allowed the control of carbonate content for desired medical applications.
A study on the effects of alkali treatment and compatibilising agent on the tensile properties of pineappleleaf fibre (PALF) reinforced high impact polystyrene (HIPS) composite is presented in this paper. Thetensile properties of natural fibre reinforced polymer composites are mainly influenced by the interfacialadhesion between the matrix and the fibres. In this study, several chemical modifications were employedto improve the interfacial matrix-fibre bonding and this resulted in the enhancement of tensile propertiesof the composites. In this study, the surface modification of pineapple fibre with alkali treatments andcompatibilizer were used to improve the adhesion between hydrophilic pineapple fibre and hydrophobicpolymer matrix. There are two concentrations of NaOH treatments and compatibilizer used in this study,namely, 2 and 4 wt. %. The results show that the alkali treated fibre and the addition of compatibilisingagent in PALF/HIPS composites have improved the tensile strength and tensile modulus of the composites.
Synthesis of palm oil based-urethane acrylate (POBUA) resins was carried out by acrylation of epoxidizedpalm oil (EPOP) using acrylic acid in the presence of a catalyst and followed by isocyanation to obtainthe POBUA. Using the monomer as a diluent in the formulation, 4% of photoinitiator and incorporationof organoclay (1-5% wt), nanocomposites were obtained upon UV irradiation. The X-ray DiffractoryXRD study revealed that the nanocomposites obtained were of the exfoliation type. The presence ofthe clay improved the hardness and did not affect the thermal stability. Similarly, it increased the glasstransition temperature Tg but reduced the modulus as the clay content was increased. The improvementof the tensile strength was only obtained when the clay concentration was 5 phr.
Electron beam irradiation, without any addition of cross-linking agents, was investigated at varying
doses of EB-Irradiation to develop an environmentally friendly hybridized kenaf (bast)/ pineapple leaf
fibre (PALF) bio-composites. Improvement in tensile property of the hybrid was achieved with the result
showing a direct proportionality relationship between tensile properties and increasing radiation dose.
Statistical analysis software (SAS) was employed to validate the result. HDPE has been shown to have
self-cross-linked, enabling interesting tensile properties with irradiation. Statistical analysis validated
the results obtained and also showed that adequate mixing of fibres and matrix had taken place at 95%
confidence level. Hybridization and subsequent irradiation increased the tensile strength and modulus
of HDPE up to 31 and 185%, respectively, at about 100kGy. Meanwhile, SEM was used to view the
interaction between the fibres and matrix.
Epoxidised Natural Rubber (ENR) is now a commercially available polymer produced by chemical modification of natural rubber. Currently, three types of ENR are commercially available, and these are ENR 10, ENR 25, and ENR 50 with 10%, 25%, and 50% mol epoxidation, respectively. Studies on prevulcanisation of ENR 50 and postvulcanisation of the latex films were carried out. The objective of this study was to develop ENR 50 that could be dipped easily in coagulant dipping solution to produce dipped products. Several attempts were made by compounding prevulcanised ENR 50 at various sulphur levels ranging from 0.5 to 3.0 pphr. Using suitable coagulant dipping systems, ENR 50 film could be formed despite the high contents of non-ionic surfactant. It was found that the tensile strength of prevulcanised ENR 50 film decreased with the increase in the sulphur level. The results show that as level of sulphur increased, M300 also increased to an optimum value of 1.5 pphr of sulphur. For the postvulcanised ENR 50 film, however, the tensile strength increased and then decreased with the increasing sulphur level. Meanwhile M300 increased with the increasing postvulcanization time and sulphur level. The postvulcanisation of ENR 50 film seems to be a more effective way of increasing tensile properties than by prevulcanisation of ENR 50.
Linear density polyethylene (LDPE)/thermoplastic sago starch (TPSS), blended with and without the addition of compatibilizer [Polyethylene-grafted-Maleic Anhydride, (PE-g-MA)] were prepared for soil burial test. The test was conducted in the natural soil environment for 3 and 6 months. Different loading of TPSS (10, 20, 30, 40, and 50 wt. %) were used in this study. After soil burial, the blends were evaluated for their tensile properties and scanning electron microscopy (SEM) to observe the surface morphology properties after the test. For LDPE/TPSS, it was observed that the tensile strength decreased with the increase of soil burial time, as well as Young modulus and elongation at break (EB). The LDPE/TPSS/PE-g-MA also showed the same trend for the tensile properties, but with higher properties as compared to uncompatibilized blends. The tensile properties also decreased with the increase in the TPSS loading for both the LDPE/TPSS and LDPE/TPSS/PE-g-MA. Meanwhile,
the scanning electron microscopy (SEM) on the blend surfaces after the soil burial test showed that degradability increased with the increase in the exposure time as well as the TPSS loading.
Natural fiber is incompatible with hydrophobic polymer due to its hydrophilic nature. Therefore, surface modification of fiber is needed to impart compatibility. In this work,superheated steam (SHS)-alkali was introduced as novel surface treatment method to modify oil palm mesocarp fiber (OPMF) for fabrication of biocomposites. The OPMF was first pre-treated with SHS and subsequently treated with varying NaOH concentration (1, 2, 3, 4 and 5%) and soaking time (1, 2, 3 and 4h) at room temperature. The biocomposites were then fabricated by melt blending of 70 wt% SHS-alkali treated-OPMFs and 30 wt% poly(butylene succinate) in a Brabender internal mixer followed by hot-pressed moulding. The combination treatment resulted in fiber with rough surface as well as led to the exposure ofmicrofibers. The tensile test result showed that fiber treated at 2% NaOH solution and 3h soaking time produced biocomposite with highest improvement in tensile strength (69%) and elongation at break (36%) in comparison to that of untreated OPMF. The scanning electron micrographs of tensile fracture surfaces of biocomposite provide evident for improved adhesion between fiber and polymer after thetreatments.This work demonstrated that combination treatments of SHS and NaOH could be a promising way to modify OPMF for fabrication of biocomposite.
Banana pulp (BP) noodles prepared by partial substitution of wheat flour with green Cavendish banana pulp flour were assessed pH, color, tensile strength and elasticity, and in-vitro hydrolysis index (HI) and estimated glycemic index (GI). BP noodles had lower L* (darker) and b* values (less yellow) but higher tensile strength and elasticity modulus than control noodles. Following an in-vitro starch hydrolysis studies, it was found that GI of BP noodles was lower than control noodles. Partial substitution of green banana pulp into noodles may be useful for controlling starch hydrolysis of yellow noodles.
Polyvinyl chloride (PVC) and ammonio methacrylate copolymer (Eudragit RS 100) were used as models in binary mixture tablets of direct compression study. Eudragit RS 100 is a copolymer synthesized from acrylic and methacrylic acid esters with a low content of quaternary ammonium groups. Combination of PVC and Eudragit RS 100 of different polarities and knowing the surface free energy values allow the possibility of predicting the tensile strength of the tablets. Specimens of 500 mg in the form of thin plates (25 mm x 12.5 mm), were made by compressing each powder at 20 000 MP a compression pressure using a special punch and die set. A Howden Universal Testing Machine was used to compress the powder. Contact angle measurements of the samples were carried out using a Wilhelmy balance, ran by a Cahn Dynamic Contact Angle Machine while different test liquids media such as water, glycerol, formamide and PEG 200 were used in the study. The surface free energy values of the solid materials were calculated using Wu's equation. The results showed large differences between the advancing and receding contact angle values for both materials when tested with glycerol: PVC (0) and PVC (0,) were 93.2 and 65.24 while Eudragit RS 100 (0) and Eudragit RS 100 (0) were 94.56 and 68.18 respectively. The surface free energy values for PVC using PEG 200-glycerol liquid pair were Is: 38.01, ysci: 33.42, ysP: 4.59 and for Eudragit RS 100 using formamide-glycerol liquid pair were ys: 75.03, yd: 51.66, ysP : 23.37, respectively. The results showed harder solid material like Eudragit RS 100 had higher surface free energy compared to elastic material like PVC.
The objectives of this study were to develop composite films using various gelatin sources with corn oil (CO) incorporation (55.18%) and to investigate the mechanical and physical properties of these films as potential packaging films. There were increases (p < 0.05) in the tensile strength (TS) and puncture strength (PS) of films when the concentration of gelatin increased. The mechanical properties of these films were also improved when compared with films produced without CO. Conversely, the water barrier properties of composite films decreased (p < 0.05) when the concentration of gelatin in composite films increased. Comparing with pure gelatin films, water and oxygen barrier properties of gelatin films decreased when manufactured with the inclusion of CO.
This study examines the effects of varying the concentrations of sorbitol (S) and glycerol (G) on the physical, morphological, thermal, and mechanical properties of Dioscorea hispida, starch-based films. In this context, the films of Dioscorea hispida starch were developed using solution casting technique with glycerol (G), sorbitol (S), and a mixture of sorbitol-glycerol (SG) as plasticizers at the ratios of 0, 30, 45, and 60 wt%. The films' moisture contents were increased when increasing the plasticizer contents. The tensile strengths were decreased, but elongations at break were increased; 7.38%-11.54% for G-plasticized films, 10.17%-15.76% for S-plasticized films, and 14.41%- 16.10% for SG-plasticized films with increasing plasticizer concentrations of the film samples. Varying plasticizer concentrations exhibited a minor effect on the S-plasticized film's thermal properties. Significant decrement in the glass transition temperatures of Dioscorea hispida starch films was observed when the plasticizer contents were raised from 30% to 60%. Significantly, the present work has shown that plasticized Dioscorea hispida starch can be considered a promising biopolymer for the applications of biodegradable films.
We formulated a pH-sensitive chlorhexidine-loaded mesoporous silica nanoparticles (MSN) modified with poly-(lactic-co-glycolic acid) (CHX-loaded/MSN-PLGA) and incorporated into experimental resin-based dentin adhesives at 5 and 10 wt%. Nanocarriers were characterized in terms of morphology, physicochemical features, spectral analyses, drug-release kinetics at varying pH and its effect on dentin-bound proteases was investigated. The modified dentin adhesives were characterized for cytotoxicity, antimicrobial activity, degree of conversion (DC) along with CHX release, micro-tensile bond strength (μTBS) and nano-leakage expression were studied at different pH values and storage time. CHX-loaded/MSN-PLGA nanocarriers exhibited a significant pH-dependent drug release behavior than CHX-loaded/MSN nanocarriers without PLGA modification. The highest percentage of CHX release was seen with 10 wt% CHX-loaded/MSN-PLGA doped adhesive at a pH of 5.0. CHX-loaded/MSN-PLGA modified adhesives exhibited more profound antibiofilm characteristics against S. mutans and more sustained CHX-release which was pH dependent. After 6 months in artificial saliva at varying pH, the 5 wt% CHX-loaded/MSN-PLGA doped adhesive showed excellent bonding under SEM/TEM, higher μTBS, and least nano-leakage expression. The pH-sensitive CHX-loaded/MSN-PLGA could be of crucial advantage for resin-dentin bonding applications especially in reduced pH microenvironment resulting from biofilm formation; and the activation of dentin-bound proteases as a consequence of acid etching and acidic content of bonding resin monomers.
In this paper, the effects of stacking sequence and ply orientation on the mechanical properties of pineapple leaf fibre (PALF)/carbon hybrid laminate composites were investigated. The hybrid laminates were fabricated using a vacuum infusion technique in which the stacking sequences and ply orientations were varied, which were divided into the categories of cross-ply symmetric, angle-ply symmetric, and symmetric quasi-isotropic. The results of tensile and flexural tests showed that the laminate with interior carbon plies and ply orientation [0°, 90°] exhibited the highest tensile strength (187.67 MPa) and modulus (5.23 GPa). However, the highest flexural strength (289.46 MPa) and modulus (4.82 GPa) were recorded for the laminate with exterior carbon plies and the same ply orientation. The fracture behaviour of the laminates was determined by using scanning electron microscopy, and the results showed that failure usually initiated at the weakest PALF layer. The failure modes included fibre pull-out, fibre breaking, matrix crack, debonding, and delamination.
Renewable materials have some bearing on the environment and have since increased research works related to polymer composites. This work was conducted to investigate the effects of interwoven kenaf fibres and the use of kenaf fibres in composites. In this research, interwoven between kenaf and polyethylene terephthalate (PET) was prepared and epoxy was used as the polymer matrix to form composites. The kenaf fibre composites with various kenaf fibre contents (2, 5, 8, and 10 wt %) interwoven with (PET) fibres were prepared by using open mould method. The properties of kenaf/PET/epoxy composites (KPTE) were studied. The kenaf fibre composites characterization was determined based on their mechanical properties, water absorption, morphology and thermal properties. The tensile strength test was performed using Testometric machine. The finding shows that the strength increases as the amount of kenaf fibres in the composites increases. The composites with 10% kenaf fibres interwoven PET displayed the highest tensile strength (85.3 ± 2.9 MPa) while unfilled epoxy show the lowest tensile strength (64.1 ± 16.5 MPa). The addition of kenaf fibres minimally increases the water absorption up to about 1.4%. The increases of kenaf fibres also reduces the overall thermal stability of the composites compared to the PET and epoxy resin composites. The morphology properties of KPTE composites support the tensile properties surface of the composites. This study assists to propose the kenaf fibres as a potential filler for properties improvements in epoxy-based composites contributing to the development of another environment-friendly material.