Methods: Seeds of T. ammi were extracted using three different solvents n-hexane, chloroform, and methanol by using soxhlet apparatus. To assess the immunomodulatory effect, delayed-type hypersensitivity (DTH) assay method was used and by the DTH assay, the effect of T. ammi on the skin thickness of rats was estimated. To find the exact dose for administration, acute toxicity test was performed using crude methanolic extract at a dose of 400, 800, 1600, and 3200mg/kg. After acute toxicity test, 500mg/kg dose was determined as safe for therapeutic effect and immunomodulatory effect was evaluated at this dose. Dose of 500mg/kg was administered to Wistar rats daily for 14 days and skin thickness of rats was measured at 24, 48, and 72h.
Results: Results were obtained from six groups of rats, which were positive control group, negative control group, and the groups receiving the test drugs. Standard drug was the combination of sodium selenite, vitamin E, and sodium chloride and it showed more positive results as compared to that of test drug. Furthermore, among the three extracts, methanol extract showed more effectiveness on skin thickness.
Conclusion: There was a meaningful difference was observed between the skin thickness of rats which shows that T. ammi have good immunomodulatory as well as immunostimulant activity.
MATERIAL AND METHOD: Two hundred discs of PEEK were prepared of 6 mm × 2 mm × 10 mm dimension. The discs were randomly divided into five groups (n = 40) for treatment, Group I: treatment with deionized distilled water (control group); Group II: PD therapy using curcumin PS; Group III: discs treated and abraded with air-borne particles (ABP) silica (30 μm particle size) modified alumina (Al); Group IV: ABP of alumina (110 μm particle size); and Group V: The PEEK were finished with 600-μm grit size straight diamond cutting bur installed in high speed hand-piece. The surface profilometer was used to evaluate the values of surface roughness (SRa) of pretreated PEEK discs. The discs were luted and bonded to discs of composite resin. The bonded PEEK samples were placed in Universal testing machine to evaluate shear BS. The type of BS failure for PEEK discs pre-treated with five regimes respectively was evaluated under stereo-microscope. The data was statistically analyzed using one-way ANOVA and the comparisons between mean values of shear BS were evaluated by Tukey's test (ρ≤0.05).
RESULTS: The PEEK samples pre-treated with diamond cutting straight fissure burs displayed statistically significant highest value of SRa values (3.258± 0.785 µm). Similarly, the shear BS was observed to be higher for the PEEK discs pre-treated with straight fissure bur (22.37±0.78 MPa). A comparable difference but not statistically significant difference was observed between PEEK discs pre-treated by curcumin PS and ABP-silica modified alumina (ρ ≥ 0.05).
CONCLUSION: PEEK discs pre-treated with diamond grit straight fissure bur displayed highest values of SRa and shear BS. It was trailed by ABP-Al pre-treated discs; whereas the SRa and shear BS values for the discs pre-treated with ABP-silica modified Al and curcumin PS did not show competitive difference.