METHODS: To assess neurosurgery research in Afghanistan, searches were conducted in databases for articles originating from Afghanistan neurosurgeons and/or neurosurgery departments. We developed a 30-question English-language survey to assess the current state of neurosurgical capacity. Surveys were distributed to neurosurgeons throughout Afghanistan via email with the assistance of our English-speaking Afghan neurosurgical colleagues.
RESULTS: The neurosurgical disease burden of Afghanistan is poorly understood due to the lack of centralized and accessible databases. There are an estimated 124 neurosurgeons in the country based on modeled data. Surveys showed that government hospitals are poorly equipped, with private and military hospitals having access to slightly more modernized equipment but less accessible to the general population. The country lacks neurosurgery research with only 15 papers discovered through database searches deemed relevant to neurosurgery with Afghan affiliations.
CONCLUSIONS: Afghanistan is facing existential humanitarian threats. Developing the country's neurosurgical capacity and general health care capabilities is crucial. Emphasis on training physicians and establishing communication routes, and aid deliverance with the country and its leaders is key to overcoming the many crises it faces.
MATERIAL AND METHOD: Two hundred discs of PEEK were prepared of 6 mm × 2 mm × 10 mm dimension. The discs were randomly divided into five groups (n = 40) for treatment, Group I: treatment with deionized distilled water (control group); Group II: PD therapy using curcumin PS; Group III: discs treated and abraded with air-borne particles (ABP) silica (30 μm particle size) modified alumina (Al); Group IV: ABP of alumina (110 μm particle size); and Group V: The PEEK were finished with 600-μm grit size straight diamond cutting bur installed in high speed hand-piece. The surface profilometer was used to evaluate the values of surface roughness (SRa) of pretreated PEEK discs. The discs were luted and bonded to discs of composite resin. The bonded PEEK samples were placed in Universal testing machine to evaluate shear BS. The type of BS failure for PEEK discs pre-treated with five regimes respectively was evaluated under stereo-microscope. The data was statistically analyzed using one-way ANOVA and the comparisons between mean values of shear BS were evaluated by Tukey's test (ρ≤0.05).
RESULTS: The PEEK samples pre-treated with diamond cutting straight fissure burs displayed statistically significant highest value of SRa values (3.258± 0.785 µm). Similarly, the shear BS was observed to be higher for the PEEK discs pre-treated with straight fissure bur (22.37±0.78 MPa). A comparable difference but not statistically significant difference was observed between PEEK discs pre-treated by curcumin PS and ABP-silica modified alumina (ρ ≥ 0.05).
CONCLUSION: PEEK discs pre-treated with diamond grit straight fissure bur displayed highest values of SRa and shear BS. It was trailed by ABP-Al pre-treated discs; whereas the SRa and shear BS values for the discs pre-treated with ABP-silica modified Al and curcumin PS did not show competitive difference.