This paper presents a multitasking electrical impedance tomography (EIT) system designed to improve the flexibility and durability of an existing EIT system. The ability of the present EIT system to detect, locate, and reshape objects was evaluated by four different experiments. The results of the study show that the system can detect and locate an object with a diameter as small as 1.5 mm in a testing tank with a diameter of 134 mm. Moreover, the results demonstrate the ability of the current system to reconstruct an image of several dielectric object shapes. Based on the results of the experiments, the programmable EIT system can adapt the EIT system for different applications without the need to implement a new EIT system, which may help to save time and cost. The setup for all the experiments consisted of a testing tank with an attached 16-electrode array made of titanium alloy grade 2. The titanium alloy electrode was used to enhance EIT system's durability and lifespan.
This paper reviews the phase structures and oxidation kinetics of complex Ti-Al alloys at oxidation temperatures in the range of 600-1000 °C. The mass gain and parabolic rate constants of the alloys under isothermal exposure at 100 h (or equivalent to cyclic exposure for 300 cycles) is compared. Of the alloying elements investigated, Si appeared to be the most effective in improving the oxidation resistance of Ti-Al alloys at high temperatures. The effect of alloying elements on the mechanical properties of Ti-Al alloys is also discussed. Significant improvement of the mechanical properties of Ti-Al alloys by element additions has been observed through the formation of new phases, grain refinement, and solid solution strengthening.
The composite reinforcement technique has been used clinically to salvage damaged root-filled teeth compromised by caries, trauma, developmental abnormalities, internal resorption and iatrogenic causes. This clinical case report describes the use of the technique to reattach a fractured fragment in a compromised endodontically treated root besides reinforcing it for continued function in the mouth. Factors of clinical importance related to this additional application; including reattachment of tooth fragments, post crown retention, coronal microleakage and fracture resistance and strength, are also briefly discussed.
Matched MeSH terms: Metal Ceramic Alloys/chemistry
The present study was conducted to compare the cleaning efficacy (debris and smear layer removal) of hand and two NiTi rotary instrumentation systems (K3 and ProTaper).
In this research, due to the present pandemic of COVID-19, we are proposing a stable and fixed semitransparent photo-thermoelectric cell (PTEC) module for green energy harvesting. This module is based on the alloy of Bismuth Telluride Selenide (Bi2Te3Se), designed in a press tablet form and characterized under solar energy. Here, both aspects of solar energy i.e., light and heat are utilized for both energy production and water heating. The semitransparent PTEC converts heat energy directly to electrical energy due to the gradient of temperature between two electrodes (top and bottom) of thermoelectric cells. The PTEC is 25% transparent, which can be varied according to the necessity of the utilizer. The X-ray diffraction of material and electric characterization of module i.e., open-circuited voltage (VOC) and Seebeck coefficient were performed. The experimental observations disclose that in the proposed PTEC module with an increment in the average temperature (TAvg) from 34 to 60 °C, results in the rise of VOC ∼ 2.4 times. However, by modifying the size of heat-absorbing top electrode and by increasing the temperature gradient through the addition of water coolant under the bottom electrode, an uplift in the champion device results in as increment of VOC ∼5.5 times and Seebeck coefficient obtained was -250 μV/0C, respectively. Results show that not only the selection of material but also the external modifications in the device highly effective the power efficiency of the devices. The proposed modules can generate electric power from light and utilize the penetrating sunlight inside the room and for the heating of the water which also acts as a coolant. These semitransparent thermoelectric cells can be built-in within windows and roofs of buildings and can potentially contribute to green energy harvesting, in situations where movement is restricted locally or globally.
The current study is proposing a design envelope for porous Ti-6Al-4V alloy femoral stems to survive under fatigue loads. Numerical computational analysis of these stems with a body-centered-cube (BCC) structure is conducted in ABAQUS. Femoral stems without shell and with various outer dense shell thicknesses (0.5, 1.0, 1.5, and 2 mm) and inner cores (porosities of 90, 77, 63, 47, 30, and 18%) are analyzed. A design space (envelope) is derived by using stem stiffnesses close to that of the femur bone, maximum fatigue stresses of 0.3σys in the porous part, and endurance limits of the dense part of the stems. The Soderberg approach is successfully employed to compute the factor of safety Nf > 1.1. Fully porous stems without dense shells are concluded to fail under fatigue load. It is thus safe to use the porous stems with a shell thickness of 1.5 and 2 mm for all porosities (18-90%), 1 mm shell with 18 and 30% porosities, and 0.5 mm shell with 18% porosity. The reduction in stress shielding was achieved by 28%. Porous stems incorporated BCC structures with dense shells and beads were successfully printed.
A brief survey to assess the sensitivity and efficacy of some common etching reagents for revealing obliterated engraved marks on Al-Si alloy surfaces is presented. Experimental observations have recommended use of alternate swabbing of 10% NaOH and 10% HNO(3) on the obliterated surfaces for obtaining the desired results. The NaOH etchant responsible for bringing back the original marks resulted in the deposition of some dark coating that has masked the recovered marks. The coating had been well removed by dissolving it in HNO(3) containing 10-20% acid. However, the above etching procedure was not effective on aluminium (99% purity) and Al-Zn-Mg-Cu alloy surfaces. Also the two reagents (i) immersion in 10% aq. phosphoric acid and (ii) alternate swabbing of 60% HCl and 40% NaOH suggested earlier for high strength Al-Zn-Mg-Cu alloys [23] were quite ineffective on Al-Si alloys. Thus different aluminium alloys needed different etching treatments for successfully restoring the obliterated marks. Al-Si alloys used in casting find wide applications especially in the manufacture of engine blocks of motor vehicles. Hence, the results presented in this paper are of much relevance in serial number restoration problems involving this alloy.
A systematic study to assess the concentration of radionuclides in primary coolant and associated water samples from the operation of a TRIGA Mark II reactor has been carried out. The samples were transferred into appropriate counting container and were counted by efficiency-calibrated gamma spectrometer systems for several hours to obtain statistically adequate data for qualitative and quantitative evaluation of the radioactive materials presence. The primary coolant was found to contain various gamma emitting radionuclides including 24Na, 41Ar, 42K, 51Cr, , 54Mn, 56Mn, 60Co, 99mTc, 122Sb, 124Sb and 187W. Most of the detected radionuclides were inferred to be originated from activation products of (n,) nuclear reactions of elements of reactor components such as stainless steel and aluminium alloy used in the reactor system. The study confirms the integrity of the reactor system with no apparent release of any fission products radionuclide into the coolant water system.
This review briefly describes some of the techniques available for analysing surfaces and illustrates their usefulness with a few examples such as a metal and alloy. In particular, Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS) and laser Raman spectroscopy are all described as advanced surface analytical techniques. In analysing a surface, AES and XPS would normally be considered first, with AES being applied where high spatial resolution is required and XPS where chemical state information is needed. Laser Raman spectroscopy is useful for determining molecular bonding. A combination of XPS, AES and Laser Raman spectroscopy can give quantitative analysis from the top few atomic layers with a lateral spatial resolution of
This study aimed to investigate the effects of element diffusion on the alloying behaviour and microstructure of a Ti-10%Mo10%Cr
alloy during sintering and furnace cooling. A theoretical calculation of the average diffusion distance for each
element was performed to predict the alloying behaviour during sintering and furnace cooling. The Ti-10%Mo-10%Cr
alloy was fabricated using a blended element powder metallurgy approach. Micrograph of the samples after sintering
showed bright-circle structures and significantly decreased equiaxed structures. The number of plate-like structures
increased with prolonged sintering time. Microstructural changes occurred because of element diffusion resulting from
the prolonged sintering time. Moreover, the diffusion distance of each element also increased with prolonged sintering
time. Although elements can sufficiently diffuse during both sintering and furnace cooling, the diffusion distance during
sintering was considerably higher than that during furnace cooling for all elements. The diffusion distances of Cr and
Mo were the highest and lowest, respectively, during sintering and furnace cooling. This study showed that alloying
behaviour mostly occurred during sintering and was controlled by the diffusion of Mo atoms.
Resistance spot welding (RSW) is one of the most effective welding methods for titanium alloys, in particular Ti-6Al-4V. Ti-6Al-4V is one of the most used materials with its good ductility, high strength, weldability, corrosion resistance, and heat resistance. RSW and Ti-6Al-4V materials are often widely used in industrial manufacturing, particularly in automotive and aerospace industries. To understand the phenomenon of resistance spot weld quality, the physical and mechanical properties of Ti-6Al-4V spot weld are essential to be analyzed. In this study, an experiment was conducted using the Taguchi L9 method to find out the optimum level of the weld joint strength. The given optimum level sample was analyzed to study the most significant affecting RSW parameter, the failure mode, the weld nugget microstructure, and hardness values. The high heat input significantly affect the weld nugget temperature to reach and beyond the β-transus temperature. It led to an increase in the weld nugget diameter and the indentation depth. The expulsion appeared in the high heat input and decreased the weld nugget strength. It was caused by the molten material ejection in the fusion zone. The combination of high heat input and rapid air cooling at room temperature generated a martensite microstructure in the fusion zone. It increased the hardness, strength, and brittleness but decreased the ductility.
The enhancement of microwave absorbing properties in nickel zinc ferrite (Ni0.5Zn0.5Fe2O4) via multiwall carbon nanotubes (MWCNT) growth is studied in this research work. Ni0.5Zn0.5Fe2O4 was initially synthesized by mechanical alloying followed by sintering at 1200 °C and the microstructural, electromagnetic and microwave characteristics have been scrutinized thoroughly. The sintered powder was then used as a catalyst to grow MWCNT derived from chemical vapor deposition (CVD) method. The sample was mixed with epoxy resin and a hardener for preparation of composites. The composite of multi-walled carbon nanotubes/Ni0.5Zn0.5Fe2O4 shown a maximum reflection loss (RL) of -19.34 dB at the frequency and bandwidth of 8.46 GHz and 1.24 GHz for an absorber thickness of 3 mm for losses less than -10 dB. This acquired result indicates that multi-walled carbon nanotubes/Ni0.5Zn0.5Fe2O4 could be used as a microwave absorber application in X-band.
The importance of protein detection system for protein functions analyses in recent post-genomic era is rising with the emergence of label-free protein detection methods. We are focusing on a simple and practical label-free optical-detection method called anomalous reflection (AR) of gold. When a molecular layer forms on the gold surface, significant reduction in reflectivity can be observed at wavelengths of 400-500 nm. This allows the detection of molecular interactions by monitoring changes in reflectivity. In this chapter, we describe the AR method with three different application platforms: (1) gold, (2) gold containing alloy/composite (AuAg2O), and (3) metal-insulator-metal (MIM) thin layers. The AuAg2O composite and MIM are implemented as important concepts for signal enhancement process for the AR technique. Moreover, the observed molecular adsorption and activity is aided by a three-dimensional surface geometry, performed using poly(amidoamine) or PAMAM dendrimer modification. The described system is suitable to be used as a platform for high-throughput detection system in a chip format.
The aim of this study was to evaluate in vitro the apical sealing ability of cold lateral and system B root filling techniques using dye penetration. Eighty-six extracted single-rooted human teeth were prepared and randomly divided into two experimental groups to be obturated by cold lateral condensation (n = 33) and system B (n = 33). The remaining 20 teeth served as positive and negative controls. The roots were embedded for 72 h in methylene blue dye solution and sectioned transversely for dye penetration evaluation using stereomicroscope. The results of this study showed that cold lateral condensation leaked significantly more (P < 0.001) than system B technique.
In the recent years, electronic packaging provides significant research and development challenges
across multiple disciplines such as performance, materials, reliability, thermals and interconnections.
New technologies and techniques frequently adopted can be implemented in soldering alloys of
semiconductor sectors in terms of optimisation. Wetting contact angle or wettability of solder alloys
is one of the important factors which has got the attention of scholars. Hence in this study, due to the
remarkable similarity over classical solder alloys (Pb-Sn), Bi-Ag solder was investigated. Data were
collected through the effects of aging time variation and different weight percentages of Ag in solder
alloys. The contact angle of the alloys with Cu plate was measured by optical microscopy. Artificial
neural networks (ANNs) were applied on the measured datasets to develop a numerical model for further
simulation. Results of the experiments and simulations showed that the coefficient of determination (R2
)
is around 0.97, which signifies that the ANN set up is appropriate for the evaluation.
The search for a high temperature lead-free solder replacement for high temperature leaded solder eutectic alloy has been an evolving process as the threat of a regional lead ban became a reality in July 2006. The advantages and disadvantages of lead-free solder in terms of manufacturing, performance and reliability have been increasingly revealed through companies’ Research and Development (R&D), industrial consortia and university researchers. Materials and component design are the primary criteria to focus on the development for the current generation of high temperature lead-free solder alloys. According to the current status of high temperature lead free soldering, there are many unsolved technical problems such as explanation on the lift-off phenomenon, establishment of high temperature lead-free plating technology, construction of a database of physical properties (solder, parts, PCBs), standardization of high temperature solder materials evaluation technology, and most importantly, the best candidate material for high temperature solder. Clearly, high temperature soldering is one of the unsolved problems of the century in lead-free soldering. Moreover, most of the questions still remain unanswered by researchers. This paper reviews research conducted on the Bi-Ag solder alloy, which is one of the candidate alloys that has been proposed as an alternative for high temperature lead-free solder.
A feasible production of poly (methyl methacrylate)@alloy (gold-silver) core shell has
been presented as candidate in enhanced detection of surface enhanced Raman scattering
(SERS). Free emulsifier- emulsion synthesised PMMA sphere with average size of 419 nm in
diameter were used as core material for incorporation of alloy nanoparticles (6 nm) resulting
a core-shell structure. The fabrication of PMMA@alloy SERS substrate was successfully
done via self-assembly thus the produced SERS substrate that comprise of unique optical
properties combination arising from periodic core arrangement and plasmonic activity of
alloy nanoparticles. Alloy is bimetallic nanoparticles in which the combination of silver
(Ag) and gold (Au) present an absolutely improved light resistance as compared to single
metal alone with great surface plasmon resonance. Morphology and elemental analysis was
performed through scanning electron microscope (SEM) and the analysis showing species of
both Au and Ag in single alloy nanoparticles. The alloy nanoparticles were also observed to
homogenously coating the PMMA sphere. Surface plasmon resonance activity was maximum
at 476 nm obtained from UV-Visible spectroscopy. High surface production was observed
to have periodically arranged PMMA@alloy core -shell and potentially to be used as SERS
substrate.
This study was aimed to improve of the corrosion resistance and mechanical properties of Mg/15TiO2/5HA nanocomposite by silicon and magnesium oxide coatings prepared using a powder metallurgy method. The phase evolution, chemical composition, microstructure and mechanical properties of uncoated and coated samples were characterized. Electrochemical and immersion tests used to investigate the in vitro corrosion behavior of the fabricated samples. The adhesion strength of ~36MPa for MgO and ~32MPa for Si/MgO coatings to substrate was measured by adhesion test. Fabrication a homogenous double layer coating with uniform thicknesses consisting micro-sized particles of Si as outer layer and flake-like particles of MgO as the inner layer on the surface of Mg/15TiO2/5HA nanocomposite caused the corrosion resistance and ductility increased whereas the ultimate compressive stress decreased. However, after immersion in SBF solution, Si/MgO-coated sample indicates the best mechanical properties compared to those of the uncoated and MgO-coated samples. The increase of cell viability percentage of the normal human osteoblast (NHOst) cells indicates the improvement in biocompatibility of Mg/15TiO2/5HA nanocomposite by Si/MgO coating.
This research has been accomplished using the advanced selective laser melting (SLM) technique as well as HIP post-treatment in order to improve mechanical properties and biocompatibility of Mg- Ca-Sr alloy. Through this research it becomes clearly noticeable that the Mg-1.5Ca-xSr (x = 0.6, 2.1, 2.5) alloys with Sr exhibited better mechanical properties and corrosion potentials. This is more particular with the Mg-1.5Ca-2.5Sr alloy after HIP post-treatment allowing it to provide a desired combination of degradation and mechanical behavior for orthopedic fracture fixation during a desired treatment period. In vivo trials, there was a clear indication and exhibition that this Mg-1.5Ca-2.5Sr alloy screw can completely dissolve in miniature pig's body which leads to an acceleration in growth of bone tissues. Mg-Ca-Sr alloy proved potential candidate for use in orthopedic fixation devices through Our results concluded that Mg-Ca-Sr alloy are potential candidate for use in orthopedic fixation devices through mechanical strength and biocompatibility evaluations (in vitro or In vivo).