METHODS: Six master dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Thirty copings (Procera AllCeram) of 0.6-mm thickness were manufactured. Three types of luting media were used: zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and dual-cured composite resin cement (Panavia F). Ten copings were cemented with each type. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.
RESULTS: ANOVA revealed significant differences in the load at fracture among the three groups (p < 0.001). The fracture strength results showed that the mean fracture strength of zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and resin luting cement (Panavia F) were 1091.9 N, 784.8 N, and 1953.5 N, respectively.
CONCLUSION: Different luting agents have an influence on the fracture resistance of Procera AllCeram copings.
MATERIALS AND METHODS: Sound extracted human molars were randomly divided into: manufacturer's instructions (MI), manual blend 2 mm (MB2), and manual blend 4 mm (MB4). Occlusal enamel was removed and flattened, dentin surfaces were bonded by Prime & Bond universal (Dentsply and Optibond FL, Kerr). For the MI group, adhesives were applied following the manufacturer's instructions then light-cured. For MB groups, SDR flow+ bulk-fill flowable composite resin was applied in 2- or 4-mm increment then manually rubbed by a micro brush for 15 s with uncured dentine bonding agents and the mixture was light-cured. Composite buildup was fabricated incrementally using Ceram.X One, Dentsply nanohybrid composite resin restorative material. After 24-h water storage, the teeth were sectioned to obtain beams of about 0.8 mm2 for 24-h and thermocycled micro-tensile bond strength at 0.5 mm/min crosshead speed. Degree of conversion was evaluated with micro-Raman spectroscopy. Contraction gaps at 24 h after polymerization were evaluated and atomic force microscopy (AFM) nano-indentation processes were undertaken for measuring the hardness across the interface. Depth of resin penetration was studied using a scanning electron microscope (SEM). Bond strength data was expressed using two-way ANOVA followed by Tukey's test. Nanoindentation hardness was separately analyzed using one-way ANOVA.
RESULTS: Factors "storage F = 6.3" and "application F = 30.11" significantly affected the bond strength to dentine. For Optibond FL, no significant difference in nanoleakage was found in MI/MB4 groups between baseline and aged specimens; significant difference in nanoleakage score was observed in MB2 groups. Confocal microscopy analysis showed MB2 Optibond FL and Prime & Bond universal specimens diffusing within the dentine. Contraction gap was significantly reduced in MB2 specimens in both adhesive systems. Degree of conversion (DC) of the MB2 specimens were numerically more compared to MS1 in both adhesive systems.
CONCLUSION: Present study suggests that the new co-blend technique might have a positive effect on bond strengths of etch-and-rinse adhesives to dentine.
METHODS: 75 human mandibular molars were randomly divided into five equal groups. Teeth were standardized, endodontically-treated and restored according the assigned group as follows: amalgam core only, prefabricated titanium post in the distal canal and amalgam core, composite core only; fiber post in the distal canal and composite core. One group of untreated sound teeth was used as a control. Non-precious metal crowns were fabricated and cemented on the prepared specimens with Rely X U200 resin cement. All specimens were subjected to a compressive load at crosshead speed 0.5 mm/minute, 25° to the long axis of the tooth. Failure loads and modes were recorded.
RESULTS: Mean failure loads among the groups were significantly different (P= 0.035). Post-hoc multiple pair-wise comparisons revealed the amalgam core and composite core groups produced significantly lower fracture resistance than the control group (P= 0.041 and P= 0.025, respectively) and no significant differences among the different intra-radicular techniques (P> 0.05). The composite core with fiber post and amalgam core with titanium posts showed the highest percentage of favorable failures (67%) and non-favorable failures (87%) respectively.
CLINICAL SIGNIFICANCE: The composite core with fiber post is the most appropriate intraradicular restoration in cases of severely compromised molars.
Materials and Methods: In this in-vitro study, a total of 48 single-rooted permanent human teeth were decoronated, and the roots were treated endodontically. Following post space preparation, the sample was divided into four groups (n= 12 each) based on the types of post and cement. Two different types of post [GC everStick®POST (ES) and Parapost® Fiber LuxTM (PF)], and two different types of cement [G-CEMTM (G), and RelyXTM Unicem (R)] were used according to the manufacturer's instructions. All roots were sectioned at the coronal and middle thirds with a thickness of 3±0.1mm. The Push-out bond strength (PBS) test was performed using a universal testing machine at a cross-head speed of 0.5mm/ min. The bond strength values were recorded, and the data were analyzed using the SPSS program. Apart from descriptive statistics, three-way ANOVA was used for the interaction of the independent variables (post, cement, and root level). For differences between the groups, the Mann-Whitney U test was used. A P-value of less than 0.05 was considered significant for all analyses.
Results: Push-out bond strength of samples at the middle level (11.38±10.31 MPa), with PF posts (11.18±9.98 MPa), and of those luted with RelyXTM Unicem cement (13.26±8.73 MPa) was higher than that of their counterparts. The PBS means of RelyXTM Unicem cement at both root levels were much higher than PBS means of G-CEMTM cement. Three-way ANOVA test revealed a significant effect for each variable with a higher effect of cement (Sum of Squares= 1310.690; P< 0.001). No significant difference (P= 0.153) was found between the coronal and middle parts and between ES and PF posts (P= 0.058). However, a highly significant difference (P< 0.001) was found between RelyXTM Unicem and G-CEMTM cements.
Conclusion: The type of cement had a significant effect on push-out bond strength with RelyXTM Unicem which had higher values than G-CEMTM. However, the type of post and root level had no significant effect on PBS, although Parapost® Fiber LuxTM and middle root level had higher values than their counterparts.