The Burstein-Moss shift and band gap narrowing of sputtered indium-doped zinc oxide (IZO) thin films are investigated as a function of carrier concentrations. The optical band gap shifts below the carrier concentration of 5.61 × 1019 cm-3 are well-described by the Burstein-Moss model. For carrier concentrations higher than 8.71 × 1019 cm-3 the shift decreases, indicating that band gap narrowing mechanisms are increasingly significant and are competing with the Burstein-Moss effect. The incorporation of In causes the resistivity to decrease three orders of magnitude. As the mean-free path of carriers is less than the crystallite size, the resistivity is probably affected by ionized impurities as well as defect scattering mechanisms, but not grain boundary scattering. The c lattice constant as well as film stress is observed to increase in stages with increasing carrier concentration. The asymmetric XPS Zn 2p3/2 peak in the film with the highest carrier concentration of 7.02 × 1020 cm-3 suggests the presence of stacking defects in the ZnO lattice. The Raman peak at 274 cm-1 is attributed to lattice defects introduced by In dopants.
The effects of scanning rates (1, 5, 10 and 20 degrees C/min) on the DSC cooling profiles of 11 vegetable oils have been determined in order to monitor peak transition temperatures, onset temperatures and crystallisation enthalpies. Triacylglycerol (TAG) profiles and iodine value analyses were used to complement the DSC data. The melted samples exhibited complicated crystallising exotherms. As the cooling rate increased, the crystallisation temperature decreased and the breadth of the crystallisation exotherm on cooling from the melt increased. In addition, the intensity of the exothermic peak increased somewhat when the cooling rate was increased. At slow cooling rates, TAG had more time to interact. It is conceivable that, at a low cooling rate (1 degree C/min), a prominent exotherm would be observed on crystallisation of vegetable oils and fats. The occurrence of one exotherm upon cooling indicated the co-crystallisation of the TAG upon slow cooling. On the basis of the corollary results obtained, vegetable oils may be differentiated by their onset temperature (Ton) values in the DSC cooling curves. Generally, there was a shift of Ton toward lower values with increasing cooling rates.
Nitrogen-infused wet oxidation at different temperatures (400-1000 °C) was employed to transform tantalum-hafnia to hafnium-doped tantalum oxide films. High-temperature wet oxidation at 1000 °C marked an onset of crystallization occurring in the film, accompanied with the formation of an interfacial oxide due to a reaction between the inward-diffusing hydroxide ions, which were dissociated from the water molecules during wet oxidation. The existence of nitrogen has assisted in controlling the interfacial oxide formation. However, high-temperature oxidation caused a tendency for the nitrogen to desorb and form N-H complex after reacting with the hydroxide ions. Besides, the presence of N-H complex implied a decrease in the passivation at the oxide-Si interface by hydrogen. As a consequence, defect formation would happen at the interface and influence the metal-oxide-semiconductor characteristics of the samples. In comparison, tantalum-hafnia subjected to nitrogen-infused wet oxidation at 600 °C has obtained the highest dielectric constant, the largest band gap, and the lowest slow trap density.
Interesterification reaction involves rearrangement of the fatty acid radicals on the glycerol backbone, either randomly (chemical interesterification) or regioselectivity (enzymatic interesterification). Refined, bleached and deodourised palm oil (RBDPO) and palm kernel oil (RBDPKO) were blended in ratios from 25:75 to 75:25 (wt/wt). All blends were subjected to enzymatic (EI) and chemical interesterification (CI) using Lipozyme TL IM (4% w/w) and sodium methoxide (0.2% m/m) as the catalysts, respectively. The effect of EI and CI on the triacylglycerol (TAG) composition, thermal behaviour, polymorphism, crystal morphology and crystallisation kinetics were studied. The aim of this research is to characterise the nature of crystals in food product for certain desired structure. The crystallisation behaviour discussed in this study involves microstructure (PLM), polymorphism (XRD), thermal properties and crystallisation kinetics by DSC. The alteration in TAG composition was greater after CI as compared to EI with the reduction of LaLaLa (from 11.00% to 5.15%) and POO (from 14.28% to 4.87%). The DSC complete melting and crystallisation temperature of blend with 75% PO increased after CI, from 39.58 °C to 41.67 °C and from -30.84 °C to -28.33 °C, respectively. EI contributed to finer crystals than CI. However, the β' and β polymorph mixture and crystallisation kinetics (n = 2) of PO-PKO blends did not change after CI and EI. The knowledge on controlling crystallisation of RBDPO and RBDPKO blends is vital for proper processing condition like margarine production.
Fission tracks are linear trails of intense radiation damage in the crystal structure of a mineral, produced by spontaneous fissioning of uranium-238 (238U) atoms. Detail information on the low-temperature thermal histories of rocks, below∼120 °C for tracks in apatite and below∼350 °C for zircon, can be provided by Fission-track (FT) analysis. The purpose of this article is to present apatite and zircon fission-track data, and U-Pb granite ages that provide information about the cooling histories of a rock which can be crucial in comprehending the exhumation episodes of the study area, in particular, and the region, in general. Granite samples were collected along the same vertical profile at different elevation, 178-944 m.a.s.l. These samples were used to determine Fission-Track and crystallization ages. HeFTy software was employed to interpret the cooling histories of the samples using forward and inverse models. The inverse model was an approach of reproducing the observed data, and it was carried out only for fission-track data from the apatite grains. And it was constructed after generating a number of forward models, where in each of these models the predicted apatite fission-track parameters were compared to the measured values. The apatite fission track (AFT) and zircon fission track (ZFT) data indicated expected age trends, i.e. the older ages at higher elevations and the younger ages at lower elevations. Similarly, the data shows that the apatite and zircon FT ages appear younger than the age of the rock crystallization. The U-Pb age in zircon consistently suggest the age of the granite is Late Triassic.
A combinative effect of two or more individual material properties, such as lattice parameters and chemical properties, has been well-known to generate novel nanomaterials with special crystal growth behavior and physico-chemical performance. This paper reports unusually high catalytic performance of AgPt nanoferns in the hydrogenation reaction of acetone conversion to isopropanol, which is several orders higher compared to the performance shown by pristine Pt nanocatalysts or other metals and metal-metal oxide hybrid catalyst systems. It has been demonstrated that the combinative effect during the bimetallisation of Ag and Pt produced nanostructures with a highly anisotropic morphology, i.e., hierarchical nanofern structures, which provide high-density active sites on the catalyst surface for an efficient catalytic reaction. The extent of the effect of structural growth on the catalytic performance of hierarchical AgPt nanoferns is discussed.
Methyl ester sulphonates (MES) have been considered as an alternative green surfactant for the detergent market. Investigation on the purification of methyl ester sulphonates (MES) with various carbon chains of C12, C14, C16 and C16-18 derived from palm methyl ester is of great interest. These MES powders have been repeatedly crystallized with ethanol and the purity of MES has increased to a maximum of 99% active content and 96% crystallinity index without changing the structure. These crystallized MES with high active content have 1.0% to 2.3% moisture content and retained its di-salt content in the range of 5%. The crystallized MES C16 and C16-18 attained excellent flow characteristics. Morphology, structural and its crystallinity analyses showed that the crystals MES had good solubility properties, stable crystal structure (β polymorphic) and triclinic lateral structure when it is in high active content. The brittleness of MES crystals increased from a β' to a β subcell. Crystal with high brittleness has the potential to ease production of powder, which leads to a reduction in the cost of production and improves efficiency.
Offretite zeolite synthesis in the presence of cetyltrimethylammonium bromide (CTABr) is reported. The offretite crystals were synthesized with a high crystallinity and hexagonal prismatic shape after only 72 h of hydrothermal treatment at 180 °C. The CTABr has dual-functions during the crystallization of offretite, viz. as structure-directing agent and as mesoporogen. The resulting offretite crystals, with a Si/Al ratio of 4.1, possess more acid sites than the conventional offretite due to their high crystallinity and hierarchical structure. The synthesized offretite is also more reactive than its conventional counterpart in the acylation of 2-methylfuran for biofuel production under non-microwave instant heating condition, giving 83.5% conversion with 100% selectivity to the desired product 2-acetyl-5-methylfuran. Hence, this amphiphile synthesis approach offers another cost-effective and alternative route for crystallizing zeolite materials that require expensive organic templates.
Phytosterols (PSs) are insoluble in water and poorly soluble in oil, which hampers their potential as cholesterol level regulator in human. To mitigate this problem, monoglycerides (MGs) were used to modulates the crystallization behavior of PSs. Therefore, the understanding on mixing behavior provides the insight into different aspects of crystallization and the resultant effects. The effects on thermal, morphology, diffraction, and spectroscopy behavior were investigated for binary mixtures of 11 different ratios (100:0 to 0:100 MGs:PSs). The phase behavior of binary mixtures of commercial MGs and PSs exhibited complexity with the formation of eutectic mixtures at 90:10 and 80:20 (MGs:PSs) combinations. These combinations revealed a single melting profile and reduced melting enthalpy, though after a month of storage at 5 °C. Conversely, two separate melting regions were observed in others. Furthermore, powder X-ray diffraction (PXRD) analysis of selected combinations revealed a change in crystalline forms with changes in the peaks located between 18-19° (2θ) and 25-26° (2θ). Accordingly, Raman spectroscopy results revealed changes in intensities and peak shape. Therefore, the change in crystalline forms or behavior correlated well to the change in thermal properties. Overall, the characterizations revealed the formation of eutectic mixtures between MGs and PSs at 90:10 and 80:20 (MGs:PSs) in which MGs modified the crystallization of PSs and changed the crystal forms thus, thermal behaviors. This study provides new insight into the mixing behavior of MGs and PSs which supports other research. Therefore, the results of this study are beneficial for the improvement of formulation of phytosterols in food and pharmaceutical products. Nonetheless, this study reveals a simple technique to alter crystal forms of phytosterols through simple complexation with monoglycerides.
This paper clarified the microstructural element distribution and electrical conductivity changes of kaolin, fly ash, and slag geopolymer at 900 °C. The surface microstructure analysis showed the development in surface densification within the geopolymer when in contact with sintering temperature. It was found that the electrical conductivity was majorly influenced by the existence of the crystalline phase within the geopolymer sample. The highest electrical conductivity (8.3 × 10-4 Ωm-1) was delivered by slag geopolymer due to the crystalline mineral of gehlenite (3Ca2Al2SiO7). Using synchrotron radiation X-ray fluorescence, the high concentration Ca boundaries revealed the appearance of gehlenite crystallisation, which was believed to contribute to development of denser microstructure and electrical conductivity.
Powdered-photocatalysis of organic wastewater is widely investigated, unfortunately not industrially implemented due to its high energy requirement. Interestingly, such issue may be alleviated via the elimination of mechanical stirring required. Core-shell ZnO-based photocatalysts were developed herein, subsequently demonstrated efficient photocatalytic activities in the absence of mechanical stirring. Results show that the developed SiO2-cored ZnO photocatalyst are highly crystalline, while significantly smaller than coreless, pure ZnO due to the multi-point crystallization prompted. Additionally, it is also inherited with considerable buoyancy ability from SiO2-core in the absence of mechanical stirring, concurrently rendered with UV-active properties due to its ZnO-shell. Experimentally, 55% of particles of ZnO_0.0025 (0.0025 mol of ZnO-deposition) were found stably suspended for 60 min in liquid substrate, as opposed to the instant-settling of pure ZnO particles. In term of photocatalytic activity, ZnO_0.01 manifested the best methylene blue (MB) degradation with 150 mL/min of O2-bubbling. 67.63% of MB was degraded with photocatalyst loading of 0.2 g/L after 120 min UV-irradiation, simultaneously recorded the highest pseudo-first order reaction constant of 9.636 × 10-3 min-1. As summary, the auto-suspending photocatalysis conceptualized in current study offers a high possibility in reducing energy requirement for photo-treatment of wastewater, hence advocating its industrialization potential in near future.
Fly ash (PFA) is a complex material produced after combustion in coal-fired power plants. About half of this fly ash is disposed as solid wastes. A possible alternative to disposal of the fly ash is the synthesis of zeolite. Zeolite Boggsite (Na37Ca74Al185Si775O192 7H2O) was synthesized from fly ash by hydrothermal treatment with NaOH solutions as identified by x-ray diffraction. The zeolite type and degree of crystallization were found to be dependent on the reaction conditions and mineralogy of the raw material, particularly in terms of the relative concentrations of SiO2 and Al2O3.
The present investigation deals with the development of ethanol-vapour-sensing materials coated with the semiconducting oxide TiO2. Thick films of anatase TiO2 were deposited using the sol-gel dip-coating technique on alumina substrates by conventional alkoxide sol and modified sol added with Degussa P-25 as the sensing medium. It was shown that crystallised TiO2 anatase was obtained at the annealing temperature of 500oC. The fabricated TiO2 sensors exhibited highest sensitivity at the sensing temperature of 350 ºC. Sensitivity towards the ethanol vapour was further increased with UV light effect. The enhancement of the sensitivity of the modified catalytic pellet can be explained by the crystallite of anatase TiO2 and the effect of the photocatalytic of TiO2. The high sensitivity of the TiO2 film deposited with modified sol revealed that the modified sol could be a new alternative in the development of a TiO2 ethanol sensor.
Mechanical properties of blended polyethylene (PE) containing the antioxidant Irganox 1010 and the UV-absorber Tinuvin 326 were studied for future use as radiation capsule material for the TRIGA Mark II research reactor. High density and low density polyethylene were blended with the additives and tested for elongation at break, impact strength and gel content, before and after irradiation inside the nuclear reactor. Characterization via FTIR as well as determination of crystallization and melt transition temperatures through DSC were also conducted. It was found that the addition of the antioxidant at different amounts (from 0 to 4 phr) had various effects on the properties of the blended PE, with 0 phr being the amount at which there was the biggest increase in elongation at break and impact strength, post-irradiation.
We put attention on Intrinsic Josephson Junction (IJJ) to study the fundamental physic for device applications. Convenient self-flux method was used to grow BSCCO single crystals. We investigated the lid effect to examine the single crystal growth of high TC (Critical Temperature). We found that for the crystal growth with no lid, two stage transitions of TC ≅ 61 K and 77 K were observed. While for the crystal growth with lid, the BSCCO has TC ≅ 80K, ΔTC = 10K and approximately average size5x2mm 2 . When we increased weight of lid, the single crystal have increased to TC =80K, ΔTC = 4K and the typical size was ≅7x3mm 2 . TC and the crystal growth show a tendency to increase by the effect of the lid. From observed quasi-particle characteristics, c-axis direction changed from semiconductor to intrinsic Josephson characteristic with decreasing temperature.
Glass-ceramics are a group of materials that takes advantage of the various glass-forming methods before they are subsequently heat-treated in a controlled manner to effect nucleation and crystallization to produce crystalline materials. The production of glassceramic materials is to overcome the low mechanical strength in pure glassy materials. In this work, a study on the crystallisation of a soda-lime-silica glass was undertaken to ascertain how the processing parameters affect the crystallization of such glasses, viz. either via a single or two-step heat-treatment procedure, as well as the effect of soaking duration at the heat-treatment temperature. A soda-lime-silica glass system was chosen because the raw materials for producing such glasses are readily available and can be considered to be the cheapest. The glass produced was examined by thermal analysis to determine the nucleation and crystallization temperatures before they were heat-treated using a single-step and a two-stage heat-treatment procedures. The resultant glassceramics produced were characterized using x-ray diffraction as well as by scanning electron microscopy. The results thus obtained showed that a two-stage heat-treatment procedure is more successful in producing a well-crystallized glass-ceramic product.
Cs2Pb(MoO4)2crystals were prepared by crystallization from their own melt, and the crystal structure has been studied in detail. At 296 K, the molybdate crystallizes in the low-temperature α-form and has a monoclinic palmierite-related superstructure (space group C2/m, a = 2.13755(13) nm, b = 1.23123(8) nm, c = 1.68024(10) nm, β = 115.037(2)°, Z = 16) possessing the largest unit cell volume, 4.0066(4) nm3, among lead-containing palmierites. The compound undergoes a distortive phase transition at 635 K and incongruently melts at 943 K. The electronic structure of α-Cs2Pb(MoO4)2was explored by using X-ray emission spectroscopy (XES) and X-ray photoelectron spectroscopy methods. For α-Cs2Pb(MoO4)2, the photoelectron core-level and valence-band spectra and the XES band representing the energy distribution of Mo 4d and O 2p states were recorded. Our results allow one to conclude that the Mo 4d and O 2p states contribute mainly to the central part and at the top of the valence band, respectively, with also significant contributions throughout the whole valence-band region of the molybdate under consideration.
GDSL esterase J15 (EstJ15) is a member of Family II of lipolytic enzyme. The enzyme was further classified in subgroup SGNH hydrolase due to the presence of highly conserve motif, Ser-Gly-Asn-His in four conserved blocks I, II, III, and V, respectively. X-ray quality crystal of EstJ15 was obtained from optimized formulation containing 0.10 M ammonium sulphate, 0.15 M sodium cacodylate trihydrate pH 6.5, and 20% PEG 8000. The crystal structure of EstJ15 was solved at 1.38 Å with one molecule per asymmetric unit. The structure exhibits α/β hydrolase fold and shared low amino acid sequence identity of 23% with the passenger domain of the autotransporter EstA of Pseudomonas aeruginosa. The active site is located at the centre of the structure, formed a narrow tunnel that hinder long substrates to be catalysed which was proven by the protein-ligand docking analysis. This study facilitates the understanding of high substrate specificity of EstJ15 and provide insights on its catalytic mechanism.
In this research work, graphene nanoplatelets (GNP) were selected as alternative reinforcing nanofillers to enhance the properties of polypropylene (PP) using different compatibilizers called polypropylene grafted maleic anhydride (PP-g-MA) and ethylene-octene elastomer grafted maleic anhydride (POE-g-MA). A twin screw extruder was used to compound PP, GNP, and either the PP-g-MA or POE-g-MA compatibilizer. The effect of GNP loading on mechanical and thermal properties of neat PP was investigated. Furthermore, the influence and performance of different compatibilizers on the final properties, such as mechanical and thermal, were discussed and reported. Tensile, flexural, impact, melting temperature, crystallization temperature, and thermal stability were evaluated by using a universal testing system, differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). For mechanical properties, it was found that increasing GNP content from 1 wt.% to 5 wt.% increased tensile strength of the neat PP up to 4 MPa. The influence of compatibilizers on the mechanical properties had been discussed and reported. For instance, the addition of PP-g-MA compatibilizer improved tensile strength of neat PP with GNP loading. However, the addition of compatibilizer POE-g-MA slightly decreased the tensile strength of neat PP. A similar trend of behavior was observed for flexural strength. For thermal properties, it was found that both GNP loading and compatibilizers have no significant influence on both crystallization and melting temperature of neat PP. For thermal stability, however, it was found that increasing the GNP loading had a significant influence on improving the thermal behavior of neat PP. Furthermore, the addition of compatibilizers into the PP/GNP nanocomposite had slightly improved the thermal stability of neat PP.
Polylactic acid (PLA)/Epoxidized natural rubber (ENR-50) blends were prepared by melt extrusion followed by injection
molding to fabricate the test samples. The effect of ENR-50 loadings on the morphological, mechanical, chemical
resistance and water absorption properties of the blends were studied using standard methods. The toughness of the
blend improved with ENR loading up to 20 wt. % but flexural and tensile strength decreased. The balanced mechanical
properties were obtained at 20 wt. % ENR-50 loading. SEM showed good distribution and increased ENR particle size
as ENR content increased from 10 to 30 wt. %. The differential scanning calorimeter (DSC) showed a steady drop in
crystallization temperature (Tc
) as ENR content increases while the glass transition temperature (Tg
) remained unchanged.
Water absorption was observed to increase with ENR loadings. Increase in ENR content was also observed to reduce the
chemical resistance of the blends.