The valorization of lignin to replace phenol is significant in the production of phenolic resins. However, a great challenge is to produce lignin-based resin (LR) with a suitable viscosity and high substitution rate of lignin to phenol. In this study, LRs were produced using hardwood technical lignin derived from the pulping industry. Structural analysis of the LRs indicated that the unsubstituted para and ortho carbon atoms of the aromatic ring influenced the curing temperature and activation energy of the resins. The curing kinetics and thermal decomposition study implied that urea and methylene groups in cured LRs were significant factors that affected the thermal stability negatively. The prepared LRs showed desirable features if used as adhesives to make plywood. This is the first approach in which a substitution rate of up to 65 % is achieved for low-reactive-site hardwood lignin, which provides a solution to the challenge of the simultaneous realization of the high addition of lignin and the adaptive viscosity of resins.
Nanocellulose was extracted from short bast fibers, from hemp (Cannabis sativa L.) plants harvested at seed maturity, non-retted, and mechanically decorticated in a defibering apparatus, giving non-aligned fibers. A chemical pretreatment with NaOH and HCl allowed the removal of most of the non-cellulosic components of the fibers. No bleaching was performed. The chemically pretreated fibers were then refined in a beater and treated with a cellulase enzyme, followed by mechanical defibrillation in an ultrafine friction grinder. The fibers were characterized by microscopy, infrared spectroscopy, thermogravimetric analysis and X-ray diffraction after each step of the process to understand the evolution of their morphology and composition. The obtained nanocellulose suspension was composed of short nanofibrils with widths of 5-12 nm, stacks of nanofibrils with widths of 20-200 nm, and some larger fibers. The crystallinity index was found to increase from 74% for the raw fibers to 80% for the nanocellulose. The nanocellulose retained a yellowish color, indicating the presence of some residual lignin. The properties of the nanopaper prepared with the hemp nanocellulose were similar to those of nanopapers prepared with wood pulp-derived rod-like nanofibrils.
Thermally assisted hydrolysis and methylation-gas chromatography (THM-GC) in the presence of an organic alkali was validated for the compositional analysis of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(3HB-co-3HHx)] accumulated in whole bacterial cells. Recombinant Cupriavidus necator Re2058/pCB113 was grown in a batch fermentation with different concentration of palm oil and fructose in order to control the molar fraction of 3HHx in P(3HB-co-3HHx) produced in the cells. Trace amounts (30μg) of freeze-dried cells were directly subjected to THM-GC in the presence of tetramethylammonium hydroxide (TMAH) at 400°C. The obtained chromatograms clearly showed nine characteristic peaks, attributed to the THM products from 3HB and 3HHx units in the polymer chains, without any appreciable interference by the bacterial matrix components. Based on these peak intensities, the copolymer compositions were determined rapidly without using any cumbersome and lengthy sample pretreatment as in conventional GC method. Moreover, the compositions thus obtained were strongly correlated with those by NMR and conventional GC involving solvent extraction.
This paper introduces novel vacuum/compression valves (VCVs) utilizing paraffin wax. A VCV is implemented by sealing the venting channel/hole with wax plugs (for normally-closed valve), or to be sealed by wax (for normally-open valve), and is activated by localized heating on the CD surface. We demonstrate that the VCV provides the advantages of avoiding unnecessary heating of the sample/reagents in the diagnostic process, allowing for vacuum sealing of the CD, and clear separation of the paraffin wax from the sample/reagents in the microfluidic process. As a proof of concept, the microfluidic processes of liquid flow switching and liquid metering is demonstrated with the VCV. Results show that the VCV lowers the required spinning frequency to perform the microfluidic processes with high accuracy and ease of control.
The Australian, heat-resistant, a virulent V4 strain of Newcastle disease (ND) virus was selected for further heat resistance to give a variant designated V4-UPM. V4-UPM was sprayed on to food pellets which were fed to chickens in amounts calculated to give about 10(6) EID50 per chicken. Chickens vaccinated only once by feeding developed no haemagglutination-inhibition (HI) antibodies and were not protected against challenge with a viscerotropic velogenic strain of ND virus. Chickens given food pellet vaccine at 3 and 6 weeks of age developed HI antibodies and were substantially protected against parenteral and contact challenge with virulent ND virus. Similar protection was achieved when the V4-UPM vaccine was given intranasally on two occasions or when the vaccine virus was allowed to spread by contact from intranasally vaccinated chickens to nonvaccinated chickens. Heat resistant ND vaccine incorporated in food pellets may provide a method for protecting village chickens against ND in tropical countries.
Research was conducted to determine suitable chemical parameters as indicators of odor from decomposing food wastes. Prepared food scraps were stored in 18 l plastic buckets (2 kg wet weight each) at 20 °C and 8 °C to reproduce high and low temperature conditions. After 1, 3, 7, 10 and 14 days of storage, the odor from the buckets were marked to an intensity scale of 0 (no odor) to 5 (intense) and the corresponding leachate analyzed for volatile fatty acids, ammonia and total organic carbon. A linear relationship between odor intensity and the measured parameter indicates a suitable odor indicator. Odor intensified with longer storage period and warmer surroundings. The study found ammonia and isovaleric acid to be promising odor indicators. For this food waste mixture, offensive odors were emitted if the ammonia and isovaleric acid contents exceeded 360 mg/l and 940 mg/l, respectively.
Aquaculture activity has increased the population of crab, hence increasing the generation of related wastes, particularly the shell. In addition, the number of molting process in crabs compounds further the amount of waste shell generated. As such, in the present work, the application of the waste crab shell as a source of CaO in transesterification of palm olein to biodiesel (methyl ester) was investigated. Preliminary XRD results revealed that thermally activated crab shell contains mainly CaO. Parametric study has been investigated and optimal conditions were found to be methanol/oil mass ratio, 0.5:1; catalyst amount, 4 wt. %; and reaction temperature, 338 K. As compared to laboratory CaO, the catalyst from waste crab shell performs well, thus creating another low-cost catalyst source for producing biodiesel as well as adding value to the waste crab shell. Reusability of crab shell CaO has also been studied and the outcome confirmed that the catalyst is capable to be reutilized up to 11 times, without any major deterioration.
The CO2 capture capacity and cyclic stability of calcium oxide (CaO) prepared from cockle shells (CS) were enhanced by incorporating rice husk (RH) and binder through wet-mixing method. The cyclic reaction of calcination and carbonation was demonstrated using thermal gravimetric analyzer (TGA) which the calcination was performed in a pure N2 environment at 850 °C for 20 min and carbonation at 650 °C for 30 min in 20 vol% of CO2 in N2. The analysis using x-ray fluorescence (XRF) identified silica (Si) as the major elements in the sorbents. The RH-added sorbents also contained several types of metal elements such as which was a key factor to minimize the sintering of the sorbent during the cyclic reaction and contributed to higher CO2 capture capacity. The presence of various morphologies also associated with the improvement of the synthesized sorbents performance. The highest initial CO2 capture capacity was exhibited by CS+10%RH sorbent, which was 12% higher than the RH-free sorbent (CS). However, sorbents with the higher RH loading amount such as 40 and 50 wt% were preferred to maintain high capture capacity when the sorbents were regenerated and extended to the cyclic reaction. The sorbents also demonstrated the lowest average sorption decay, which suggested the most stable sorbent for cyclic-reaction. Once regenerated, the capture capacity of the RH-added sorbent was further increased by 12% when clay was added into the sorbent. Overall, the metal elements in RH and clay were possibly the key factor that enhances the performance of CaO prepared from CS, particularly for cyclic CO2 capture. Graphical abstract Cyclic calcination and carbonation reaction.
Red mud as industrial waste from bauxite was utilized as a precursor for the synthesis of mesoporous ZSM-5. A high concentration of iron oxide in red mud was successfully removed using alkali fusion treatment. Mesoporous ZSM-5 was synthesized using cetyltrimethylammonium bromide (CTABr) as a template via dual-hydrothermal method, and the effect of crystallization time was investigated towards the formation of mesopores. Characterization using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), N2 adsorption-desorption, scanning electron microscopy (SEM), and transmission electron microscopy (TEM) indicated the formation of cubic crystallite ZSM-5 with high surface area and mesopore volume within 6 h of crystallization. Increasing the crystallization time revealed the evolution of highly crystalline ZSM-5; however, the surface area and mesoporosity were significantly reduced. The effect of mesoporosity was investigated on the adsorption of methylene blue (MB). Kinetic and thermodynamic analysis of MB adsorption on mesoporous ZSM-5 was carried out at a variation of adsorption parameters such as the concentration of MB solution, the temperatures of solution, and the amount of adsorbent. Finally, methanol, 1-butanol, acetone, hydrochloric acid (HCl), and acetonitrile were used as desorbing agents to investigate the reusability and stability of mesoporous ZSM-5 as an adsorbent for MB removal.
In this study, pyrolysis technique was utilized for converting palm oil sludge to value added materials: bio-oil (liquid fuel) and bio-char (soil amendment). The bio-oil yield obtained was 27.4±1.7 wt.% having a heating value of 22.2±3.7 MJ/kg and a negligible ash content of 0.23±0.01 wt.%. The pH of bio-oil was in alkaline region. The bio-char yielded 49.9±0.3 wt.%, which was further investigated for sorption efficiency by adsorbing metal (Cd(2+) ions) from water. The removal efficiency of Cd(2+) was 89.4±2%, which was almost similar to the removal efficiency of a commercial activated carbon. The adsorption isotherm was well described by Langmuir model. Therefore, pyrolysis is proved as an efficient tool for palm oil sludge management, where the waste was converted into valuable products.
The production of beta-mannanase from palm kernel cake (PKC) as a substrate in solid substrate fermentation (SSF) was studied using a laboratory column bioreactor. The simultaneous effects of three independent variables, namely incubation temperature, initial moisture content of substrate and airflow rate, on beta-mannanase production were evaluated by response surface methodology (RSM) on the basis of a central composite face-centered (CCF) design. Eighteen trials were conducted in which Aspergillus niger FTCC 5003 was cultivated on PKC in an aerated column bioreactor for seven days under SSF process. The highest level of beta-mannanase (2117.89 U/g) was obtained when SSF process was performed at incubation temperature, initial moisture level and aeration rate of 32.5 degrees C, 60% and 0.5 l/min, respectively. Statistical analysis revealed that the quadratic terms of incubation temperature and initial moisture content had significant effects on the production of beta-mannanase (P < 0.01). A similar analysis also demonstrated that the linear effect of initial moisture level and an interaction effect between the initial moisture content and aeration rate significantly influenced the production of beta-mannanase (P < 0.01). The statistical model suggested that the optimal conditions for attaining the highest level of beta-mannanase were incubation temperature of 32 degrees C, initial moisture level of 59% and aeration rate of 0.5 l/min. A beta-mannanase yield of 2231.26 U/g was obtained when SSF process was carried out under the optimal conditions described above.
A series of bimetallic catalysts containing nickel supported over MgO-ZrO2 were tested for activity in the dry reforming of carbon dioxide. A nickel-cobalt bimetallic catalyst gave the best performance in terms of conversion and coke resistance from a range of Ni-X bimetallic catalysts, X=Ca, K, Ba, La, and Ce. The nitrogen-adsorption and hydrogen-chemisorption studies showed the Ni-Co bimetallic supported catalyst to have good surface area with high metal dispersion. This contributed to the high catalytic activity, in terms of conversion activity and stability of the catalyst, at an equimolar methane/carbon dioxide feed ratio. The kinetics of methane dry reforming are studied in a fixed-bed reactor over an Ni-Co bimetallic catalyst in the temperature range 700-800 °C by varying the partial pressures of CH4 and CO2. The experimental data were analyzed based on the proposed reaction mechanism using the Langmuir-Hinshelwood kinetic model. The activation energies for methane and carbon dioxide consumption were estimated at 52.9 and 48.1 kJ mol(-1), respectively. The lower value of CO2 activation energy compared to the activation energy of CH4 indicated a higher reaction rate of CO2, which owes to the strong basicity of nanocrystalline support, MgO-ZrO2.
In this work, two low-cost wastes, bivalve shell (BS) and Zea mays L. husk leaf (ZHL), were investigated to adsorb malachite green (MG) from aqueous solutions. The ZHL was treated with calcined BS to give the BS-ZHL, and its ability to adsorb MG was compared with untreated ZHL, calcined BS and Ca(OH)(2)-treated ZHL under several different conditions: pH (2-8), adsorbent dosage (0.25-2.5 g L(-1)), contact time (10-30 min), initial MG concentration (10-200 mg L(-1)) and temperature (303-323 K). The equilibrium studies indicated that the experimental data were in agreement with the Langmuir isotherm model. The use of 2.5 g L(-1) BS-ZHL resulted in the nearly complete removal of 200 mg L(-1) of MG with a maximum adsorption capacity of 81.5 mg g(-1) after 30 min of contact time at pH 6 and 323 K. The results indicated that the BS-ZHL can be used to effectively remove MG from aqueous media.
An ionic liquid, 1-n-butyl-3-methylimidazolium chloride (BmimCl) was blended with urea at 1:1 mole ratio to create a BmimCl/Urea mixture. The agarose/talc composite films containing the BmimCl/Urea mixture were then acquired through a gelation method. The weight ratio of agarose and talc was fixed at 4:1, while the content of BmimCl/Urea was varied from 0 to 10 wt % relative to the overall weight of the composite films. The tensile stress and modulus results showed the optimum BmimCl/Urea content in the composite film lies at 8 wt %. The talc particles are embedded in the agarose matrix and there are no pullouts for the composite films containing BmimCl/Urea as demonstrated by SEM micrographs. The addition of BmimCl/Urea increased the glass transition temperature of the composite films, however, the thermal decomposition temperature decreased drastically. FTIR and FT-Raman spectra indicated the existence of interaction between agarose and talc, which improves their interfacial adhesion. As a conclusion, a BmimCl/Urea mixture can be utilized as a coupling agent for agarose/talc composite films.
Matched MeSH terms: Temperature; Transition Temperature
In recent years, many efforts have been directed to explore the methods to reduce the production costs of industrial lipase by improving the yield and the use of low-cost agricultural wastes. Coconut dregs, which is a lignocellulosic by-product from coconut oil and milk processing plants, is rich in cellulose (36%) and crude fat (9%). A newly isolated Bacillus stratosphericus has been demonstrated to perform cellulose hydrolysis on coconut dregs producing fermentable sugars. The highest extracellular lipase activity of 140 U/mL has been achieved in submerged fermentation with acid pre-treated coconut dregs. The lipase was found to be active over a wide range of temperatures and pHs. The activity of lipase can be generally increased by the presence of detergent ingredients such as Tween-80, cetyltrimethylammonium bromide, hydrogen peroxide and phosphate per sulphate. The great compatibility of lipase in commercial detergents has also underlined its potential as an additive ingredient in biodetergent formulations.
The present work reports the successful synthesis of biosynthesized iron oxide nanoparticles (Fe3O4-NPs) with the use of non-toxic leaf extract of Neem (Azadirachta indica) as a reducing and stabilizing agent. The successful synthesis was confirmed by infrared spectra analysis with strong peak observed between 400-600 cm-1 that corresponds to magnetite nanoparticles characteristics. X-ray diffraction (XRD) analysis revealed that iron oxide nanoparticles were of high purity with crystalline cubic structure phases in nature. Besides, the average size of magnetite nanoparticles was observed to be 9-12 nm with mostly irregular shapes using a transmission electron microscope (TEM) and was supported by field emission scanning electron microscope (FESEM). Energy dispersive X-ray analysis shown that the elements iron (Fe) and oxygen (O) were present with atomic percentages of 33.29% and 66.71%, respectively. From the vibrating sample magnetometer (VSM) analysis it was proven that the nanoparticles exhibited superparamagnetic properties with a magnetization value of 73 emu/g and the results showed superparamagnetic behavior at room temperature, suggesting potential applications for a magnetic targeting drug delivery system.
Iron and steel industries are among the contributors of CO2 emission in large volume into the atmosphere, causing detrimental effects to the environment and the ecosystem at large scale. These industries also generate solid wastes in the form of electric arc furnace (EAF) slag during operations which result in about 10-15% slag wastes per ton of steel produced. In this study, the EAF slags from an iron and steel-making factory in Klang, Malaysia was utilized for CO2 sequestration through direct aqueous mineral carbonation. According to the surface area analysis, the fresh EAF slag has a mesoporous structure, its elemental composition shows the presence of 20.91 wt.% of CaO that was used for the sequestration of CO2 through carbonation. The sequestration capacity was found to be 58.36 g CO2/kg of slag at ambient temperature in 3 h, with the liquid/solid (L/S) ratio of 5:1 and using <63μm particle size. Moreover, the shrinking core model (SCM) was used to analyze the solid-fluid reaction in a heterogeneous phase and the CO2 sequestration shows to be controlled by the product layer phase. The EAF slag is demonstrated to have the potential of CO2 sequestration at ambient temperature.
Guava is a climacteric fruit which has high nutritional content. It is a highly perishable fruit, undergoes rapid postharvest ripening in a few days under ambient condition. This paper aims to determine the effect of palm stearin and palm kernel olein blends on maintaining the quality of guava during storage. Two different coating formulations of palm stearin (PS) and palm kernel olein (PKOo) blends (1:1 and 3:2) were analysed for their slip melting point (SMP), cohesiveness, viscosity and density. Beeswax was used as a commercial coating for comparison whiles the uncoated guava was used as control. These coatings were applied onto guavas by hand-wipe technique using a sponge. Guavas were dried in corrugated fibre board boxes and stored in an air-conditioned room maintained at 20°C while a chiller maintained at 10°C was used for chilled temperature. Coating pick up, thickness and surface area were measured while guava properties were analysed for coating effect on weight loss, O2 and CO2 gases, firmness and glossiness during storage at ambient temperature (20°C) for 21 days and chilled temperature (10ºC) for 30 days. Microstructure analysis was conducted within 2 days of coating at ambient temperature (20ºC). The results obtained indicated that 1:1 PSPKOo blends had higher cohesiveness compared to beeswax. Both PSPKOo blends significantly (p
Stack ventilation in the hot and humid climate is inherently inefficient due to minimal air temperature differences between indoor and outdoor environment of a naturally ventilated building. Solar induced ventilation is a viable alternative in enhancing this stack ventilation. This paper aims to demonstrate investigations on the effective solar collector orientation and stack height for a solar induced ventilation prototype that utilizes roof solar collector and vertical stack. The orientation of the solar collector is significant as it determines the amount of solar radiation absorbed by the solar collector. Meanwhile, the height of the vertical stack influences the creation of the stack pressure in inducing air movement. Investigations were executed using a simulation modelling software called FloVENT. The validation of the simulation modelling against physical experiment indicated a good agreement between these two results. Analyses were executed on the air temperature increments inside the solar collector. A high increment of the air temperature resulted in the effective orientation. Meanwhile, the air temperature and mass flow rate of the various heights of the vertical stack were also analyzed. The findings concluded that the recommended orientation for the prototype’s solar collector is the west-facing orientation. It was also found that the higher the vertical stack, the lower the air temperature inside the stack would be, but with greater induced mass flow rate.
Manual ground searches and cadaver dogs are traditional methods for locating remains, but they can be time- and resource-intensive, resulting in the decomposition of bodies and delay in victim identification. Therefore, thermal imaging has been proposed as a potentially useful tool for detecting remains based on their temperature. This study investigated the potential of a novel search technique of thermal drones to detect surface remains through the detection of maggot mass temperatures. Two trials were carried out at Selangor, Malaysia, each utilizing 12 healthy male Oryctolagus cuniculus European white rabbits and DJI Matrice 300 RTK drone China, equipped with a thermal camera; Zenmuse H20T to record the thermal imaging footage of the carcasses at various heights (15, 30, 60-100 m) for 14 days for each trial. Our results demonstrated that the larval masses and corresponding heat emissions were at their largest during the active decay stage; therefore, all the carcasses were observable in thermal images on day 5 and remained until day 7. Statistical analyses showed that (1) no statistically significant differences in thermal images between clothed and unclothed subjects (p > 0.05); (2) 15 m above ground level was proven to be the optimal height, as it showed the greatest contrast between the carcass heat signature and the background (p