METHODS: Upper limb tendons were harvested with consent from patients with crush injuries and non-replantable amputations. These tendons (both extensor and flexor) measuring 1 cm are sutured to either side of a 0.5 cm synthetic tendon strip and cultured in growth medium. At 2, 4, 6 and 8 weeks, samples were fixed into paraffin blocks, cut and stained with haematoxylin-eosin (H&E) and Masson's trichrome.
RESULTS: Minimal tendon ingrowth were seen in the first 2 weeks of incubation. However at 4 weeks, the cell ingrowth were seen migrating towards the junction between the tendon and the synthetic scaffold. This ingrowth continued to expand at 6 weeks and up to 8 weeks. At this point, the demarcation between human tendon and synthetic scaffold was indistinct.
CONCLUSIONS: We conclude that tendon ingrowth composed of collagen matrix were able to proliferate into a synthetic scaffold in vitro.
METHODS: The present study consisted of 50 lower limbs from formalin-fixed male adult cadavers aged about 70 years (45-85) belonging to the South Indian population. Total length of the quadriceps tendon, patellar height, patellar ligament height, proximal width, distal width and thickness of the patellar ligament were measured meticulously. Mean, standard deviation, median scores of each parameter were computed for groups using SPSS 16.0. Level of significance was considered as p
METHODS: This study was conducted between the years 2014 to 2016 at the Tissue Engineering Centre, UKM Medical Centre. OTC-I was extracted from ovine tendon, and fabricated into 3D scaffolds in the form of sponge, hydrogel and film. A polystyrene surface coated with OTC-I was used as the 2D culture condition. Genipin was used to crosslink the OTC-I. A non-coated polystyrene surface was used as a control. The mechanical strength of OTC-I scaffolds was evaluated. Attachment, proliferation and morphological features of HDF were assessed and compared between conditions.
RESULTS: The mechanical strength of OTC-I sponge was significantly higher than that of the other scaffolds. OTC-I scaffolds and the coated surface significantly enhanced HDF attachment and proliferation compared to the control, but no differences were observed between the scaffolds and coated surface. In contrast, the morphological features of HDF including spreading, filopodia, lamellipodia and actin cytoskeletal formation differed between conditions.
CONCLUSION: OTC-I can be moulded into various scaffolds that are biocompatible and thus could be suitable as scaffolds for developing tissue substitutes for clinical applications and in vitro tissue models. However, further study is required to determine the effect of morphological properties on the functional and molecular properties of HDF.