METHODS: 12 human incisors were embedded in resin except for a window on the buccal surface. Bonding agent was applied to half of the window, creating an exposed and non-exposed area. Baseline measurements were taken with QLF, OCT and surface microhardness. Samples were immersed in orange juice for 60 min and measurements taken stepwise every 10 min. QLF was used to compare the loss of fluorescence between the two areas. The OCT system, OCS1300SS (Thorlabs Ltd.), was used to record the intensity of backscattered light of both areas. Multiple linear regression and paired t test were used to compare the change of the outcome measures.
RESULTS: All 3 instruments demonstrated significant dose responses with the erosive challenge interval (p < 0.05) and a detection threshold of 10 min from baseline. Thereafter, surface microhardness demonstrated significant changes after every 10 min of erosion, QLF at 4 erosive intervals (20, 40, 50 and 60 min) while OCT at only 2 (50 and 60 min).
CONCLUSION: It can be concluded that OCT and QLF were able to detect demineralization after 10 min of erosive challenge and could be used to monitor the progression of demineralization of initial enamel erosion in vitro.
Purpose: In this work, polyethylene glycol (PEG), layered double hydroxide (LDH) and 5-fluorouracil (5-FU) were used as a stabilizing agent, a carrier and an anticancer active agent, respectively.
Characterization and methods: Magnetite nanoparticles (Fe3O4) coated with polyethylene glycol (PEG) and co-coated with 5-fluorouracil/Mg/Al- or Zn/Al-layered double hydroxide were synthesized by co-precipitation technique. Structural, magnetic properties, particle shape, particle size and drug loading percentage of the magnetic nanoparticles were investigated by XRD, TGA, FTIR, DLS, FESEM, TEM, VSM, UV-vis spectroscopy and HPLC techniques.
Results: XRD, TGA and FTIR studies confirmed the formation of Fe3O4 phase and the presence of iron oxide nanoparticles, polyethylene glycol, LDH and the drug for all the synthesized samples. The size of the nanoparticles co-coated with Mg/Al-LDH is about 27 nm compared to 40 nm when they were co-coated with Zn/Al-LDH, with both showings near uniform spherical shape. The iron oxide nanoparticles retain their superparamagnetic property when they were coated with polyethylene glycol, polyethylene glycol co-coated with Mg/Al-LDH and polyethylene glycol co-coated with Zn/Al-LDH with magnetic saturation value of 56, 40 and 27 emu/g, respectively. The cytotoxicity study reveals that the anticancer nanodelivery system has better anticancer activity than the free drug, 5-FU against liver cancer HepG2 cells and at the same time, it was found to be less toxic to the normal fibroblast 3T3 cells.
Conclusion: These are unique core-shell nanoparticles synthesized with the presence of multiple functionalities are hoped can be used as a multifunctional nanocarrier with the capability of targeted delivery using an external magnetic field and can also be exploited as hypothermia for cancer cells in addition to the chemotherapy property.