AIMS: The aim of this study was to look into the current perceptions and awareness about file separation during endodontic treatment among the dental house officers (DHOs).

MATERIALS AND METHODS: A novel validated questionnaire comprising of 15 close-ended questions was distributed anonymously via Google Forms through email to 1100 DHOs across Pakistan. The questionnaire consisted of two parts: the first component (Section I) collected demographic data and the second component (Section II) investigated the causes of EFS during root canal treatment. Following the completion of socioeconomic information, including age and gender, the DHOs were asked to answer a few questions about the various reasons for endodontic instrument fracture.

RESULTS: A total of 800 responses were recorded, with an effective rate of 72.8%. The majority of the DHOs (p value < 0.001) perceived that endodontic instrument fracture occurred in the posterior (61.5%) and apical third of the canal (50.5%) and in older permanent dentition (67.3%), possibly due to patient anxiety (62%). Better choice of instrument (61.15%), operators' experience (95.3%), knowledge (87.5%), and proper root canal cleaning (91.1%) are believed to be the vital steps in reducing endodontic file separation/fracture. Furthermore, majority of them (p value < 0.001) perceived that stainless steel was a superior alloy for filing instruments. Manual files tend to be more prone to fractures due to repeated use than rotary files.

METHODS: Different volume percentages of HEMA were tested in four experimental silane-based primer solutions (additions of HEMA: 0, 5.0 vol%, 25.0 vol% and 50.0 vol%). An experimental silane blend (primer) of 1.0 vol% 3-isocyanatopropyltrimethoxysilane (ICMS) + 0.5% bis-1,2-(triethoxysilyl) ethane (BTSE) was prepared and used. The experimental primers together with the control group were applied onto acid-etched premolars for attachment of orthodontic brackets. After artificial aging by thermocycling the shear-bond strength was measured. The fractured surfaces of all specimens were examined under scanning electron microscopy (SEM) to evaluate the failure mode on the enamel surface.

RESULTS: The experimental primers showed the highest shear-bond strength of 21.15 MPa (SD ± 2.70 MPa) and with 25 vol% showed a highly significant increase (P < 0.05) in bond strength. The SEM images showed full penetration of adhesive agents when using silane-based primers. In addition, the SEM images suggested that the predominant failure type was not necessarily the same as for the failure propagation.

METHODS: Six master dies were duplicated from the prepared maxillary first premolar tooth using nonprecious metal alloy (Wiron 99). Thirty copings (Procera AllCeram) of 0.6-mm thickness were manufactured. Three types of luting media were used: zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and dual-cured composite resin cement (Panavia F). Ten copings were cemented with each type. Two master dies were used for each group, and each of them was used to lute five copings. All groups were cemented according to manufacturer's instructions and received a static load of 5 kg during cementation. After 24 hours of distilled water storage at 37 degrees C, the copings were vertically compressed using a universal testing machine at a crosshead speed of 1 mm/min.

RESULTS: ANOVA revealed significant differences in the load at fracture among the three groups (p < 0.001). The fracture strength results showed that the mean fracture strength of zinc phosphate cement (Elite), glass ionomer cement (Fuji I), and resin luting cement (Panavia F) were 1091.9 N, 784.8 N, and 1953.5 N, respectively.