OBJECTIVE: The main objective of this study was to optimize the production of NPG diesters and to characterize the optimized esters with typical chemical, physical and electrical properties to study its potential as insulating oil.
METHODS: The transesterification reaction between HOPME and NPG was conducted in a 1L three-neck flask reactor at specified temperature, pressure, molar ratio and catalyst concentration. For the optimization, four factors have been studied and the diester product was characterized by using gas chromatography (GC) analysis. The synthesized esters were then characterized with typical properties of transformer oil such as flash point, pour point, viscosity and breakdown voltage and were compared with mineral insulating oil and commercial NPG dioleate. For formulation, different samples of NPG diesters with different concentration of pour point depressant were prepared and each sample was tested for its pour point measurement.
RESULTS: The optimum conditions inferred from the analyses were: molar ratio of HOPME to NPG of 2:1.3, temperature = 182°C, pressure = 0.6 mbar and catalyst concentration of 1.2%. The synthesized NPG diesters showed very important improvement in fire safety compared to mineral oil with flash point of 300°C and 155°C, respectively. NPG diesters also exhibit a relatively good viscosity of 21 cSt. The most striking observation to emerge from the data comparison with NPG diester was the breakdown voltage, which was higher than mineral oil and definitely in conformance to the IEC 61099 limit at 67.5 kV. The formulation of synthesized NPD diesters with VISCOPLEX® pour point depressant has successfully increased the pour point of NPG diester from -14°C to -48°C.
CONCLUSION: The reaction time for the transesterification of HOPME with NPG to produce NPG diester was successfully reduced to 1 hour from the 14 hours required in the earlier synthesis method. The main highlight of this study was the excess reactant which is no longer methyl ester but the alcohol (NPG). The optimum reaction conditions for the synthesis were molar ratio of 2:1.13 for NPG:HOPME, 182°C, 0.6 mbar and catalyst concentration of 1.2 wt%. The maximum NPG diester yield of 87 wt% was consistent with the predicted yield of 87.7 wt% obtained from RSM. The synthesized diester exhibited better insulating properties than the commercial products especially with regards to the breakdown voltage, flash point and moisture content.
METHODS: We searched 13 electronic databases and Google scholar, conducted citation searching and a review of reference lists to find studies which investigated the relationship of alcohol with clinical outcome of pesticide self-poisoning in different countries. Thirteen studies, including 11 case series/reports and two cohort studies were considered for inclusion.
RESULTS: Meta-analysis showed that alcohol co-ingestion in pesticide self-poisoning was associated with increased risk of death [odds ratio (OR) 4.9, 95% confidence interval (CI) 2.9-8.2 P<0.0001] and that alcohol co-ingested group required intubation eight times more often than non-co-ingested group in organophosphorus insecticide self-poisoning (OR 8.0, 95% CI 4.9-13.0 P<0.0001). Cases who co-ingested alcohol were older than non-alcohol group in two studies. One cohort study demonstrated that alcohol co-ingestion was associated with larger pesticide ingestions but did not itself affect the outcome.
CONCLUSIONS: This systematic review indicates that alcohol co-ingestion may worsen clinical outcome in pesticide self-poisoning.
RESULTS: ET 2.0 was found to be the best enzyme for hydrolysis. Under the optimum condition, the FFA content achievable was 790 g kg-1 after 24 h of reaction with 1:1 water-to-oil mass ratio at 50 °C and stirring speed of 9 × g. Furthermore, with the addition of 2 g kg-1 ascorbic acid, it was found that 98% of carotenoids and 96% of tocols could be retained after hydrolysis.
CONCLUSION: This work shows that enzymatic hydrolysis, which is inherently safer, cleaner and sustainable is feasible to replace the conventional methanolysis for the production of palm phytonutrients. © 2022 The Authors. Journal of The Science of Food and Agriculture published by John Wiley & Sons Ltd on behalf of Society of Chemical Industry.
Methods and Results: The study population was the postmortem cases of Asian population ranging from 16 to 75 years old in which blood and/or urine samples sent for alcohol and/or drug of abuse (DoA) analysis in year 2016 at our centre. Out of 434 cases, 54 from each group of positive and negative alcohol and/or DoA. Postmortem findings of lungs and postmortem CT scan urinary bladder volume (UBV) were recorded. Statistical significant correlation was obtained between urinary bladder distension on postmortem CT scan and cases with positive alcohol detection. However, the sensitivity was relatively low at 51.7%, whereas the specificity was 75% at the cut-off point. Low sensitivity and specificity at around 52.7% were obtained for pulmonary edema related to alcohol/DoA. This showed that UBV alone or pulmonary edema alone was not really a good indicator for alcohol or DoA intoxication. However, combination of both indicators provided higher sensitivity (73.3%) although specificity was lowered to 53.8%.
Conclusion: The findings of postmortem CT scan bladder distension and pulmonary edema could possibly identify intoxication cases but not conclusive.
OBJECTIVES: This study examined the relationship between exposure to teacher violence and mental health problems.
PARTICIPANTS AND SETTING: An international sample of young adults aged 18 to 24 (N = 283).
METHODS: Participants completed self-report measures of childhood trauma, exposure to teacher violence, depressive symptoms, post-traumatic stress, and alcohol misuse.
RESULTS: Exposure to teacher violence could be reliably and validly measured using the Teacher Violence Scale (TVS). Current mental health problems - including depressive symptoms, post-traumatic stress, and alcohol misuse - were associated with exposure to teacher violence during high school years, but not with childhood non-betrayal trauma.
CONCLUSIONS: Our findings expand the application of the betrayal trauma theory to school settings and point to the importance of preventing and managing teacher violence. It is important to provide more support and training to teachers and enhance monitoring measures in schools. More research on the prevalence and correlates of exposure to teacher violence is needed. We also provided first evidence supporting the reliability and validity of the English version of the TVS to facilitate future research.
OBJECTIVES: The objectives of this study were to evaluate the degradation effects of each dietary solvent on the microhardness of the different CAD/CAM dental composites and to observe the degradation effects of dietary solvent on the inorganic elements of the dental composites investigated.
METHODS: Fifty specimens with dimensions 12 mm x 14 mm x 1.5 mm were prepared for direct composite (Filtek Z350 XT [FZ]), indirect composite (Shofu Ceramage [CM]), and three CAD/CAM composites (Lava Ultimate [LU], Cerasmart [CS], and Vita Enamic [VE]). The specimens were randomly divided into 5 groups (n = 10) and conditioned for 1-week at 37°C in the following: air (control), distilled water, 0.02 N citric acid, 0.02 N lactic acid and 50% ethanol-water solution. Subsequently, the specimens were subjected to microhardness test (KHN) using Knoop hardness indenter. Air (control) and representative postconditioning specimens with the lowest mean KHN value for each material were analyzed using energy dispersive X-ray spectroscopy (EDX). Statistical analysis was done using one-way ANOVA and post hoc Bonferroni test at a significance level of p = 0.05.
RESULTS: Mean KHN values ranged from 39.7 ± 2.7 kg/mm2 for FZ conditioned in 50% ethanol-water solution to 79.2 ± 3.4 kg/mm2 for VE conditioned in air (control). With exception to LU, significant differences were observed between materials and dietary solvents for other dental composites investigated. EDX showed stable peaks of the inorganic elements between air (control) and representative postconditioning specimens.
CONCLUSIONS: The microhardness of dental composites was significantly affected by dietary solvents, except for one CAD/CAM composite [LU]. However, no changes were observed in the inorganic elemental composition of dental composites between air (control) and 1-week postconditioning.