Reclaimed rubber from rejected natural rubber (NR) latex gloves (r-NRG) was evaluated as partial
replacement for Standard Malaysian Rubber (SMR) 20 in producing microcellular rubber. In the study, the amount of reclaimed rubber varied from 20 pphr to 95 pphr for the purpose of cost reduction, environmental interest and as processing aids in reducing internal porosity, swells and to minimize shrinkage and air-trapped problems in producing microcellular rubber. A typical formulation in making microcellular rubber slab was developed and two-roll mill was used for compounding. The cure characteristics and mechanical properties, such as density, hardness, tensile strength, and elongation at break, were evaluated. Scorch time and cure rate index performed marginal decreased with increasing of r-NRG content. 95 pphr r-NRG blends showed a consequential drop in hardness. Both tensile properties and elongation at break decreased as the r-NRG content was increased.
Thermoplastic natural rubber sample is found isotropic based on SAXS pattern. Morphological parameter was obtained based on ideal lamellar morphology using 1-D correlation function. The fitting was carried out using Porod tail model and Vonk for back-extrapolated model. It is found that the long period value is 15.7nm which is comparable to results obtained from Lorents corrected profile, 20nm. Crystalline thickness and amorphous thickness was found as 13.4 and 2.31nm respectively
The thermal conductivity of boron carbide filled thermoplastic natural rubber blend composite is studied experimentally as a function of filler loading and filler size. A polymer blend of 60/40 NR/HDPE was used as matrix for incorporation of particulate nano- and micro-sized B4C as filler to form the composite. As the filler loading is increased from 2-10%wt, a reduction and increment of thermal conductivity was observed. The results show at lower filler loading, HDPE crystallinity affects the thermal conductivity up to 4 and 6%wt of filler for nano- and micro-composite respectively. Further increase the loading do not much alter the crystallinity as the filler is distributed in continues phase of NR. The increment of filler amount in the amorphous NR causes the thermal conductivity to gradually increase which indicates the formation of interconnecting filler network structures
This article aims to provide insights into the factors that contribute to the separation efficiency of solid particles. In this study, a pneumatic jigging technique was used to assess the separation of solid waste materials that consisted of copper, glass and rubber insulator. Several initial experiments were carried out to evaluate the strengths and limitations of the technique. It is found that despite some limitations of the technique, all the samples prepared for the experiments were successfully separated. The follow-up experiments were then carried out to further assess the separation of copper wire and rubber insulator. The effects of air flow and pulse rates on the separation process were examined. The data for these follow-up experiments were analysed using a sink float analysis technique. The analysis shows that the air flow rate was very important in determining the separation efficiency. However, the separation efficiency may be influenced by the type of materials used.
This study investigated the accumulation of debris at four sites, namely, Gebeng, Batu Hitam, Cherok Paloh, and Air Leleh, along the Pahang coastline, Peninsular Malaysia from March 2019 to February 2020. Plastic was the dominant debris (86.1%) and followed by cloth/fabric-based debris (6.0%), processed lumber debris (3.3%), rubber (2.7%), glass (1.5%), and metal (0.4%). The land-based debris (82.0%) was the major source of the deposition of marine waste. A statistically significant relationship was found between the seasonal variation and marine debris density in tidal and seasonal current along the Pahang coastline. In general, the Northeast Monsoon season had a higher amount of debris than the Southwest Monsoon season.
Poor performance of wet scrubbers in rubber processing plants due to breakthrough of specific volatile organic compounds (VOCs) causes odour impact events. The performance of wet scrubbers in the rubber drying process to remove VOCs was investigated in order to determine the responsible odorants. VOC emissions originating at the inlet and outlet of wet scrubbers were quantified using gas chromatography-mass spectrometry/olfactometry (GC-MS/O). Critical VOCs were identified alongside seasonal and daily variations of those VOCs. Altogether, 80 VOCs were detected in rubber emissions with 16 classified as critical VOCs based on their chemical concentration, high odour activity value (OAV) and unpleasant odour. Volatile fatty acids (VFAs) were the dominant VOCs with seasonal variations affecting emission composition. Results demonstrated the ineffectiveness of the wet scrubbers to mitigate odorous VOCs whereas the removal of some VOCs could be improved based on their polarity and solubility. It was found that there is a correlation between the wet scrubber performance and VFAs concentration in the emissions. The findings demonstrated that combining quantitative and sensory analyses improved accuracy in identifying odorous VOCs, which can cause odour annoyance from rubber processing. A VOC identification framework was proposed using both analyses approaches.
Orthodontic elastic bands are an important iatrogenic etiologic factor in the causation of periodontal attachment apparatus breakdown. Appropriate diagnosis and a well constructed treatment plan tailor-made to suit the requirements of the particular patient is imperative for management of periodontal lesions induced by subgingival retention of rubber band. There are conflicting reports regarding the reattachment and regeneration of lost periodontal supporting tissues in such cases. The present case report highlights the spontaneous reversal and correction of periodontal destruction due to iatrogenic orthodontic elastic band displacement deep into the subgingival tissues.
Tropical primary forests are being destroyed at an alarming rate and converted for other land uses which is expected to greatly influence soil carbon (C) cycling. However, our understanding of how tropical forest conversions affect the accumulation of compounds in soil functional C pools remains unclear. Here, we collected soils from primary forests (PF), secondary forests (SF), oil-palm (OP), and rubber plantations (RP), and assessed the accumulation of plant- and microbial-derived compounds within soil organic carbon (SOC), particulate (POC) and mineral-associated (MAOC) organic C. PF conversion to RP greatly decreased SOC, POC, and MAOC concentrations, whereas conversion to SF increased POC concentrations and decreased MAOC concentrations, and conversion to OP only increased POC concentrations. PF conversion to RP decreased lignin concentrations and increased amino sugar concentrations in SOC pools which increased the stability of SOC, whereas conversion to SF only increased the lignin concentrations in POC, and conversion to OP just increased lignin concentrations in POC and decreased it in MAOC. We observed divergent dynamics of amino sugars (decrease) and lignin (increase) in SOC with increasing SOC. Only lignin concentrations increased in POC with increasing POC and amino sugars concentrations decreased in MAOC with increasing MAOC. Conversion to RP significantly decreased soil enzyme activities and microbial biomasses. Lignin accumulation was associated with microbial properties, whereas amino sugar accumulation was mainly associated with soil nutrients and stoichiometries. These results suggest that the divergent accumulation of plant- and microbial-derived C in SOC was delivered by the distribution and original composition of functional C pools under forest conversions. Forest conversions changed the formation and stabilization processes of SOC in the long run which was associated with converted plantations and management. The important roles of soil nutrients and stoichiometry also provide a natural-based solution to enhance SOC sequestration via nutrient management in tropical forests.
Streptomyces sp. strain CFMR 7, which naturally degrades rubber, was isolated from a rubber plantation. Whole genome sequencing and assembly resulted in 2 contigs with total genome size of 8.248 Mb. Two latex clearing protein (lcp) genes which are responsible for rubber degrading activities were identified.
Rubber materials have greatly contributed to human civilization. However, being a polymeric material does not decompose easily, it has caused huge environmental problems. On the other hand, only few bacteria are known to degrade rubber, with studies pertaining them being intensively focusing on the mechanism involved in microbial rubber degradation. The Streptomyces sp. strain CFMR 7, which was previously confirmed to possess rubber-degrading ability, was subjected to whole genome sequencing using the single molecule sequencing technology of the PacBio® RS II system. The genome was further analyzed and compared with previously reported rubber-degrading bacteria in order to identify the potential genes involved in rubber degradation. This led to the interesting discovery of three homologues of latex-clearing protein (Lcp) on the chromosome of this strain, which are probably responsible for rubber degrading activities. Genes encoding oxidoreductase α-subunit (oxiA) and oxidoreductase β-subunit (oxiB) were also found downstream of two lcp genes which are located adjacent to each other. In silico analysis reveals genes that have been identified to be involved in the microbial degradation of rubber in the Streptomyces sp. strain CFMR 7. This is the first whole genome sequence of a clear-zone-forming natural rubber- degrading Streptomyces sp., which harbours three Lcp homologous genes with the presence of oxiA and oxiB genes compared to the previously reported Gordonia polyisoprenivorans strain VH2 (with two Lcp homologous genes) and Nocardia nova SH22a (with only one Lcp gene).
Determination of the thermal characteristics and temperature-dependent rheological properties of the magnetorheological elastomers (MREs) is of paramount importance particularly with regards to MRE applications. Hitherto, a paucity of temperature dependent analysis has been conducted by MRE researchers. In this study, an investigation on the thermal and rheological properties of epoxidized natural rubber (ENR)-based MREs was performed. Various percentages of carbonyl iron particles (CIPs) were blended with the ENR compound using a two roll-mill for the preparation of the ENR-based MRE samples. The morphological, elemental, and thermal analyses were performed before the rheological test. Several characterizations, as well as the effects of the strain amplitude, temperature, and magnetic field on the rheological properties of ENR-based MRE samples, were evaluated. The micrographs and elemental results were well-correlated regarding the CIP and Fe contents, and a uniform distribution of CIPs was achieved. The results of the thermal test indicated that the incorporation of CIPs enhanced the thermal stability of the ENR-based MREs. Based on the rheological analysis, the storage modulus and loss factor were dependent on the CIP content and strain amplitude. The effect of temperature on the rheological properties revealed that the stiffness of the ENR-based MREs was considered stable, and they were appropriate to be employed in the MRE devices exposed to high temperatures above 45 °C.
As the living cytoplasm of laticiferous cells, Hevea brasiliensis latex is a rich blend of organic substances that include a mélange of proteins. A small number of these proteins have given rise to the problem of latex allergy. The salient characteristics of H. brasiliensis latex allergens that are recognized by the International Union of Immunological Societies (IUIS) are reviewed. These are the proteins associated with the rubber particles, the cytosolic C-serum proteins and the B-serum proteins that originate mainly from the lutoids. Procedures for the isolation and purification of latex allergens are discussed, from latex collection in the field to various preparative approaches adopted in the laboratory. As interest in recombinant latex allergens increases, there is a need to validate recombinant proteins to ascertain equivalence with their native counterparts when used in immunological studies, diagnostics, and immunotherapy.
Gloves that will provide a barrier of protection from infectious organisms are an essential feature of medical practice for the protection of both patients and medical personnel. Natural rubber latex has consistently been the most satisfactory raw material for the manufacture of gloves. Certain latex proteins, carried over into the finished product by inadequate manufacturing processes, may pose a risk of provoking allergic reactions in some patients and medical workers. As with any allergy, the risk depends on the route of exposure and dose. Hence, the method of manufacture, including the means used to coat gloves to make donning easy, can influence the eventual exposure of sensitive people to latex allergens. In this article, we describe the several processes in use and their effects on latex protein content.
Potato starch nanocrystals were found to serve as an effective reinforcing agent for natural rubber (NR). Starch nanocrystals were obtained by the sulfuric acid hydrolysis of potato starch granules. After mixing the latex and the starch nanocrystals, the resulting aqueous suspension was cast into film by solvent evaporation method. The composite samples were successfully prepared by varying filler loadings, using a colloidal suspension of starch nanocrystals and NR latex. The morphology of the nanocomposite prepared was analyzed by field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). FESEM analysis revealed the size and shape of the crystal and their homogeneous dispersion in the composites. The crystallinity of the nanocomposites was studied using XRD analysis which indicated an overall increase in crystallinity with filler content. The mechanical properties of the nanocomposites such as stress-strain behavior, tensile strength, tensile modulus and elongation at break were measured according to ASTM standards. The tensile strength and modulus of the composites were found to improve tremendously with increasing nanocrystal content. This dramatic increase observed can be attributed to the formation of starch nanocrystal network. This network immobilizes the polymer chains leading to an increase in the modulus and other mechanical properties.
A new method of Standard Malaysian Rubber (SMR) process wastewater treatment was developed based on in situ hypochlorous acid generation. The hypochlorous acid was generated in an undivided electrolytic cell consisting of two sets of graphite as anode and stainless sheets as cathode. The generated hypochlorous acid served as an oxidizing agent to destroy the organic matter present in the SMR wastewater. For an influent COD concentration of 2960 mg/L at an initial pH 4.5+/-0.1, current density 74.5 mA/cm(2), sodium chloride content 3% and electrolysis period of 75 min, resulted in the following residual values pH 7.5, COD 87 mg/L, BOD(5) 60 mg/L, TOC 65 mg/L, total chlorine 146 mg/L, turbidity 7 NTU and temperature 48 degrees C, respectively. In the case of 2% sodium chloride as an electrolyte for the above said operating condition resulted in the following values namely: pH 7.2, COD 165 mg/L, BOD(5) 105 mg/L, TOC 120 mg/L, total chlorine 120 mg/L, turbidity 27 NTU and temperature 53 degrees C, respectively. The energy requirement were found to be 30 and 46 Wh/L, while treating 24 L of SMR wastewater at 2 and 3% sodium chloride concentration at a current density 74.5 mA/cm(2). The observed energy difference was due to the improved conductivity at high sodium chloride content.
This paper details a study conducted to evaluate the performance of cold in-place recycling (CIPR) using polymer modified asphalt emulsion (PMAE). The asphalt emulsion was modified using natural rubber latex (NRL). Four proportions of reclaimed asphalt pavement (RAP) which are 0%, 25%, 50% and 75% were mixed with natural aggregates and modified asphalt emulsion using natural rubber latex (NRL). The results showed that the optimum modified asphalt emulsion for each proportion of RAP decreased due to the increase in RAP content. Results obtained from Indirect Tensile Strength (ITS) and Uniaxial Compressive Strength (UCS) test for the mixes complied with the requirements of the Road Engineering Association of Malaysia (REAM) specifications. The unsoaked and soaked ITS values obtained were 0.2 MPa and 0.15 MPa respectively, and the minimum compressive strength of CIPR mix obtained was 0.7 MPa. Based on the evaluation of performance for the four RAP proportions, it was determined that 50% of RAP gave the best combination of the CIPR mixture.
A safety evaluation test on human for latex films made from Radiation Prevulcanized Natural Rubber Latex (RVNRL) with sulfur-containing antioxidant was studied. Sulfur test has confirmed that there was sulfur compound presence in RVNRL derived from antioxidant used in this study. Two types of safety evaluation test were being adopted which are Patch Test and Modified Draize-95 test and this test proved that there is no clinical evidence on the presence of sulfur compound in RVNRL that may induce Type IV allergy in the unsensitized general user population. Both clinical test shows that the highest score value produced by test subjects is 1 and not exceed the allowable limit.
Peroxide pre-vulcanized natural rubber latex prepared by using gamma irradiation technique is an alternative over the conventionally prepared peroxide pre-vulcanized that used activator to promote the peroxide decomposition in natural rubber latex. Through this technique the problems aroused by some activators such as tends to darken the natural rubber latex film during the drying process can also be overcome. For this preliminary study, data obtained from crosslink density and mechanical measurements were used to evaluate the effectiveness of gamma irradiation in the vulcanization process. Increasing the quantity of tert-butyl hydroperoxide (t-BHPO) from 0.1 pphr to 0.3 pphr while the irradiation dose maintain at 12 kGy has successfully delivered peroxide vulcanized natural rubber latex films with average tensile strength, modulus @ 500% and modulus @ 700% around 15.33, 1.01 and 3.42 MPa, respectively. The effective pre-vulcanization irradiation dose with respect to maximum crosslinking density (85.8 %) was observed on film prepared at 0.1 pphr t-BHPO.
Hevea brasiliensis is one of the popular industrial crops in Malaysia better known as rubber tree belongs to the family Euphorbiaceace. From more than 12 species of Hevea, only Hevea brasiliensis is economically exploited because the milky latex extracted from the tree is the primary source of natural rubber. As in other crops, various plant physiological conditions and pathogenic diseases influence rubber production. Brown bast is one of the most serious threats to natural rubber production. In general, high-yielding clones of rubber tree are often considered to be more susceptible to this physiological disorder also commonly termed Tapping Panel Dryness (TPD). It is estimated that brown bast leads to approximately 15-20% decrease in yield. There is no known cure for brown bast yet. However, many plantation practices manage brown bast in rubber by giving tapping rest and changing tapping panel. Hence, this review condenses the causal of brown bast, symptoms of diseases and also control of brown bast affected Hevea tree.
Nowadays, development of cable-stayed bridges is increasing around the world. The mitigation of seismic forces to these bridges are obligatory to prevent damages or failure of its structural members. Herein, this paper aimed to determine the near-fault ground motion effect on an existing cablestayed bridge equipped with lead-rubber bearing. In this context, Shipshaw cable-stayed bridge is selected as the case study. The selected bridge has a span of 183.2 m composite deck and 43 m height of steel tower. 2D finite element models of the non-isolated and base isolated bridges are modelled by using SAP2000. Three different near-fault ground motions which are Tabas 1978, Cape Mendocino 1992 and Kobe 1995 were subjected to the 2D FEM models in order to determine the seismic behaviour of the bridge. The near-fault ground motions were applied to the bridge in the longitudinal direction. Nonlinear dynamic analysis was performed to determine the dynamic responses of the bridge. Comparison of dynamic response of nonisolated and base isolated bridge under three different near-fault ground motions were conducted. The results obtained from numerical analyses of the bridge showed that the isolation system lengthened the period of bridge and minimised deck displacement, base shear and base moment of the bridge. It is concluded that the isolation system significantly reduced the destructive effects of near-fault ground motions on the bridge.